NASA NTRS1972

Superconductivity in thin films of the Mo-Re system.

A series of Mo-Re alloy films has been prepared by sputtering from a composite molybdenum and rhenium cathode. These films were deposited in an ultra-high purity environment onto sapphire substrates which were held at temperatures ranging from 400 to 1300 C. Maximum transition temperatures observed were 15 K which is significantly greater than the highest reported bulk values. Critical current and field characteristics also were found to be considerably greater in the films compared to corresponding bulk samples. Upper critical fields of over 100 kOe were measured. These enhanced properties are discussed in relation to the structural characteristics of the sputtered films.

Gavaler, J. R.↗
NASA NTRS1971

Superconducting properties as a function of thickness in NbN films.

Measurement of the superconducting properties of NbN films prepared by a high purity reactive sputtering process. The transition temperature was found to decrease with decreasing film thickness, while in contrast the critical current vs magnetic field was largely independent of film thickness and even slightly increased when the film thickness went down to 100 A. The average resistivity of the NbN films was 1000 microohm-cm.

Gavaler, J. R.↗