DOE OSTI2022

A Fiber-Based 3D Lithium Host for Lean Electrolyte Lithium Metal Batteries

3D hosts are promising to extend the cycle life of lithium metal anodes but have rarely been implemented with lean electrolytes thus impacting the practical cell energy density. To overcome this challenge, a 3D host that is lightweight and easy to fabricate with optimum pore size that enables full utilization of its pore volume, essential for lean electrolyte operations, is reported. The host is fabricated by casting a VGCF (vapor-grown carbon fiber)-based slurry loaded with a sparingly soluble rubidium nitrate salt as an additive. The network of fibers generates uniform pores of ≈3 µm in diameter with a porosity of 80%, while the nitrate additive enhances lithiophilicity. This 3D host delivers an average coulombic efficiency of 99.36% at 1 mA cm -2 and 1 mAh cm -2 for over 860 cycles in half-cell tests. Full cells containing an anode with 1.35-fold excess lithium paired with LiNi 0.8 Mn 0.1 Co 0.1 O 2 (NMC811) cathodes exhibit capacity retention of 80% over 176 cycles at C/2 under a lean electrolyte condition of 3 g Ah -1 . This work provides a facile and scalable method to advance 3D lithium hosts closer to practical lithium-metal batteries.

36 MATERIALS SCIENCE↗

DOE OSTI2021

Examining CO 2 as an Additive for Solid Electrolyte Interphase Formation on Silicon Anodes

In this study, we demonstrate that the addition of CO 2 to a standard 1.0 M LiPF 6 3:7 wt% ethylene carbonate:ethyl methyl carbonate electrolyte results in the formation of a thinner insoluble solid electrolyte interphase (SEI) that is dominated by the presence of LiF. In contrast, cells without CO 2 result in a thicker insoluble SEI layer containing more organic constituents. The CO 2 is incorporated in the dimethyl carbonate soluble part of the SEI composed primarily of polymeric poly(ethylene oxide) (PEO) on the surface of a thin inorganic layer. This combination of properties from CO 2 addition provides an improved cycling performance through the reduction of irreversible side reactions, leading to higher coulombic efficiency. The results indicate that CO 2 incorporates into the SEI and plays a role similar to additives like fluorinated ethylene carbonate and vinylene carbonate with respect to polymeric components.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗

DOE OSTI2021

Alloying–realloying enabled high durability for Pt–Pd-3d-transition metal nanoparticle fuel cell catalysts

Abstract Alloying noble metals with non-noble metals enables high activity while reducing the cost of electrocatalysts in fuel cells. However, under fuel cell operating conditions, state-of-the-art oxygen reduction reaction alloy catalysts either feature high atomic percentages of noble metals (>70%) with limited durability or show poor durability when lower percentages of noble metals (<50%) are used. Here, we demonstrate a highly-durable alloy catalyst derived by alloying PtPd (<50%) with 3d-transition metals (Cu, Ni or Co) in ternary compositions. The origin of the high durability is probed by in-situ/operando high-energy synchrotron X-ray diffraction coupled with pair distribution function analysis of atomic phase structures and strains, revealing an important role of realloying in the compressively-strained single-phase alloy state despite the occurrence of dealloying. The implication of the finding, a striking departure from previous perceptions of phase-segregated noble metal skin or complete dealloying of non-noble metals, is the fulfilling of the promise of alloy catalysts for mass commercialization of fuel cells.

25 ENERGY STORAGE↗