Glass Bubbles Insulation for Liquid Hydrogen Storage Tanks

A full-scale field application of glass bubbles insulation has been demonstrated in a 218,000 L liquid hydrogen storage tank. This work is the evolution of extensive materials testing, laboratory scale testing, and system studies leading to the use of glass bubbles insulation as a cost efficient and high performance alternative in cryogenic storage tanks of any size. The tank utilized is part of a rocket propulsion test complex at the NASA Stennis Space Center and is a 1960's vintage spherical double wall tank with an evacuated annulus. The original perlite that was removed from the annulus was in pristine condition and showed no signs of deterioration or compaction. Test results show a significant reduction in liquid hydrogen boiloff when compared to recent baseline data prior to removal of the perlite insulation. The data also validates the previous laboratory scale testing (1000 L) and full-scale numerical modeling (3,200,000 L) of boiloff in spherical cryogenic storage tanks. The performance of the tank will continue to be monitored during operation of the tank over the coming years.

Glass bubble↗

NASA NTRSDate not supplied

Ground-Based Cryogenic Leak Test of Fittings for Cryogenic Fluid Management

Mechanically connected fluid joints are virtually unavoidable in complex cryogenic system designs. In the case of spacecraft, the performance of these joints is critical to mission success. This is especially true for long-duration space missions where even very low leak rates can eventually lead to significant propellant losses or failure of vital cryogenic cooling systems. NASA has recently undertaken an effort to quantify the leak rate of Vacuum Coupling Radiation (VCR) fittings over the temperature range from ambient to 20 K, both before and after exposure to a launch vibration profile. A test apparatus employing a cryocooler and a calibrated helium mass spectrometer was developed, validated, and used to obtain quantifiable leak rates at a fitting test pressure of 31 bar (450 psig). Three different fitting sizes were tested, 25.4 mm (¼ inch), 12.7 mm (½ inch), and 6.35 mm (1 inch) and two gasket materials, stainless steel, and silver-plated nickel. Each fitting configuration (size/seal material) was subjected to two consecutive cryogenic thermal cycles/measurement tests, followed by a launch vibration test profile at ambient temperature, and then two additional cryogenic thermal cycles/measurement tests. The design and development of the test apparatus, and test data are presented and discussed in detail.

G J Tamasy↗