Disclosed are passive NOx adsorbers and methods for synthesizing the same. Small-pore zeolitic materials with practical loadings of transition metals atomically dispersed in the micropores are described herein. Also demonstrated are simple and scalable synthesis routes to high loadings of atomically dispersed transition metals in the micropores of a small-pore zeolite.
Supported vanadium oxide catalysts are important industrial materials for a wide array of chemical transformations. The condition of surface hydration is of particular interest as a reflection of the state of a freshly manufactured catalysts prior to its activation in catalytic reactors or under conditions of photocatalysis where surface vandia are exposed to moisture. Under such conditions, the surface vanadia species undergo structural changes as evidenced by 51 V MAS NMR in this study. For low surface vanadia densities on titania, a modest trend towards the formation of dimeric and oligomeric vanadia species was observed under hydrated conditions when compared to the corresponding dehydrated catalyst, which contains a large abundance of monomeric vanadia species. The incorporation of tungsten oxide to the V 2 O 5 /TiO 2 catalyst with low surface vanadia density, however, is found to better stabilize the surface vanadia species on the titania support upon hydration than its tungsta-free counterpart. This stabilization is not an intrinsic property of more extensively oligomerized surface vanadia species in the presence of tungsten oxide, evidenced by conditions of high concentrations of surface vanadia oligomers on titania that exhibit dramatic structural changes upon hydration. At high surface vanadia coverage under hydrated environments, the simultaneous observation of crystalline V 2 O 5 nanoparticles and a mobile phase of surface vanadia species is apparent, where vanadia species are dissolved in the thin hydration layer on the titania support. These new findings have broad implications on the behavior of other metal oxide species on high surface oxide supports under hydrated conditions.
Abstract γ‐alumina is one of the oldest and most important commercial catalytic materials with high surface area and stability. These attributes enabled its use as the first commercial large‐scale heterogeneous catalyst for ethanol dehydration. Despite progress in materials characterization the nature of the specific sites on the surface of γ‐alumina that are responsible for its unique catalytic properties has remained obscure and controversial. By using combined infrared spectroscopy, electron microscopy and solid‐state nuclear magnetic resonance measurements we identify the octahedral, amphoteric (O) 5 Al(VI)‐OH sites on the (100) segments of massively restructured (110) facets on typical rhombus‐platelet γ‐alumina as well as the (100) segments of irrational surfaces (invariably always present in all γ‐alumina samples) responsible for its unique catalytic activity. Such (O) 5 Al(VI)‐OH sites are also present on the macroscopically defined (100) facets of γ‐alumina with elongated/rod‐like geometry. The mechanism by which these sites lose ‐OH groups upon thermal dehydroxylation resulting in coordinatively unsaturated penta‐coordinate Al +3 O 5 sites is clarified. These coordinatively unsaturated penta‐coordinate Al sites produce well‐defined thermally stable Al‐carbonyl complexes. Our findings contribute to the understanding of the nature of coordinatively unsaturated Al sites on the surface of γ‐alumina and their role as catalytically active sites.
γ-alumina is one of the oldest and most important commercial catalytic materials with high surface area and stability. These attributes enabled its use as the first commercial large-scale heterogeneous catalyst for ethanol dehydration. Despite progress in materials characterization the nature of the specific sites on the surface of γ-alumina that are responsible for its unique catalytic properties has remained obscure and controversial. By using combined infrared spectroscopy, electron microscopy and solid-state nuclear magnetic resonance measurements we identify the octahedral, amphoteric (O) 5 Al(VI)-OH sites on the (100) segments of massively restructured (110) facets on typical rhombus-platelet γ-alumina as well as the (100) segments of irrational surfaces (invariably always present in all γ-alumina samples) responsible for its unique catalytic activity. Such (O) 5 Al(VI)-OH sites are also present on the macroscopically defined (100) facets of γ-alumina with elongated/rod-like geometry. The mechanism by which these sites lose -OH groups upon thermal dehydroxylation resulting in coordinatively unsaturated penta-coordinate Al +3 O 5 sites is clarified. These coordinatively unsaturated penta-coordinate Al sites produce well-defined thermally stable Al-carbonyl complexes. Overall, our findings contribute to the understanding of the nature of coordinatively unsaturated Al sites on the surface of γ-alumina and their role as catalytically active sites.
A series of Ag–ZrO 2 /SiO 2 catalysts with different metal–support interfaces were synthesized in an effort to elucidate the roles of specific interfaces in controlling the ethanol to 1,3–butadiene conversion and selectivity. According to the results of detailed characterizations (e.g. CO/pyridine–DRIFTS, XPS, TEM, NH 3 –TPD, and 1 H MAS NMR), it was found that the Ag–O–Si interfaces significantly enhanced the dehydrogenation of ethanol while the presence of ZrO 2 improved the interaction between Ag and ZrO 2 /SiO 2 , creating more Ag δ+ active sites. In this research, the high dispersion of ZrO 2 on SiO 2 generated abundant Zr–O–Si interfaces with medium and weak Lewis acidity, promoting the condensation of acetaldehyde to crotonaldehyde. These Zr–O–Si interfaces in close interaction with Ag δ+ species played a critical role in the enhanced H transfer during the MPV reduction of crotonaldehyde to crotyl alcohol. The synergies among the interfaces resulted in retarded ethanol dehydration reactivity, balanced ethanol dehydrogenation and condensation reactions, and a subsequent high 1,3–butadiene yield.
