Comparative Mechanical Properties Analysis of Triple Ion-Beam Irradiated and Neutron Irradiated Potential Plasma Facing Components

Abstract Several classes of materials are being proposed for use in fusion reactors including oxide dispersion strengthened (ODS) and reduced activation ferritic-martensitic (RAF/M) steels to withstand the severe and harsh conditions. In this work, the mechanical properties of a Fe-16Cr-4Al-2W-0.3Ti-0.3Y 2 O 3 (K3) (ODS) ferritic steel and a Fe-8.9Cr-1.1W-0.47Mn-0.2V-0.14Ta-0.11C (Eurofer 97) (RAF/M) steel) after triple ion beam irradiation were locally evaluated utilizing in-situ micro-pillar compression tests, and continuous stiffness/quasi-static nanoindentation. No change in mechanical properties was observed in the K3 ODS steel. However, the Eurofer 97 RAF/M steel exhibited radiation-induced effects via increases in yield strength. Micro-pillar techniques were expanded to neutron-irradiated materials via an in-situ testing technique employing lift-out methods on Fe-14Cr-0.9Ti-0.3Mo-0.25Y 2 O 3 (MA957) ODS ferritic steel. Both the non-irradiated and irradiated compressive yield stresses of the MA 957 micro-pillars were in good agreement with bulk yield stress values reported in the literature, suggesting that the lift-out micro-pillar compression testing technique is a promising method. The demonstration of these techniques on ion beam and neutron irradiated ODS steels and ion beam RAF/M steels gives information to inform models of the material degradation during use in a fusion device.

alloys↗
DOE OSTI2023

In situ measurements of non-equilibrium positron state defects during He irradiation in Si

Radiation-induced property changes in materials originate from the energy transfer from an incoming particle to the existing lattice, displacing atoms. The displaced atoms can cause the formation of extended defects including dislocation loops, voids, or precipitates. The non-equilibrium defects created during damage events determine the extent of these larger defects and are a function of dose rate, material, and temperature. However, these defects are transient and can only be probed indirectly. Herein, we present direct experimental measurements and evidence of irradiated non-equilibrium vacancy formation, where in situ positron annihilation spectroscopy was used to prove the generation of non-equilibrium defects in silicon.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Dose and dose rate effects on the microstructural and mechanical stability of long-range ordered precipitates in Inconel 718

Nickel-based alloys offer exceptional mechanical properties and corrosion resistance for various applications in extreme environments such as high neutron flux, temperature, and stress. Precipitates, resulting from thermal treatments, increase the strength and creep resistance of these alloys. Here, heavy ion irradiation is shown to destabilize the γ' and γ" precipitates in Inconel 718 nickel-based alloy by disordering and dissolution processes. Transmission electron microscopy and atom probe tomography reveal that the disordering and dissolution rates of the precipitates are proportional to both irradiation dose and dose rate. Irradiation induced disordering occurs at a higher rate than the dissolution. From analyzing the hardening contributions, microscale mechanical results suggest radiation-induced disordering is responsible for the majority of the softening response at low dose. In addition, low dose radiation-induced disordering results in strain localization and is believed to be the primary cause for the drastic degradation of uniform elongation and toughness in irradiated Inconel 718.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Post-irradiation characterization of a high burnup mixed oxide fuel rod with minor actinides

The Advanced Fuels Campaign performed a series of irradiation tests of minor actinide-bearing mixed oxide fuel (MA-MOX), the so-called AFC-2C&D experiments, to investigate the transmutation of long-lived transuranic actinide isotopes contained in spent nuclear fuel via fast reactor technology at burnups exceeding 10 % fission of initial metallic atoms. This manuscript reports the test results derived from one of the five MA-MOX rodlets taken to higher burnup in the AFC-2D irradiation. This includes both non-destructive investigations, such as gamma and neutron spectrometry, and destructive investigations, such as fission gas release, ceramography, and chemical burnup analysis. In addition, the microstructure of the fuel was investigated using advanced electron microscopy techniques including electron backscatter diffraction (EBSD) and transmission electron microscopy (TEM). Here, it was observed with EBSD that the pellet had subdivision of the grains and the TEM observed migration of cladding material into the 5 metal precipitates in the fuel which could have been from the higher than desired oxygen/metal ratio. The TEM also showed an enrichment of Cr in fuel clad chemical interaction (FCCI) layer.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2021

Neutron irradiation induced defects in oxides and their impact on the oxide properties

Understanding the irradiation-induced defects in oxides is of interest for a wide range of applications. ZnO is an interesting oxide with mixed ionic and covalent bonding that contains a variety of point defect structures—making it an excellent model for studying irradiation-induced defects and their impact on properties. Here, we investigate the effects of neutron irradiation on the formation of defects and on the structural, optical, and electrical properties of ZnO single crystals. We observe the formation of vacancies and voids via positron annihilation spectroscopy. Neutron irradiation led to a significant deterioration of the ZnO structure and formed a high concentration of point defects, vacancy clusters, and voids with large disparities in their structure across variable irradiation times. It also led to significant changes in the optical properties and sample color. Irradiation for 444 h induced a high concentration of Cu acceptors as well as a high concentration of Ga donors. Additionally, temperature-dependent Hall effect measurements revealed the competing production of donors and acceptors and showed an increase in the slope of the carrier freeze-out curve with increasing irradiation dose. This work demonstrates the combined effects of neutron irradiation in producing a wide range of structural defects, impurities, and dopants in oxides and their enormous impact on modifying the oxide structure and both the optical and electronic properties. It particularly emphasizes the importance of considering the production of new impurities and dopants during the neutron irradiation of oxides.

