Dynamic Deformation in Nuclear Graphite and Underlying Mechanisms
Time-dependent deformation in nuclear graphite is influenced by the creation and migration of radiation-induced defects in the reactor environment. This study investigates the role of pre-existing defects such as point defect clusters and Mrozowski cracks in nuclear graphite IG-110. Separate specimens were irradiated with a 2.8 MeV Au 2+ beam with a fluence of 4.38 × 10 14 cm −2 and an 8 MeV C 2+ beam with a fluence of 1.24 × 10 16 cm −2 . Microscopic specimens were either mechanically loaded inside a transmission electron microscope (TEM) or subjected to ex situ indentation-based creep loading. In situ TEM tests showed significant plasticity in regions highly localized around the Mrozowski cracks, resembling slip or ripplocation bands. Slip bands were also seen near regions without pre-existing defects but at very high stresses. Ex situ self-ion irradiation embrittled the specimens and decreased the creep displacement and rate, while heavy ion irradiation resulted in the opposite behavior. We hypothesize that the large-sized gold ions (compared to the carbon atoms) induced interplanar swelling as well as cross-plane channels for increased defect mobility. These findings illustrate the role of pre-existing defects in the dynamic relaxation of stresses during irradiation and the need for more studies into the radiation environment’s impact on the mechanical response of nuclear graphite.