Electronic cigarette usage has spiked in popularity over recent years. The enhanced prevalence has consequently resulted in new health concerns associated with the use of these devices. Degradation of the liquids used in vaping have been identified as a concern due to the presence of toxic compounds such as aldehydes in the aerosols. Typically, such thermochemical conversions are reported to occur between 300 and 400 °C. Herein, the low-temperature thermal degradation of propylene glycol and glycerol constituents of e-cigarette vapors are explored for the first time by natural abundance 13 C NMR and 1 H NMR, enabling in situ detection of intact molecules from decomposition. The results demonstrate that the degradation of electronic nicotine delivery system (ENDS) liquids is strongly reliant upon the oxygen availability, both in the presence and absence of a material surface. When oxygen is available, propylene glycol and glycerol readily decompose at temperatures between 133 and 175 °C over an extended time period. Among the generated chemical species, formic and acrylic acids are observed which can negatively affect the kidneys and lungs of those who inhale the toxin during ENDS vapor inhalation. Further, the formation of hemi- and formal acetals is noted from both glycerol and propylene glycol, signifying the generation of both formaldehyde and acetaldehyde, highly toxic compounds, which, as a biocide, can lead to numerous health ailments. The results also reveal a retardation in decomposition rate when material surfaces are prevalent with no directly observed unique surface spectator or intermediate species as well as potentially slower conversions in mixtures of the two components. The generation of toxic species in ENDS liquids at low temperatures highlights the dangers of low-temperature ENDS use.
Most multivalent secondary batteries have employed electrolytes composed of cyclic ether solvents such as tetrahydrofuran or linear glycol ether solvents (glymes) such as 1,2-dimethoxyethane (G1). A robust understanding of multivalent cation solvation tendencies in these classes of solvents provides insight into corresponding structure–property relationships which, in turn, promotes the design and discovery of improved electrolytes. In this work, our goal is to systematically address how electrolyte constituent properties, namely, ether solvent structure and dication size, direct the solvation interactions of divalent electrolytes and their resultant properties. This study utilizes pulsed-field gradient (PFG) nuclear magnetic resonance (NMR) spectroscopy in conjunction with Raman spectroscopy and ionic conductivity measurements to elucidate the preferential interactions between multivalent cations, anions, and solvent molecules along with their correlated ion dynamics. These investigations incorporate two representative divalent cations (Ca 2+ and Zn 2+ ) as well as two ethereal solvent representatives from both the cyclic ether and glyme structural classes. The results reveal that anions coordinate more readily with divalent cations in cyclic ethers than in glymes. Furthermore, the coordination of the anions with Ca 2+ , i.e., contact-ion pair (CIP) formation is more pronounced than with Zn 2+ in a glyme solvent of limited chain length (G1), providing insight into cation size effects that are important for translating solvation behavior across various multivalent electrolytes. Importantly, we find that specific anion coordination is more strongly controlled by solvent structure than by salt concentration in the practical range of 0.1–0.5 M. However, simply reducing these inner-sphere inter-ionic interactions by changing solvent structure does not necessarily de-correlate ionic motion. Instead, concentration-dependent changes in molar ionic conductivity suggest that second-shell interactions, i.e., solvent separated ion pairs (SSIPs), are prevalent in these electrolytes and that the solution dielectric constant, which is increased by the presence of dipolar ion pairs, is critical for controlling these interactions. These findings thus provide a basis for understanding the physical chemistry of multivalent battery electrolytes.
Herein, a detailed analysis was carried out using high-field (19.9 T) 27Al magic-angle spinning (MAS) nuclear magnetic resonance (NMR) on three specially prepared aluminum oxide samples where the ?-, d-, and ?-Al2O3 phases are dominantly expressed through careful control of the synthesis conditions. Specifically, two-dimensional (2D) multiquantum (MQ) MAS 27Al was used to obtain high spectral resolution, which provided a guide for analyzing quantitative 1D 27Al NMR spectra. Six aluminum sites were resolved in the 2D MQ MAS NMR spectra, and seven aluminum sites were required to fit the 1D spectra. A set of octahedral and tetrahedral peaks with well-defined quadrupolar line shapes was observed in the ?-phase dominant sample and was unambiguously assigned to the ?-Al2O3 phase. The distinct line shapes related to the ?-Al2O3 phase provided an opportunity for effectively deconvoluting the more complex spectrum obtained from the d-Al2O3 dominant sample, allowing the peaks/quadrupolar parameters related to the d-Al2O3 phase to be extracted. The results show that the d-Al2O3 phase contains three distinct AlO sites and three distinct AlT sites. This detailed Al site structural information offers a powerful way of analyzing the most complex ?-Al2O3 spectrum. It is found that the ?-Al2O3 phase consists of Al sites with local structures similar to those found in the d-Al2O3 and ?-Al2O3 phases albeit with less ordering. Spin–lattice relaxation time measurement further confirms the disordering of the lattice. Collectively, this study uniquely assigns 27Al features in transition aluminas, offering a simplified method to quantify complex mixtures of aluminum sites in transition alumina samples.
