DOE OSTI2023

Exploring the Storage Mechanism of Alkali Ions in Non-Graphitic Hard Carbon Anodes

This study aims to develop high-capacity hard carbon anode materials for alkali-ion batteries by controlling the microstructures of non-graphitic hard carbon through an annealing protocol and investigating the effects on the alkali-ion storage mechanisms using physical, chemical, and electrochemical analytical techniques. The hard carbon materials were synthesized at temperatures ranging from 900 °C to 1600 °C. Those synthesized at 1100 °C with high surface area and abundant defects exhibited the highest reversible capacity in Li- and K-ion systems, with the storage dominated by surface-adsorption mechanisms. In contrast, the hard carbon compounds prepared at 1400 °C with numerous curve-featured pores delivered the highest reversible capacity in the Na-ion system, indicating that these pores are the preferred Na-ion storage sites, particularly in low-voltage plateau regions. This study provides a comprehensive understanding of the relationship between microstructures and alkali-ion storage mechanisms in non-graphitic hard carbon and highlights the importance of tailoring the microstructures of hard carbon to achieve high specific capacity for the desired alkali-ion species.

25 ENERGY STORAGE↗

DOE OSTI2021

Effect of Microstructural Bands on the Localized Corrosion of Laser Surface-melted 316L Stainless Steel

The localized corrosion of laser surface melted (LSM) 316L stainless steel is investigated by a combination of potentiodynamic anodic polarization in 0.1M HCl and microscopic investigation of the initiation and propagation of localized corrosion. The pitting potential of LSM 316L is significantly lower than the pitting potential of wrought 316L. The LSM microstructure is highly banded as a consequence of the high laser power density and high linear energy density. The bands are composed of zones of changing modes of solidification, cycling between very narrow regions of primary austenite solidification and very wide regions of primary ferrite solidification. Pits initiate in the outer edge of each band where the mode of solidification is primary austenite plane front solidification and primary austenite cellular solidification. The primary austenite regions have low chromium concentration (and possibly low molybdenum concentration), which explains their susceptibility to pitting corrosion. The ferrite is enriched in chromium, which explains the absence of pitting in the primary ferrite regions. The presence of the low chromium regions of primary austenite solidification explains the lower pitting resistance of LSM 316L relative to wrought 316L. The influence of banding on localized corrosion is applicable to other rapidly solidified processes such as additive manufacturing.

36 MATERIALS SCIENCE↗

DOE OSTI2021

Laser-based three-dimensional manufacturing technologies for rechargeable batteries

Laser three-dimensional (3D) manufacturing technologies have gained substantial attention to fabricate 3D structured electrochemical rechargeable batteries. Laser 3D manufacturing techniques offer excellent 3D microstructure controllability, good design flexibility, process simplicity, and high energy and cost efficiencies, which are beneficial for rechargeable battery cell manufacturing. In this review, notable progress in development of the rechargeable battery cells via laser 3D manufacturing techniques is introduced and discussed. The basic concepts and remarkable achievements of four representative laser 3D manufacturing techniques such as selective laser sintering (or melting) techniques, direct laser writing for graphene-based electrodes, laser-induced forward transfer technique and laser ablation subtractive manufacturing are highlighted. Finally, major challenges and prospects of the laser 3D manufacturing technologies for battery cell manufacturing will be provided.

25 ENERGY STORAGE↗