Magnetic properties versus interface density in rigid-exchange-coupled amorphous multilayers with induced uniaxial anisotropy
We demonstrate the possibility to tune the saturation magnetization, coercivity, and uniaxial in-plane anisotropy constant in amorphous bilayers and multilayers of Co 85 (Al 70 Zr 30 ) 15 and Sm 11 Co 82 Ti 7 through the interface density. From magnetometry and x-ray circular dichroism (XMCD) measurements, we conclude that the easy-axis coercivity μ 0 H c increases four times when the number of bilayer repetitions, N, increases from 1 to 10 within a constant total sample thickness of 20 nm. At the same time, the anisotropy constant K u also increases by a factor four, whereas the saturation magnetization M s decreases slightly. The Co spin and orbital moments, m s and m l , are found to be approximately constant within the sample series. The average total Co moment is only 0.8-0.9 μ B /atom, but the m l /m s ratio is strongly enhanced compared to pure Co. Magnetization curves extracted from XMCD measurements show that the Co and Sm moments are ferromagnetically coupled for all samples.