Corrosion behavior of additively manufactured FeCrAl in out-of-pile light water reactor environments
Not Available
Materials Science↗
Engineering topics
Hoffman, Andrew K.
Publications and source records attributed to Hoffman, Andrew K..
Elucidating precipitation in FeCrAl alloys through explainable AI: A case study
Not Available
Materials Science↗
FeCrAl fuel/clad chemical interaction in light water reactor environments
This article investigates the fuel-cladding chemical interaction (FCCI) behavior of two commercial FeCrAl alloys, APMT composition (Fe-21Cr-5Al-3Mo wt.%) and C35M (Fe-13Cr-5Al-2Mo-0.2Si-0.03Y wt.%), after neutron irradiation. “H-cup” diffusion multiples of FeCrAl alloys and ceramic UO 2 fuel were irradiated at a temperature of ~300 °C to a total estimated burnup of 26 GWd/tHM. Post-irradiation Examination results demonstrate the excellent degradation resistance of FeCrAl alloys as accident tolerant fuel (ATF) cladding materials in light water reactor conditions. The study concludes that there was no irradiation-induced defects observed in either of the two commercial FeCrAl claddings. The formation of amorphous Al/U mixed oxide was observed at the fuel-clad interface, which can serve as a tritium permeation barrier and protect against potential chemical attack from the fuel. Finally, the study attributed the formation of amorphous Al/U mixed oxide to the low temperature and limited time of neutron irradiation. APMT forms more distinct Cr and Cr-Fe intermetallic at the FeCrAl-UO 2 interface than C35M due to the higher bulk Cr:Al ratio.
22 GENERAL STUDIES OF NUCLEAR REACTORS↗
Novel effects of grain size and ion implantation on grain boundary segregation in ion irradiated austenitic steel
Nuclear reactor environments are extreme in nature due to the combination of exposure to corrosive coolant, mechanical stresses, and neutron irradiation damage. This combination of environments can lead to irradiation induced/assisted precipitation, segregation, and embrittlement coupled with enhanced creep and stress corrosion cracking. While nanostructured materials are of interest in a variety of applications due to their unique properties including high mechanical strength, for nuclear applications nanostructured materials have the added benefit of irradiation resistance due to the high volume density of sinks for irradiation-induced defects. In this study, we show unique radiation-induced segregation (RIS) behavior in nanocrystalline 304 stainless steel (SS304). Typical RIS in austenitic steels includes Ni enrichment and Cr depletion within the grain boundaries. In nanostructured SS304 this RIS is reduced. Furthermore, interestingly, some grain boundaries in the nanocrystalline SS304 in this study were found to be enriched in Cr after Fe 2+ ion irradiation at 500 °C up to 50 displacements per atom (dpa). To understand this unique observation, lattice-based atomic kinetic Monte Carlo simulations were performed to investigate the effects of grain size, thermal segregation, as well as injected interstitials (introduced as Fe self-ions). The results indicate that the Cr enrichment at grain boundaries may be caused by combined effects of grain size, self-ion injection and preferential Cr diffusion via the interstitial mechanism. In conclusion, the findings also suggest a possible difference in RIS between ion and neutron irradiations.
36 MATERIALS SCIENCE↗
The relationship between grain size distribution and ductile to brittle transition temperature in FeCrAl alloys
A FeCrAl (Fe12Cr6Al2Mo) alloy was prepared by two methods, (a) traditional wrought and (b) powder metallurgy (PM). Further, both alloys exhibited the same average grain size (~40 um), but the PM alloy displayed a wider grain size distribution. Charpy impact testing showed that the ductile to brittle transition temperature width is dependent on the grain size distribution width.
36 MATERIALS SCIENCE↗
Oxidation Resistance in 1200°C Steam of a FeCrAl Alloy Fabricated by Three Metallurgical Processes
Abstract FeCrAl alloys are a leading candidate material for accident tolerant fuel cladding due to their good performance in both normal light-water reactor operating conditions as well as their resilience to high-temperature accident scenarios. For commercial-scale production, new fabrication techniques need to be investigated. In this study, the effects of fabrication methods on the high-temperature steam oxidation performance of C26M (Fe12Cr6Al2Mo in wt.%) were investigated. Three variants of C26M were manufactured: wrought (cast and forged) (WC26M), powder metallurgy hot isostatic pressing (PMC26M), and laser powder bed fusion additive manufacturing (AMC26M). All three variants were exposed to steam at 1200°C for 2 h. Results showed no significant variation in mass change between the variants after steam exposure. All three variants effectively formed stable protective alumina films with ~0.6–1.3 µ m thickness. This study suggests FeCrAl alloys have excellent resilience to high-temperature steam in nuclear reactor accident scenarios regardless of the fabrication method.
Materials Science↗
Acid Dissolution Behavior of Ferritic FeCrAl Tubes Candidates for Nuclear Fuel Cladding
The international materials community is engaged in finding safer alternatives to zirconium alloys for the cladding of fuel in light water reactors. One solution is to replace the zirconium cladding using ferritic iron-chromium-aluminum (FeCrAl) alloys, which offer extraordinary resistance to high-temperature reaction with air or steam due to the formation of a protective alumina layer on the external surface. It is important to characterize the behavior of FeCrAl not only during accident conditions but in the entire fuel cycle, which may include reprocessing of the used fuel after it is removed from the power reactors. The reprocessing may involve the dissolution of the fuel rods in mineral acids. Little or nothing is known on the dissolution of FeCrAl alloys in common mineral acids, therefore the objective of this research was to study the dissolution of typical cladding tubing having two compositions of FeCrAl (APMT and C26M) in three acids (H 2 SO 4 , HNO 3 , and HCl) as a function of the temperature using both standard ASTM immersion tests as well as electrochemical tests. The dissolution behavior of the FeCrAl alloys is compared to the dissolution capability of other traditional nuclear materials such as austenitic stainless steels (304SS and 316SS) and austenitic nickel alloys (Alloy 600 and Hastelloy C-276). Results show that both C26M and APMT have a higher dissolution capability in the studied mineral acids, which will be beneficial for reprocessing procedures.
36 MATERIALS SCIENCE↗