Hossain, Md Alamgir | Search NASA

DOE OSTI2024

Insights into Preceramic Polymer-Based Additive Manufacturing Inks via Rheological and Scattering Studies of Preceramic Polymer-Grafted Nanoparticles Suspended in Polycarbosilane

Preceramic polymers (PCPs) offer advantages in producing ceramics due to their processability and ability to tailor the final chemistry of the produced material. However, challenges such as volumetric shrinkage and mass loss during pyrolysis often result in polymer-derived ceramics containing pores and cracks. PCP-grafted ceramic nanoparticles (PCPGNPs) have been proposed and studied as a route to mitigate the shrinkage issues associated with neat PCPs. Prior studies on PCPGNPs have principally focused on the synthesis and characterization of neat materials. Dispersing PCPGNPs in commercial preceramic polymer is another attractive, but underexplored, route to control the rheological and char yield properties of PCP systems. In this work, a systematic rheological study of commercial PCP (SMP-877) and PCPGNP (silica with poly(1,1-dimethylpropylsilane) corona) mixtures was executed to develop design rules for the processing of such systems. A rheological study demonstrated the effect of increasing particle concentration on network formation with percolation occurring between 50 and 60 wt %. Samples above the percolation threshold exhibited higher viscosities and rapid shear thinning thus demonstrating their direct-write printability. X-ray photon correlation spectroscopy (XPCS) corroborated the rheology and showed two diffusive modes when the material was above percolation. Mixtures of PCPGNPs and SMP-877 had synergistically higher char yields upon thermal treatment and pyrolysis. XPCS and rheological measurements during thermal treatment identified thermal jamming of the polymer grafts as a key factor in improving the char yield. In conclusion, with the insights gained here, we expect these mixed systems to provide attractive feedstocks for polymer-derived ceramics, with proof-of-principal application as feedstocks for direct ink write (DIW) additive manufacturing.

36 MATERIALS SCIENCE↗

DOE OSTI2020

Chemical-Biological Cyclic Process for Hexavalent Chromium Reduction to Trivalent Chromium in Aqueous Medium - 20224

Conventional treatment of chromium contamination focuses on immobilization of the highly toxic and water-soluble form Cr(VI), by reducing it to the relatively less toxic and less mobile trivalent form, Cr(III), using reducing compounds like ferrous sulfate or ferrous iron, Fe(II). The Cr(VI) also respond to biodegradation and subsequent reduction. During the reduction reaction, Fe(II) is oxidized to ferric, Fe(III), which, being at the highest oxidation state, has no ability to reduce Cr(VI), and therefore remediation process terminates. The good news is that metal-reducing bacteria, S. oneidensis MR-1, can regenerate Fe(II) from Fe(III) with the help of an organic electron donor in an appropriate bacterial media. Thus, in the Cr(VI) chemical remediation process, Fe(II) to Fe(III) conversion is reversed by the biological process, regenerating Fe(II) and the Cr(VI) chemical reduction process continues in a cyclic fashion. This study presents the results of regeneration of Fe(II) from fresh Fe(III) as well as from the reaction products of Cr(VI) and Fe(II). Both fresh Fe(III) and reaction product Fe(III) exhibited the same reduction behavior. Fe(II) production increased with the increase of initial concentration of Fe(III), resulting in 87.5% Fe(II) regeneration. The extent of Fe(III) reduction (Fe(II)t/Fe(III)0.hour) was 21 times higher than the extent of Cr(VI) reduction (Cr(VI)t/Cr(VI)0.hour) by S. oneidensis MR-1. In a cyclic process of sequential Cr(VI) addition, the amount of Fe(II) regeneration decreased with the increase in cycle number, a fixed quantity of starting S. oneidensis MR-1 could regenerate Fe(II) at least five times in a ten-hour period. More importantly, regenerated Fe(II) instantly reduced Cr(VI) to Cr(III). So, Fe(II) regeneration with metal-reducing bacteria has a good potential for application in groundwater and wastewater remediation in reducing Cr(VI) to Cr(III). As a comparison of chemical to biological transformation, chemical transformation of Cr(VI) by Fe(II) was almost 600 times greater than that of biological transformation. Therefore a chemical-biological cyclic process offers potential applications for remediation of groundwater and hexavalent chromium contaminated waste sites. (authors)

12 MANAGEMENT OF RADIOACTIVE AND NON-RADIOACTIVE W↗