72 PHYSICS OF ELEMENTARY PARTICLES AND FIELDS↗
DOE OSTI2021

Effects of radiation damage and precipitate distribution on micro-pillar compression testing of irradiated CuCrZr

The results of small-scale mechanical tests are convoluted by the so-called size effect, whereby materials appear stronger when the scale of the test is reduced to the order of microns or less. The dimensional range over which this occurs has been shown to be linked to a change in sample microstructure, such as the addition of defects induced by irradiation. To investigate this response, a CuCrZr alloy was subjected to proton irradiation and mechanically tested using micro compression of pillars with a range in size. It was found that irradiation defects dominate over the extrinsic size effect and the sensitivity to differences in precipitate microstructure was also somewhat reduced, suggesting that size-independent results could be obtained from much smaller test volumes in irradiated material compared to their non-irradiated counterparts. Lastly, comparison was made between the increase in yield strength predicted by models and the experimentally measured values to establish the key parameters driving the strengthening behaviour.

36 MATERIALS SCIENCE↗
DOE OSTI2021

The effects of microstructures and radiation damage on the deformation behavior of a HT-9 alloy using microtensile testing

Understanding the influence of radiation damage on the mechanical properties of HT-9 and other tempered martensitic alloys is part of the mission in developing radiation-tolerant materials for the next generation of nuclear reactors. Although there has been extensive data on the macroscopic mechanical properties of the irradiated HT-9 alloys and microstructural changes, it is not well-understood how radiation damage and the resulting microstructural changes influence the local mechanical properties. In this study, we utilized in situ SEM microtensile testing to investigate the deformation behavior of specific martensitic boundaries in 1 dpa proton-irradiated HT-9 and answered the question of what is the weakest link. Additionally, we provided the direct observation of the failure modes of microtensiles containing high angle and low angle martensitic boundaries. In the unirradiated condition, the deformation is ductile and no martensitic boundary failure is observed. In the irradiated condition, the high angle martensitic boundaries are more susceptible to radiation-induced boundary failure as compared to the low angle martensitic boundaries.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2020

A new mechanism for void-cascade interaction from nondestructive depth-resolved atomic-scale measurements of ion irradiation–induced defects in Fe

The nondestructive investigation of single vacancies and vacancy clusters in ion-irradiated samples requires a depth-resolved probe with atomic sensitivity to defects. The recent development of short-pulsed positron beams provides such a probe. Here, we combine depth-resolved Doppler broadening and positron annihilation lifetime spectroscopies to identify vacancy clusters in ion-irradiated Fe and measure their density as a function of depth. Despite large concentrations of dislocations and voids in the pristine samples, positron annihilation measurements uncovered the structure of vacancy clusters and the change in their size and density with irradiation dose. When combined with transmission electron microscopy measurements, the study demonstrates an association between the increase in the density of small vacancy clusters with irradiation and a remarkable reduction in the size of large voids. This, previously unknown, mechanism for the interaction of cascade damage with voids in ion-irradiated materials is a consequence of the high porosity of the initial microstructure.

36 MATERIALS SCIENCE↗
DOE OSTI2020

Measurement and Simulation of Vacancy Formation in 2-MeV Self-irradiated Pure Fe

Positron annihilation spectroscopy is a powerful tool to quantify the amount of vacancies and vacancy clusters in materials. The technique has been utilized to study the induced defects in materials after ion beam and neutron irradiations. Here we make the case for how the technique can and should be utilized to quantify the defects created by irradiation in situ during irradiation to foster a more thorough understanding of the surviving defects after initial collision cascades. This paper outlines a future experimental approach and its meaning for the nuclear materials community, being able to benchmark commonly used rate theory models of damage evolution.

36 MATERIALS SCIENCE↗
DOE OSTI2020

Cryogenic Stress-Driven Grain Growth Observed via Microcompression with in situ Electron Backscatter Diffraction

The deformation of materials at cryogenic temperature is of interest for space, arctic, and fundamental science applications. In this work, a custom-built cooling system attached to a commercial picoindenter was used for in situ cryogenic microcompression testing of equal-channel angular-pressed copper with real-time electron backscatter diffraction. Stress-driven grain growth at cryogenic temperatures was observed during a series of elastic and plastic deformations. Finally, these results provide direct evidence for the previously predicted phenomenon, whereas previous ex situ examinations demonstrated coarsening after cryogenic loading when samples were not maintained at cryogenic temperatures between deformation and characterization.

36 MATERIALS SCIENCE↗