NASA NTRS1993

Room temperature degradation of YBa2Cu3O(7-x) superconductors in varying relative humidity environments

An aging study was performed to determine the stability of YBa2Cu3O(7-x) ceramics in humid environments at 20 C. In this study, fired ceramic specimens were exposed to humidity levels ranging from 30.5 to 100 percent for 2-, 4-, and 6-week time intervals. After storage under these conditions, the specimens were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), and electrical resistance measurements. At every storage condition evaluated, the fired ceramics were found to interact with H2O present in the surrounding environment, resulting in the decomposition of the YBa2Cu3O(7-x) phase. XRD data showed that BaCO3, CuO, and Y2BaCuO5 were present after aging and that the peak intensities of these impurity phases increased both with increasing humidity level and with increasing time of exposure. Additionally, SEM analyses of the ceramic microstructures after aging revealed the development of needle-like crystallites along the surface of the test specimens after aging. Furthermore, the superconducting transition temperature T(sub c) was found to decrease both with increasing humidity level and with increasing time of exposure. All the specimens aged at 30.5, 66, and 81 percent relative humidity exhibited superconducting transitions above 80 K, although these values were reduced by the exposure to the test conditions. Conversely, the specimens stored in direct contact with water (100 percent relative humidity) exhibited no superconducting transitions.

Hooker, M. W.↗

NASA NTRS1993

Effects of process variables on the properties of YBa2Cu3O(7-x) ceramics formed by investment casting

An investment casting process has been developed to produce net-shape, superconducting ceramics. In this work, a factorial experiment was performed to determine the critical process parameters for producing cast YBa2Cu3O7 ceramics with optimum properties. An analysis of variance procedure indicated that the key variables in casting superconductive ceramics are the particle size distribution and sintering temperature. Additionally, the interactions between the sintering temperature and the other process parameters (e.g., particle size distribution and the use of silver dopants) were also found to influence the density, porosity, and critical current density of the fired ceramics.

Hooker, M. W.↗

NASA NTRS1993

Environmental considerations for application of high Tc superconductors in space

The impact of the environmental factors on the performance of the superconductive devices during spaceflight missions is reviewed. Specific factors typical of spaceflight are addressed to evaluate superconductive devices for space-based applications including preflight storage, radiation, vibration, and thermal cycling.

Carlberg, I. A.↗

NASA NTRS1993

High-Tc thermal bridges for space-borne cryogenic infrared detectors

The potential for using high-temperature superconductive elements, screen-printed onto ceramic substrates, as thermal bridges to replace the currently employed manganin wires is studied at NASA-LaRC. Substrate selection is considered to be the most critical parameter in device production. Due to the glass-like thermal behavior of yttria-stabilized-zirconia (YSZ) and fused silica substrates, these materials are found to reduce the heat load significantly. The estimated thermal savings for superconductive leads printed onto YSZ or fused silica substrates range from 6 to 14 percent.

Wise, S. A.↗

NASA NTRS1993

High T(sub c) leads for remote sensing applications

Several NASA programs designed to monitor the Earth's atmosphere from space utilize infrared detectors which operate at or below 4.2 K for optimum performance. At present, the detectors are maintained at cryogenic temperatures by a stored volume of liquid helium. These detectors must be electrically linked to amplification electronics data storage instruments maintained at 80 K. The electrical connections over the temperature gradient account for approximately 20% of the total heat load on the Dewar for some systems, accelerating the boil-off of liquid helium cryogen and reducing the operational lifetime of the space-borne instruments. The recent discovery of high temperature superconductors has provided an opportunity to develop electrically conductive, thermally insulating links to bridge this thermal gradient. This paper describes the modelling of the thermal transport properties of thick film, high T(sub c) electrical bridges across a 4.2-80 K temperature gradient and the impact of such devices on a spaceborne remote sensing system.

Selim, R.↗

NASA NTRS1989

Electrochemical cell for obtaining oxygen from carbon dioxide atmospheres

For manned missions to Mars to become a reality, an efficient and reliable means of obtaining oxygen from the carbon dioxide-rich atmosphere will be required. Otherwise, the high cost of transporting the oxygen needed to sustain the astronauts will severely restrict the expedition to the martian surface. Recently, the use of electrochemical devices has been explored as a means of obtaining oxygen from the carbon dioxide-rich atmosphere. In these devices, oxygen ions diffuse through solid oxide membranes, thus, separating oxygen from the other gases presented. This phenomenon has only recently been explored as a means of obtaining large quantities of oxygen from toxic atmospheres, although first observed by Walter nernst in 1899. Nernst observed that stabilized zirconia will conduct oxygen ions when an electrical potential is applied across metallic electrodes applied to the ceramic membrane. Diatomic oxygen molecules are dissociated at the positive electrode/electrolyte interface. The oxygen ions enter the ceramic body due to the ion density gradient which is produced by the electrical potential across the electrolytic membrane. Once the ions have diffused through the membrane, they reform diatomic oxygen molecules at the anode. The separation of oxygen from carbon dioxide is achieved by the combination of thermal and electrochemical processes. The thermal decomposition of carbon dioxide (at 1000 C) results in the production of carbon monoxide and oxygen by the reaction.

Hooker, M. W.↗