9 records

NASA NTRS1993

Superconductivity devices: Commercial use of space

The processing and screen printing of the superconducting BSCCO and 123 YBCO materials on substrates is described. The resulting superconducting properties and the use of these materials as possible electrode materials for ferroelectrics at 77 K are evaluated. Also, work performed in the development of solid-state electromechanical actuators is reported. Specific details include the fabrication and processing of high strain PBZT and PLZT electrostrictive materials, the development of PSZT and PMN-based ceramics, and the testing and evaluation of these electrostrictive materials. Finally, the results of studies on a new processing technology for preparing piezoelectric and electrostrictive ceramic materials are summarized. The process involves a high temperature chemical reduction which leads to an internal pre-stressing of the oxide wafer. These reduced and internally biased oxide wafers (RAINBOW) can produce bending-mode actuator devices which possess a factor of ten more displacement and load bearing capacity than present-day benders.

Haertling, Gene↗

NASA NTRS1993

Superconductivity devices: Commercial use of space

A YBCO thick film containing 20 percent Ag2O with a T(sub c) of 86.8 K and J(sub c) of 108 A/sq cm was obtained. The film was fabricated by a two-step firing process, i.e., firing the film at 1000 C for 10 minutes and annealing at 970 C for 30 minutes. The two-step firing process, however, was not suitable for the multiple-lead YBCO sample due to the formation of the 211 green phase at 1000 C in the multiple-lead YBCO sample. A BSCCO thick film printed on a MgO coated MSZ substrate and fired at 845 C for 2 hours exhibited a superconducting behavior at 89 K. Because of its porous microstructure, the critical current density of the BSCCO thick film was limited. This report also includes the results of the YBCO and BSCCO materials used as oxide electrodes for ferroelectric materials. The YBCO electroded PLZT showed higher remanent polarization and coercive field than the sample electroded with silver paste. A higher Curie temperature for the PLZT was obtained from the YBCO electroded sample. The BSCCO electroded sample, however, exhibited the same Curie temperature as that of a silver electroded sample. Dissipation factors of the ferroelectric samples increased when the oxide electrode was applied.

Haertling, Gene↗

NASA NTRS1992

Superconductivity devices: Commercial use of space

High T sub C superconducting thick film were prepared by a screen printing process. Y-based (YBa2Cu3O(7-x) superconducting thick film were printed on 211/Al2O3, SNT/Al2O3, and YSZ substrates. Because of poor adhesion of the superconductor thick films to 211/Al2O3 and SNT/Al2O3 substrates, relatively low T sub C and J sub C values were obtained from the films printed on these substrates. Critical temperatures (T sub C) of YBa2Cu3O(7-x) thick films deposited on 211/Al2O3 and SNT/Al2O3 substrates were about 80 K. The critical current densities (J sub C) of these films were less than 2 A/sq cm. Higher T sub C and J sub C YBa2Cu3O(7-x) thick films were printed on YSZ substrates. A YBa2Cu3O(7-x) thick film with T sub C=86.4 and J sub C= 50.4 A/sq cm was prepared by printing the film on YSZ substrate and firing at 990 C for 10 minutes. Multiple-lead samples were also prepared on the YSZ substrates. The multiple-lead samples showed lower T sub C and/or J sub C values than those of the plain samples. The electrical properties of YBa2Cu3O(7-x) thick films were determined by the microstructures of the films. The YBa2Cu3O(7-x) thick films printed on the YSZ substrates, which had the best properties among the films printed on the three different kinds of substrates, had the highest density and the best particle interconnection. The YBa2Cu3O(7-x) thick films with preferred orientation in (001) direction were obtained on the YSZ substrates. Cracks, which retard the properties of the films, were found from the films deposited on the YSZ substrates. Currently, a MSZ (Magnesium Stabilized Zirconia) substrate, which had higher thermal expansion coefficient than the YSZ substrate, is used as substrate for the YBa2Cu3O(7-x) thick film in order to eliminate the cracks on the film. Bi-based superconductor thick films were printed on polycrystalline MgO and YSZ substrates. Interactions between BSCCO thick films and the YSZ substrates were observed. Various buffer layer materials were applied onto the substrates in order to avoid the interactions between the BSCCO thick films and the ZrO2-based substrates. So far, a BSCCO printed on MgO substrate with T Sub C=89K was obtained. The J sub C of the film was lower than 0.1 A/sq cm by reason of poor interconnectivity of the BSCCO particles.

