Dynamic friction and wear of a solid film lubricant during radiation exposure in a nuclear reactor
The effect of nuclear reactor radiation on the performance of a solid film lubricant was studied. The film consisted of molybdenum disulfide and graphite in a sodium silicate binder. Radiation levels of fast neutrons (E or = 1 MeV) were fluxed up to 3.5 times 10 to the 12th power n/sq cm-sec (intensity) and fluences up to 2 times 10 to the 18th power n/sq cm (total exposure). Coating wear lives were much shorter and friction coefficients higher in a high flux region of the reactor than in a low flux region. The amount of total exposure did not affect lubrication behavior as severely as the radiation intensity during sliding.