Superconducting phase diagram in Bi x Ni 1 – x thin films: The effects of Bi stoichiometry on superconductivity
The Bi-Ni binary system has been of interest due to possible unconventional superconductivity aroused therein, such as time-reversal symmetry breaking in Bi/Ni bilayers or the coexistence of superconductivity and ferromagnetism in Bi 3 Ni crystals. While Ni acts as a ferromagnetic element in such systems, the role of the strong spin-orbit coupling element Bi in superconductivity has remained unexplored. In this work, we systematically studied the effects of Bi stoichiometry on the superconductivity of Bi x Ni 1–x thin films (x ≈ 0.5–0.9) fabricated via a composition-spread approach. Here, the superconducting phase map of Bi x Ni 1–x thin films exhibited a superconducting composition region attributable to the intermetallic Bi 3 Ni phase with different amounts of excess Bi, revealed by synchrotron x-ray diffraction analysis. Interestingly, the mixed-phase region with Bi 3 Ni and Bi showed unusual increases in the superconducting transition temperature and residual resistance ratio as more Bi impurities were included, with the maximum T c (=4.2K) observed at x ≈ 0.79. A correlation analysis of structural, electrical, and magneto-transport characteristics across the composition variation revealed that the unusual superconducting “dome” is due to two competing roles of Bi: impurity scattering and carrier doping. We found that the carrier doping effect is dominant in the mild doping regime (0.74 ≤ x ≤ 0.79), while impurity scattering becomes more pronounced at larger Bi stoichiometry.