Haertling, Gene↗

NASA NTRS1992

Superconductivity devices: Commercial use of space

The high T(sub c) superconducting ceramic materials, developed in 1987, are now being extensively investigated for a variety of engineering applications. These applications include such devices as conducting links, rotating and linear bearings, sensors, filters, switches, high Q cavities, magnets, and motors. Some of these devices take advantage of the material's ability to lose all electrical resistance at a critical temperature, T(sub c), while others make use of the repulsion forces generated between the magnetic field of a permanent magnet and a superconductor which is cooled below its T(sub c), Meissner effect. This report describes the work accomplished to date by: (1) reviewing the present state of the art in actuator technology, (2) evaluating processing and fabrication of high strain electrostrictive materials, and (3) testing these electrostrictive materials.

Haertling, Gene↗

NASA NTRS1992

Screen printed Y and Bi-based superconductors

High T(sub c) superconducting thick film was prepared by screen printing process. Y-based (YBa2Cu3O(7 - x)) superconducting thick films were printed on 211/Al2O3, SNT/Al2O3, and YSZ substrates. Because of poor adhesion of the superconducting thick films to 211/Al2O3 and SNT/Al2O3 substrates, relatively low T(sub c) and J(sub c) values were obtained from the films printed on these substrates. Critical temperatures of YBa2Cu3O(7 - x) thick films deposited on 211/Al2O3 and SNT/Al2O3 substrates were about 80 K. The critical current densities of these films were less than 2 A/cm(exp 2). Higher T(sub c) and J(sub c) films were printed on the YSZ substrates; T(sub c) = 86.4 K and J(sub c) = 50.4 A/cm(exp 2). Multiple lead samples were also prepared on the YSZ substrates. These showed lower T(sub c) and J(sub c) values than plain samples. The heat treatment conditions of the multiple lead samples are still under investigation. Bi-based superconductor thick films have been obtained so far. Improving the superconducting properties of the BSCCO screen printed thick films will be emphasized in future work.

Haertling, Gene H.↗

NASA NTRS1992

Environmental test program for superconducting materials and devices

A systematic approach to obtaining real time, superconducting YBa2Cu30(7-x) materials is presented. The work was carried out under the overall direction of Clemson University with tasks being performed at both Clemson and Westinghouse (Aiken, SC). Clemson prepared the tapecast superconducting 123 material and fabricated in into substrate-supported, environmentally-protected conducting links. Following this, all of the elements were individually tested for resistance vs. temperature and Tc; and then a portion of them were kept at Clemson for further testing while a randomly selected group was delivered to Westinghouse for specialized testing and evaluation in their low temperature/high vacuum and radiation facilities. In addition, a number of control samples (12 ea.) were put on the shelf at Clemson for further reference at the end of the testing period. The specific tests conducted at Clemson and Westinghouse/SRC are presented with a summary of the results.

Haertling, Gene↗

NASA NTRS1991

Environmental test program for superconducting materials and devices

This report is divided into two parts. The first dealing with work involved with Clemson University and the second with the results from Westinghouse/Savannah River. Both areas of work involved low noise, low thermal conductivity superconducting grounding links used in the NASA-sponsored Spectroscopy of the Atmosphere using Far Infrared Emission (SAFIRE) Project. Clemson prepared the links from YBa2Cu3O(7-x) superconductor tape that was mounted on a printed circuit board and encapsulated with epoxy resin. The Clemson program includes temperature vs. resistance, liquid nitrogen immersion, water immersion, thermal cycling, humidity, and radiation testing. The evaluation of the links under a long term environmental test program is described. The Savannah River program includes gamma irradiation, vibration, and long-term evaluation. The progress made in these evaluations is discussed.

Haertling, Gene↗

NASA NTRS1991

A new method for measuring low resistivity contacts between silver and YBa2Cu3O(7-x) superconductor

Several methods of measuring contact resistivity between silver electrodes and YBa2Cu3O(7-x) superconductors were investigated; including the two-point, the three point, and the lap-joint methods. The lap-joint method was found to yield the most consistent and reliable results and is proposed as a new technique for this measurement. Painting, embedding, and melting methods were used to apply the electrodes to the superconductor. Silver electrodes produced good ohmic contacts to YBa2Cu3O(7-x) superconductors with contact resistivities as low as 1.9 x 10 to the -9th ohm sq cm.

Hsi, Chi-Shiung↗

NASA NTRS1991

Low resistivity contacts to YBa2Cu3O(7-x) superconductors

Silver, gold, platinum, and palladium metals were investigated as electroding materials for the YBa2Cu3O(7-x) superconductors. Painting, embedding, and melting techniques were used to apply the electrodes. Contact resistivities were determined by: (1) type of electrode; (2) firing conditions; and (3) application method. Electrodes fired for long times exhibited lower contact resistivities than those fired for short times. Low-resistivity contacts were found for silver and gold electrodes. Silver, which made good ohmic contact to the YBa2Cu3O(7-x) superconductor with low contact resistivities was found to be the best electroding material among the materials evaluated in this investigation.

Hsi, Chi-Shiung↗