Effects of dust accumulation and removal on radiators surfaces on Mars

Tests were carried out to assess the impact of wind blown dust accumulation and abrasion on radiator surfaces on Mars. High emittance arc-textured copper and niobium-1 percent-zirconium samples were subjected to basaltic dust laden wind at Martian pressure (1000 Pa) at speeds varying from 19 to 97 m/s in the Martian Surface Wind Tunnel. The effect of accumulated dust was also observed by pre-dusting some of the samples before the test. Radiator degradation was determined by measuring the change in the emittance after dust was deposited and/or removed. The principle mode of degradation was abrasion. Arc textured Nb-1 percent-Zr proved to be more susceptible to degradation than Cu, and pre-dusting appeared to have lessened the abrasion.

Gaier, James R.↗

NASA NTRS1991

Effects of dust accumulation and removal on radiator surfaces on Mars

Gaier, James R.↗

NASA NTRS1990

Aeolian removal of dust from radiator surfaces on Mars

Simulated radiator surfaces made of arc-textured Cu and Nb-1 percent-Zr and ion beam textured graphite and C-C composite were fabricated and their integrated spectral emittance characterized from 300 to 3000 K. A thin layer of aluminum oxide, basalt, or iron (III) oxide dust was then deposited on them, and they were subjected to low pressure winds in the Martian Surface Wind Tunnel. It was found that dust deposited on simulated radiator surfaces may or may not seriously lower their integrated spectral emittance, depending upon the characteristics of the dust. With Al2O3 there is no appreciable degradation of emittance on a dusted sample, with basaltic dust there is a 10 to 20 percent degradation, and with Fe2O3 a 20 to 40 percent degradation. It was also found that very high winds on dusted highly textured surfaces can result in their abrasion. Degradation in emittance due to abrasion was found to vary with radiator material. Arc-textured Cu and Nb-1 percent Zr was found to be more susceptible to emittance degradation than graphite or C-C composite. The most abrasion occurred at low angles, peaking at the 22.5 deg test samples.

Gaier, James R.↗

NASA NTRS1990

High emittance surfaces for high temperature space radiator applications

Surface modification techniques are evaluated for emittance enhancement of radiator surfaces. These techniques include acid etching, heat treating, abrasion, sputter texturing, electrochemical texturing, arc texturing, and atomic oxygen beam texturing. Candidate radiator surface materials under consideration include Nb-1 pct Zr, Cu, Ti, Ti-6 pct Al-4 pct V, 304 stainless steel, Al6061-T6, Mo, W, and Ta.

Banks, Bruce A.↗

NASA NTRS1988

Arc-textured metal surfaces for high thermal emittance space radiators

Carbon arc electrical discharges struck across the surfaces of metals such as Nb-1 percent Zr, alter the morphology to produce a high thermal emittance surface. Metal from the surface and carbon from the arc electrode vaporize during arcing, and then condense on the metal surface to produce a microscopically rough surface having a high thermal emittance. Quantitative spectral reflectance measurements from 0.33 to 15 microns were made on metal surfaces which were carbon arc treated in an inert gas environment. The resulting spectral reflectance data were then used to calculate thermal emittance as a function of temperature for various methods of arc treatment. The results of arc treatment on various metals are presented for both ac and dc arcs. Surface characterization data, including thermal emittance as a function of temperature, scanning electron microscopy, and atomic oxygen durability, are also presented. The ac arc texturing was found to increase the thermal emittance at 800 K from 0.05 to 0.70.

Banks, Bruce A.↗

NASA NTRS1987

An evaluation of candidate oxidation resistant materials

Ground based testing of materials considered for Kapton solar array blanket protection, graphite epoxy structural member protection, and high temperature radiators was performed in an RF plasma asher. Ashing rates for Kapton were correlated with rates measured on STS-8 to determine the exposure time equivalent to one year in low Earth orbit (LEO) at a constant density space station orbital flux. Protective coatings on Kapton from Tekmat, Andus Corporation, and LeRC were evaluated in the plasma asher and mass loss rates per unit area were measured for each sample. All samples evaluated provided some protection to the underlying surface but ion beam sputter deposited samples of SiO2 and SiO2 with 8% polytetrafluoroethylene (PTFE) showed no evidence of degradation after 47 hours of exposure. Mica paint was evaluated as a protective coating for graphite epoxy structural members. Mica appears to be resistant to attack by atomic oxygen but only offers some limited protection as a paint because the paint vehicles evaluated to date were not resistant to atomic oxygen. Four materials were selected for evaluation as candidate radiator materials: stainless steel, copper, niobium-1% zirconium, and titanium-6% aluminum-4% vanadium. These materials were surface textured by various means to improve their emittance. Emittances as high as 0.93 at 2.5 microns for stainless steel and 0.89 at 2.5 microns for Nb-1 Zr were obtained from surface texturing. There were no significant changes in emittance after asher exposure.

Rutledge, Sharon↗

NASA NTRS1987

High temperature radiator materials for applications in the low Earth orbital environment

Radiators must be constructed of materials which have high emittance in order to efficiently radiate heat from high temperature space power systems. In addition, if these radiators are to be used for applications in the low Earth orbital environment, they must not be detrimentally affected by exposure to atomic oxygen. Four materials selected as candidate radiator materials (304 stainless steel, copper, titanium-6% aluminum-4% vanadium (Ti-6%Al-4%V), and niobium-1% zirconium (Nb-1%Zr)) were surface modified by acid etching, heat treating, abrading, sputter texturing, electrochemical etching, and combinations of the above in order to improve their emittance. Combination treatment techniques with heat treating as the second treatment provided about a factor of two improvement in emittance for 304 stainless steel, Ti-6%Al-4%V, and Nb-1%Zr. A factor of three improvement in emittance occurred for discharge chamber sputter textured copper. Exposure to atomic oxygen in an RF plasma asher did not significantly change the emittance of those samples that had been heat treated as part of their texturing process. An evaluation of oxygen penetration is needed to understand how oxidation affects the mechanical properties of these materials when heat treated.

Rutledge, Sharon K.↗

NASA NTRS1986

An evaluation of candidate oxidation resistant materials for space applications in LEO

Ground based testing of materials considered for polyimide (Kapton) solar array blanket protection and graphite-epoxy stroctural member protection was performed in an RF plasma asher. Protective coatings on Kapton from various commercial sources and from NASA Lewis Research Center were exposed to the air plasma; and mass loss per unit area was measured for each sample. All samples evaluated provided some protection to the underlying surface, but metal-oxide-fluoropolymer coatings provided the best protection by exhibiting very little degradation after 47 hr of asher exposure. Mica paint was evaluated as a protective coating for graphite-epoxy structural members. Mica appeared to be resistant to attack by atomic oxygen, but only offered limited protection as a paint. this is believed to be due to the paint vehicle ashing underneath the mica leaving unattached mica flakes lying on the surface. The protective coatings on Kapton evaluated so far are promising but further research on protection of graphite-epoxy support structures is needed.

Rutledge, Sharon↗