DOE OSTI2022

Broad Applicability of Electrochemical Impedance Spectroscopy to the Measurement of Oxygen Nonstoichiometry in Mixed Ion and Electron Conductors

Oxygen non-stoichiometry is a fundamental feature of mixed ion and electron conductors (MIECs). In this work a general electrochemical method for determining non-stoichiometry in thin film MIECs, via measurement of the chemical capacitance, is demonstrated using ceria and ceria-zirconia (Ce 0.8 Zr 0.2 O 2-δ ) as representative materials. A.C. impedance data are collected from both materials at high temperature (750-900 °C) under reducing conditions with oxygen partial pressure (pO 2 ) in the range 10-13 to 10-20 atm. Additional measurements of ceria-zirconia films are made under relatively oxidizing conditions with pO 2 in the range 0.2 to 10 -4 atm and temperatures of 800-900 °C. Under reducing conditions, the impedance spectra are described by a simple circuit in which a resistor is in series with a resistor and capacitor in parallel, and thickness dependent measurements are used to resolve the capacitance into interfacial and chemical terms. Under more oxidizing conditions, the impedance spectra (of Ce 0.8 Zr 0.2 O 2-δ ) reveal an additional diffusional feature, which enables determination of the ionic resistance of the film in addition to the capacitance, and hence the transport properties. A generalized mathematical formalism is presented for recovering the non-stoichiometry from the chemical capacitance, without recourse to defect chemical models. The ceria non-stoichiometry values are in good agreement with literature values determined by thermogravimetric measurements but display considerably less scatter and are collected on considerably shorter timescales. Here, the thermodynamic analysis of Ce 0.8 Zr 0.2 O 2-δ corroborates earlier findings that introduction of Zr into ceria enhances its reducibility.

08 HYDROGEN↗

DOE OSTI2021

High-throughput characterization of Lu-doped zirconia

Lu-doped zirconia (LuDZ) was reported in the 1960s to be a poor oxygen ion conductor. However, we identified this system as worthy of reexamination based on the results of a machine learning-based screen for promising oxygen ion conductors, further supported by a physical argument: because Lu is the heaviest and smallest of the lanthanides, it should offer the possibility of high conductivity due to its high polarizability and size compatibility with the zirconia structure. Here the relationship between dopant concentration and conductivity in the LuDZ system was determined using a high throughput experimental methodology in which spatially resolved conductivity was measured across a compositionally graded film, spanning from Zr 0.93 Lu 0.07 O 1.965 to Zr 0.82 Lu 0.18 O 1.91 . The conductivity broadly peaks with composition at 15 cation % Lu, coinciding with the approximate phase boundary of the fully stabilized cubic phase. The composition-dependent conductivity measurements reveal a surprising increase in activation energy for ion transport with increasing Lu content with no change in this trend at the composition of the conductivity maximum. The pre-exponential factor increases sharply with Lu content, but displays a distinct plateau once the conductivity maximum composition is attained. At 500 °C, the conductivity of Zr 0.85 Lu 0.15 O 1.925 is 2 × 10 –3 S cm –1 , approaching that of optimally doped Sc-stabilized zirconia, which has the highest reported conductivity among zirconia compounds. In comparison to other oxide ion conductors, Lu-stabilized zirconia offers the advantage over ceria of negligible electronic conductivity and is easier to process than (La,Sr)(Ga,Mg)O 3-δ .

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗

DOE OSTI2021

Local Multimodal Electro-Chemical-Structural Characterization of Solid-Electrolyte Grain Boundaries

Typical models of polycrystalline ionic materials treat the grain boundary properties as single valued, without consideration of the full range of values that define the macroscopically measured average. Here a unique experimental platform suitable for local multimodal characterization of individual grain boundaries in bicrystal fibers is reported. A variation of three orders of magnitude in the grain boundary conductivity of ceria is observed, as measured across six individual bicrystals by both alternating current impedance spectroscopy and direct current (D.C.) linear sweep voltammetry. Nonlinear behavior of the D.C. measurements is consistent with resistance due to a space charge effect. Time-of-flight secondary ion beam spectroscopy reveals a correlation between grain boundary resistance and the concentration of impurities Si, Al, and Ca segregated at the grain boundaries, although the bulk concentrations of these impurities are negligible. Electron backscatter diffraction analysis of the crystal orientations suggests a correlation between the misorientation across the grain boundaries and grain boundary resistance. These correlations point towards a grain boundary resistance that arises from impurity-generated space charge effects and variations in impurity concentration and hence resistivity driven by the energetics of impurity segregation to grain boundaries of differing surface energies.

36 MATERIALS SCIENCE↗