Inagaki, Yaohiro | Search NASA

DOE OSTI2022

Stirred-Reactor Coupon Analysis: An International Round Robin Study

The objective of this task was to determine the precision of the SRCA technique when used to determine the dilute condition corrosion rate. To this end, an interlaboratory round robin study was conducted per the instructions in ASTM Practice E691 to measure the precision with which the SRCA test method can be conducted. Twelve independent labs from eleven different institutions each evaluated four glass compositions in three different conditions. The ASTM procedures recommend at least 6 labs participate in a round robin testing the same 3 materials in the same conditions to determine precision. In this case, 12 labs each performed 12 independent tests. This was only possible thanks to the multi-glass testing capability of the SRCA test. A total of 108 duplicate pairs were used to calculate the repeatability of the tests, with the same glass tested in the same vessel, producing as identical conditions as possible for the replicates. These test results were quite tightly clustered, with a median difference from the average value of the pair of only 2.9%. Based on the calculations outlined in ASTM E177-20 and a measured standard deviation of 4.74%, the intralaboratory repeatability limit (r) was calculated to be within 13.3% of the expected value with 95% confidence level. The reproducibility limit (R) of the test was examined using all 277 data points from the round robin. Because of the differences in dissolution rates due to pH variability and intrinsically for the 12 conditions tested, the reproducibility limits for each condition and overall were calculated from the percent relative residual value for each test. The SRCA test is expected to be reproducible within 64% of the expected value with a 95% confidence level.

12 MANAGEMENT OF RADIOACTIVE AND NON-RADIOACTIVE W↗

DOE OSTI2022

Elucidating the Atomic Structures of the Gel Layer Formed during Aluminoborosilicate Glass Dissolution: An Integrated Experimental and Simulation Study

The altered glasses produced during aqueous dissolution of silicate and borosilicate glasses are among the most complex structures to understand at the atomic level due to their amorphous nature, random porosity and various levels of hydration. In this study, we gained insights of the complex atomic structures of altered aluminoborosilicate glasses by combining a range of experimental and computational approaches. The altered glasses were prepared by dissolution of three glasses with varying level of alumina in acid for 7 days. A comprehensive set of experimental [elemental analysis, high-energy X-ray diffraction, 29 Si and 27 Al solid-state nuclear magnetic resonance (NMR), and O 1s X-ray photoelectron spectroscopy (XPS)] and modeling (molecular dynamics (MD) simulations using non-reactive and reactive force fields) were used to study the atomic structures of these altered glasses. Elemental analysis showed that most of the B in the pristine glasses was leached into the solution and was not contained in the altered glass. The 29 Si and 27 Al solid-state NMR spectra revealed that the altered glasses have more polymerized silicate network as compared to those in the pristine glasses due to the reformation of linkages among Si and Al oxygen polyhedral in the altered glasses. The bridging and non-bridging (or hydroxyl O) atoms in the altered glasses were also quantified from their O 1s XPS spectra. Atomic structure models of the altered glasses were constructed by using MD simulations using the reactive force field based on the compositional information obtained from experiments. Various pore structures were generated using the charge-scaling (CS) method by using different initial densities and CS temperatures; the best CS parameters of each alternated glass were then determined by comparing with the experimental structure factors obtained from high energy X-ray diffraction. Pore and the atomic structures and vibrational properties around these pore surfaces were analyzed. Furthermore, these results from this comprehensive study thus provides a realistic insight into the pore morphology, atomic structure, and vibrational properties of altered glasses.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