Engineering topics
Hutchison, James E.
Publications and source records attributed to Hutchison, James E..
Three-Electrode Study of Electrochemical Ionomer Degradation Relevant to Anion-Exchange-Membrane Water Electrolyzers
Among existing water electrolysis (WE) technologies, anion-exchange-membrane water electrolyzers (AEMWEs) show promise for low-cost operation enabled by the basic solid-polymer electrolyte used to conduct hydroxide ions. The basic environment within the electrolyzer, in principle, allows the use of non-platinum-group metal catalysts and less-expensive cell components compared to acidic-membrane systems. Nevertheless, AEMWEs are still underdeveloped, and the degradation and failure modes are not well understood. To improve performance and durability, supporting electrolytes such as KOH and K 2 CO 3 are often added to the water feed. The effect of the anion interactions with the ionomer membrane (particularly other than OH – ), however, remains poorly understood. We studied three commercial anion-exchange ionomers (Aemion, Sustainion, and PiperION) during oxygen evolution (OER) at oxidizing potentials in several supporting electrolytes and characterized their chemical stability with surface-sensitive techniques. We analyzed factors including the ionomer conductivity, redox potential, and pH tolerance to determine what governs ionomer stability during OER. Specifically, we discovered that the oxidation of Aemion at the electrode surface is favored in the presence of CO 3 2– /HCO 3 – anions perhaps due to the poor conductivity of that ionomer in the carbonate/bicarbonate form. Sustainion tends to lose its charge-carrying groups as a result of electrochemical degradation favored in basic electrolytes. PiperION seems to be similarly negatively affected by a pH drop and low carbonate/bicarbonate conductivity under the applied oxidizing potential. Furthermore, the insight into the interactions of the supporting electrolyte anions with the ionomer/membrane helps shed light on some of the degradation pathways possible inside of the AEMWE and enables the informed design of materials for water electrolysis.
Electrochemistry-Induced Restructuring of Tin-Doped Indium Oxide Nanocrystal Films of Relevance to CO 2 Reduction
The electrochemical reduction of CO 2 into fuels using renewable electricity presents an opportunity to utilize captured CO 2 . Electrocatalyst development has been a primary focus of research in this area. This is especially true at the nanoscale, where researchers have focused on understanding nanostructure-property relationships. However, electrocatalyst structure may evolve during operation. Indium- and tin-based oxides have been widely studied as electrocatalysts for CO 2 reduction to formate, but evolution of these catalysts during operation is not well-characterized. Here, we report the evolution of nanoscale structure of precise tin-doped indium oxide nanocrystals under CO 2 reduction conditions. We show that sparse monolayer nanocrystal films desorb from the electrode upon charging, but thicker nanocrystal films remain, likely due to an increased number of physical contacts. Upon applying a cathodic voltage of –1.0 V vs RHE or greater, the original 10-nm diameter nanocrystals are no longer visible, and instead form a larger microstructural network. Elemental analysis suggests the network is an oxygen-deficient indium-tin metal alloy. We hypothesize that this morphological evolution is the result of nanocrystal sintering due to oxide reduction. Furthermore, these data provide insights into the morphological evolution of tin-doped indium oxide nanocrystal electrocatalysts under reducing conditions and highlight the importance of post-electrochemical structural characterization of electrocatalysts.
0D Nanocrystals as Light‐Driven, Localized Charge‐Injection Sources for the Contactless Manipulation of Atomically Thin 2D Materials
A contactless charge‐injection scheme that allows the local and quasi‐permanent manipulation of atomically thin 2D materials, such as monolayer (1L‐)MoS 2 , over spatial extents of several tens of micrometers, is reported. The possibility to precisely position and localize the charge‐injection source to the micrometer scale post‐fabrication allows the investigation of local unperturbed electronic structure of the 2D material. Thanks to this novel approach, the important impact of sample inhomogeneity on the charge‐carrier percolation that occurs over the entire extent of the 2D flake and proliferates up to 40 μm away from the localized charge injection is elucidated. The apparent driving force for carrier relocation is the initial inhomogeneous electronic landscape of the 2D material. These studies demonstrate that local and contactless charge injection with submicrometer precision delivers an alternative route for charge injection and indicates that local 2D material electronic structure can serve as a key element for novel nanoscale device design.
Evolution of Atomic-Level Structure in Sub-10 Nanometer Iron Oxide Nanocrystals: Influence on Cation Occupancy and Growth Rates
Abstract not provided