NASA NTRS1986

Solidification of Nb-Ge alloys in long drop tubes

The 30-m and 100 m-long drop tubes at the Marshall Space Flight Center have been used to obtain large undercooling in Nb-Ge alloys. Electron beam melting has been used to obtain drops approximately 2.5 mm in diam. In the 30-m tube, many specimens fell the length of the tube without solidifying, and were ultimately liquid-quenched in oil. The amount of undercooling prior to the quench was usually around 0.13 T(m). In the 100-m tube, freezing generally initiated during free fall, and the maximum undercooling was around 0.22 T(m). Microstructures were characterized by a combination of X-ray diffraction, optical microscopy, and scanning electron microscopy with energy dispersive analysis by X-rays. A variety of interesting microstructures was observed.

Bayuzick, R. J.↗

NASA NTRS1985

Undercooling of niobium-germanium alloys in a 100 meter drop tube

The undercoolings of pure Nb and Nb-Ge alloys are examined using the 100-m drop tube of the Marshall Space Flight Center. The temperatures of the samples prior to release were measured, and IR detectors were utilized to monitor recalescence from solidification. It is observed that the Nb and Nb-Ge samples undercooled to the homogeneous nucleation limit. The data reveal that all the samples displayed a dendritic primary phase, except for alloys nucleating in the beta-phase field, which had a cellular phase. The composition of these phases are studied using EDXA; it is detected that the composition of the phases corresponds to the Jorda (1978) phase diagram.

Hofmeister, W. H.↗

NASA NTRS1984

Microgravity containerless processing in long drop tubes

Extensive experience in utilizing long drop tubes for studying effects of microgravity on the solidification of alloys was obtained. While some modifications are necessary to improve versatility, the facility proved to be most useful. Both an electron beam furnace and an electromagnetic levitation furnace can be used. The electron beam furnace is used with vacuum environments (0.00001 torr), whereas the levitation furnace is presently used only in inert gas environments (above 100 torr). Experiments are best applied to refractory alloys because of the sensitivity of the detectors now being used to observe solidification. Processing of lower melting point metals and alloys simply cannot be recorded. On the other hand, expected improvements in detector sensitivity will allow experimentation with relatively low melting alloys. In such cases, solidification will occur in flight only if higher inert gas pressure is used (100 to 760 torr) to increase heat loss by convection. Under these conditions microgravity conditions no longer apply. However, as shown by results to date, it is not microgravity as such that is important in drop tube solidification. Instead it is the containerless nature of the process that is significant, leading to large degrees of undercooling before solidification and therefore to unique alloys.

Bayuzick, R. J.↗