Fundamentals of dendritic solidification. I - Steady-state tip growth. II - Development of sidebranch structure

Systematic measurements of dendrite tip radius and growth velocity in succinonitrile reveal that consideration of dendrite tip stability should be incorporated into the heat transfer theory to determine the steady-state dendritic growth condition. The dendritic stability criterion measured is 2 alpha d0/VR squared = 0.0195, where V is the dendritic growth velocity, R is the dendritic tip radius, alpha is the liquid thermal diffusivity, and d0 is a capillary length defined in the text. Several dendritic stability models are reviewed and discussed in comparison to the present experimental results.

Huang, S.-C.↗

NASA NTRS1979

Convection and diffusion effects during dendritic solidification

A report is presented of the first quantitative measurements of dendritic growth at supercooling levels where convection instead of diffusion is the controlling heat transfer mechanism. Precautions similar to that used in an investigation conducted by Glicksman et al. (1976) were taken to insure 'free' dendritic growth conditions. Dendritic growth velocity was measured as a function of growth orientation at seventeen supercoolings which ranged from 0.043 C to 2 C. Selected but representative measurements of velocity versus orientation angle are shown in a graph. The relative growth velocity of a downward growing dendrite is found to be greater than that of a diffusion-limited dendrite. This result is consistent with that expected from the enhanced heat transfer arising from natural convection.

Glicksman, M. E.↗