DOE OSTI2024

High‐Pressure Synthesis of Ultra‐Incompressible, Hard and Superconducting Tungsten Nitrides

Abstract Transition metal nitrides, particularly those of 5 d metals, are known for their outstanding properties, often relevant for industrial applications. Among these metal elements, tungsten is especially attractive given its low cost. In this high‐pressure investigation of the W–N system, two novel ultra‐incompressible tungsten nitride superconductors, namely W 2 N 3 and W 3 N 5 , are successfully synthesized at 35 and 56 GPa, respectively, through a direct reaction between N 2 and W in laser‐heated diamond anvil cells. Their crystal structure is determined using synchrotron single‐crystal X‐ray diffraction. While the W 2 N 3 solid's sole constituting nitrogen species are N 3‐ units, W 3 N 5 features both discrete N 3‐ as well as N 2 4‐ pernitride anions. The bulk modulus of W 2 N 3 and W 3 N 5 is experimentally determined to be 380(3) and 406(7) GPa, and their ultra‐incompressible behavior is rationalized by their constituting WN 7 polyhedra and their linkages. Importantly, both W 2 N 3 and W 3 N 5 are recoverable to ambient conditions and stable in air. Density functional theory calculations reveal W 2 N 3 and W 3 N 5 to have a Vickers hardness of 30 and 34 GPa, and superconducting transition temperatures at ambient pressure (50 GPa) of 11.6 K (9.8 K) and 9.4 K (7.2 K), respectively. Additionally, transport measurements performed at 50 GPa on W 2 N 3 corroborate with the calculations.

Chemistry↗

DOE OSTI2022

Thermodynamic and electrical transport properties of UTe 2 under uniaxial stress

Despite intense experimental efforts, the nature of the unconventional superconducting order parameter of UTe 2 remains elusive. This puzzle stems from reports of either a single or a double superconducting transition at ambient pressure as well as a complex pressure-temperature phase diagram. To address this issue, we measured the heat capacity and electrical resistivity of UTe 2 under compressive uniaxial stress σ applied along different crystallographic directions. We find that the critical temperature T c of the single observed bulk superconducting transition decreases with σ along [100] and [110] but increases with σ along [001]. Aside from its effect on T c , c-axis stress leads to a significant piezoresistivity. Importantly, an in-plane shear stress σ xy does not induce any observable splitting of the superconducting transition over a stress range of σ xy ≈ 0.17GPa. Furthermore, this result suggests that the superconducting order parameter of UTe 2 may be single component at ambient pressure.

75 CONDENSED MATTER PHYSICS, SUPERCONDUCTIVITY AND↗

DOE OSTI2021

Spatially inhomogeneous superconductivity in UTe 2

The newly discovered superconductor UTe 2 is a strong contender for a topological spin-triplet state wherein a multicomponent order parameter arises from two nearly degenerate superconducting states. A key issue is whether both of these states intrinsically exist at ambient pressure. Through thermal expansion and calorimetry, we show that UTe 2 at ambient conditions exhibits two detectable transitions only in some samples, and the size of the thermal expansion jump at each transition varies when the measurement is performed in different regions of the sample. This result indicates that the two transitions arise from two spatially separated regions that are inhomogeneously mixed throughout the volume of the sample, each with a discrete superconducting transition temperature (T c ). Notably, samples with higher T c only show a single transition at ambient pressure. Above 0.3 GPa, however, two transitions are invariably observed in ac calorimetry. Our results not only point to a nearly vertical line (constant pressure) in the pressure-temperature phase diagram but also provide a consistent scenario for the sample dependence of UTe 2 .

75 CONDENSED MATTER PHYSICS, SUPERCONDUCTIVITY AND↗