DOE OSTI2024

Determination of α lamellae orientation in a β-Ti alloy using electron backscatter diffraction

The spatial orientation of α lamellae in a metastable β-Ti matrix of Timetal LCB (Ti–6.8 Mo–4.5 Fe–1.5 Al in wt%) was examined and the orientation of the hexagonal close-packed α lattice in the α lamella was determined. For this purpose, a combination of methods of small-angle X-ray scattering, scanning electron microscopy and electron backscatter diffraction was used. The habit planes of α laths are close to {111} β , which corresponds to (1$\bar3$20) α in the hexagonal coordinate system of the α phase. The longest α lamella direction lies approximately along one of the $\langle$110$\rangle$ β directions which are parallel to the specific habit plane. Taking into account the average lattice parameters of the β and α phases in aged conditions in Timetal LCB, it was possible to index all main axes and faces of an α lath not only in the cubic coordinate system of the parent β phase but also in the hexagonal system of the α phase.

36 MATERIALS SCIENCE↗

DOE OSTI2024

Sol-gel derived silicate-phosphate glass SiO 2 –P 2 O 5 –CaO–TiO 2 : The effect of titanium isopropoxide on porosity and thermomechanical stability

Despite of several decades lasting extensive research of bioactive and bioresorbable glasses the systematic parametrization and determination of the key factors affecting porosity and thermomechanical characteristics still remains challenging. Here, we present silica-phosphate glasses, with the composition 70SiO 2 - 20P 2 O 5 - (10-x)CaO-xTiO 2 (mol%; x = 0, 2.5, 5, and 7.5), prepared by sol -gel method and reinforced by titanium dioxide via titanium isopropoxide (TTIP) incorporation which demonstrated tunable variation of porosity from micro-to macro -region and superb mechanical integrity during the calcination process. The presence of 7.5 mol% TiO 2 promotes dimensional stability up to 1000°C as investigated by thermomechanical analysis. The XRD showed the dominant presence of silicon phosphate [Si(P 2 O 7 )], titanium phosphate [Ti(P 2 O 7 )] and calcium phosphates [β-Ca(P 2 O 6 ) and γ- Ca 2 (P 2 O 7 )]. The effect of TiO 2 doping on the multiscale morphology and porosity was investigated by means of SEM, MIP, μCT, N 2 adsorption and USAXS/SAXS. Increasing TiO 2 content leads to the formation of open porosity up to 70vol% and drives the formation of a refined interconnected macroporosity of 2-30 μm. In contrast, mesoporosity with a dominance of 3-6nm pores decreases in all samples with increasing TiO 2 content. USAXS/SAXS revealed an increase in primary particle size with increasing TiO 2 content which is in good agreement with the nitrogen physisorption analysis showing that microporosity decreases with increasing TiO2 content.

36 MATERIALS SCIENCE↗

DOE OSTI2022

Lamellae of α phase in a metastable β -Ti alloy studied by small-angle x-ray scattering

The shapes and orientations of lamellae of the hexagonal close-packed α phase in single crystals of the body-centred cubic β phase in a metastable β -Ti alloy (Timetal LCB) were investigated by synchrotron small-angle x-ray scattering. Several steps of thermal treatment with various annealing times and temperatures were employed. The measured scattering data were fitted to a model of ellipsoidal lamellae of random sizes, and the mean lamella shapes and orientations of their axes with respect to the β -Ti matrix were determined from the fit. The number and relative volume of the lamellae were estimated from the integrated scattered intensity. The elastic energy of the lamellae as well as the energy of defects at the α / β interface (misfit dislocations) were calculated from the parameters of the lamellae. In conclusion, the results provide information on the kinetics of the β $ \rightarrow$ α transformation in metastable β -Ti alloys and allow assessing the degree of thermodynamic equilibrium of the final α / β composite.

36 MATERIALS SCIENCE↗