Huynh, Thinh | Search NASA

DOE OSTI2022

Microstructural Development in Inconel 718 Nickel-Based Superalloy Additively Manufactured by Laser Powder Bed Fusion

Excellent weldability and high temperature stability make Inconel 718 (IN718) one of the most popular alloys to be produced by additive manufacturing. Here in this study, we investigated the effects of laser powder bed fusion (LPBF) parameters on the microstructure and relative density of IN718. The samples were fabricated with independently varied laser power (125 - 350W), laser scan speed (200 - 2200 mm/s), and laser scan rotation (0° - 90°). Archimedes’ method, optical microscopy, and scanning electron microscopy were employed to assess the influence of LPBF parameters on the relative density and microstructure. Optimal processing windows were identified for a wide range of processing parameters and relative density greater than 99.5% was achieved using volumetric energy density between 50 and 100 J/mm3. Microstructural features including melt pool geometry, lack of fusion defect, keyhole porosity, and sub-grain cellular microstructure were examined and quantified to correlate to LPBF parameters. A simple empirical model was postulated to relate relative sample density and LPBF volumetric energy density. Melt pool dimensions were quantitatively measured and compared to estimations based on Rosenthal solution, which yielded a good agreement with the width, but underestimated the depth, particularly at high energy input, due to lack of consideration for keyhole mode. In addition, the sub-grain cellular-dendritic microstructure in the as-built samples was observed to decrease with increasing laser scan speed. Quantification of the sub-micron cellular-dendritic microstructure yielded estimated cooling rate in the order of 10 5 – 10 7 K/s.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

DOE OSTI2021

Mechanical Behavior Assessment of Ti-6Al-4V ELI Alloy Produced by Laser Powder Bed Fusion

The present work correlates the quasi-static, tensile mechanical properties of additively manufactured Ti-6Al-4V extra low interstitial (ELI, Grade 23) alloy to the phase constituents, microstructure, and fracture surface characteristics that changed with post-heat treatment of stress relief (670 °C for 5 h) and hot isostatic pressing (HIP with 100 MPa at 920 °C for 2 h under an Ar atmosphere). Ti-6Al-4V ELI alloy tensile specimens in both the horizontal (i.e., X and Y) and vertical (Z) directions were produced by the laser powder bed fusion (LPBF) technique. Higher yield strength (1141 MPa), higher tensile strength (1190 MPa), but lower elongation at fracture (6.9%), along with mechanical anisotropy were observed for as-stress-relieved (ASR) samples. However, after HIP, consistent and isotropic mechanical behaviors were observed with a slight reduction in yield strength (928 MPa) and tensile strength (1003 MPa), but with a significant improvement in elongation at fracture (16.1%). Phase constituents of acicular α' phase in ASR and lamellar α + β phases in HIP samples were observed and quantified to corroborate the reduction in strength and increase in ductility. The anisotropic variation in elongation at fracture observed for the ASR samples, particularly built in the build (Z) direction, was related to the presence of “keyhole” porosity.

42 ENGINEERING↗