We show for the first time that atomically dispersed Rh cations on ceria, prepared via high-temperature atom trapping synthesis, are the active species for (CO+NO) reaction. This provides a direct link with the organometallic homogeneous Rh(I) complexes capable of catalyzing dry (CO+NO) reaction but without the stability concern. In particular, thermally stable Rh cations in 0.1wt% Rh1/CeO2 achieve full NO conversion with a TOF of ~ 330 hr-1 per Rh atom at 120 °C. Under dry conditions, the main product above 100 °C is N2 with N2O being the minor product. The presence of water promotes low-temperature activity of 0.1wt% Rh1/CeO2 starting at 50 °C with full NO conversion at ~120 °C. In the case with the wet stream, however, ammonia and nitrogen are the main products with only minor N2O amounts. NH3 formation at such low temperatures is attractive because of the potential to use this as a passive SCR system. Because of the uniformity of Rh ions on the support, we are able to observe the intermediates of (CO+NO) reaction via infrared measurements on Rh cations on zeolite and ceria. Furthermore, we show that ammonia formation correlates with the WGS activity of the material and thus, rhodium hydride Rh-H species are involved in this reaction: we detect Rh(CO)Hx species on ceria using isotopic IR measurements. These findings provide new mechanistic understanding for the catalytically active species in TWC catalysis and open up a new avenue for the synthesis of novel emissions control catalysts with 100% atom economy of ultra-expensive precious metals such as Rh.
Aldol condensations of carbonyl compounds for C–C bond formation are a very important class of reactions in organic synthesis and upgrading of biomass-derived feedstocks. However, the atomic level understanding of reaction mechanisms and structure-activity correlation on widely used transition metal oxide catalysts are limited due to the high degree of struc-tural heterogeneity of catalysts such as commercial TiO 2 powders. Here, we provide a deep understanding of the reaction mechanisms, kinetics, and structure–function relationships for vapor phase acetone aldol condensation through the con-trolled synthesis of two catalysts with high surface areas and clean, dominant facets, coupled with detailed characterization and kinetic studies that are further assisted by density functional theory (DFT) calculations. Temperature-dependent diffuse reflectance infrared Fourier transform spectroscopy showed the existence of abundant acetone bonded to surface hydroxyl groups (acetone-O s H) and acetone bonded to Lewis acid sites (acetone-Ti 5c ) on surface of both {101} and {001} facet dom-inant TiO 2 . Intermolecular C–C coupling of enolate intermediate from acetone-Ti 5c and a vicinal acetone-O s H is a kinetically relevant step, which is consistent with kinetic and isotopic studies and DFT calculations. The {001} facet showed a lower apparent activation energy (or higher reactivity) than the {101} facet. This is likely caused by the weaker Lewis acid and Brønsted base strengths of the {001} facet which favors the reprotonation–desorption of the coupled intermediate, making the C–C coupling step more exothermic on the {001} facet and resulting in an earlier transition state with a lower activation barrier. It is also possible that the {001} facet has a smoother surface configuration and less steric hindrance during intermo-lecular C–C bond formation than the {101} facet.
High temperature exposure of ?-Al2O3 can lead to a series of polymorphic transformations, including the formation of ?-Al2O3 and ?-Al2O3. Quantification of the microstructure in the ?/?-Al2O3 formation range represents a formidable challenge as both phases accommodate a high degree of structural disorder. In this work, we explore the use of XRD recursive stacking formalism for quantification of high temperature transition aluminas. We formulate the recursive stacking methodology for modelling of disorder in ?-Al2O3 and twinning in ?-Al2O3 and show that explicitly accounting for the disorder is necessary to reliably model the XRD patterns of high temperature transition alumina. In the second part, we use the recursive stacking approach to study phase transformation during high temperature (1050 ºC) treatment. We show that the two different intergrowth modes of ?-Al2O3 have different transformation characteristics, and that a significant portion of ?-Al2O3 is stabilized with ?-Al2O3 even after prolonged high-temperature exposures. In discussions, we outline the limitation of the current XRD approach and discuss a possible multimodal XRD and NMR approach which can improve analysis of complex transition aluminas. This work was performed in the Wiley Environmental Molecular Sciences Laboratory (EMSL), a national scientific user facility sponsored by DOEs Office of Biological and Environmental Research and located at PNNL. The work was supported by the U.S. Department of Energy (DOE), Office of Basic Energy Sciences, Division of Chemical Sciences, Geosciences, and Biosciences.
Abstract We show for the first time that atomically dispersed Rh cations on ceria, prepared by a high‐temperature atom‐trapping synthesis, are the active species for the (CO+NO) reaction. This provides a direct link with the organometallic homogeneous Rh I complexes capable of catalyzing the dry (CO+NO) reaction. The thermally stable Rh cations in 0.1 wt % Rh 1 /CeO 2 achieve full NO conversion with a turn‐over‐frequency (TOF) of around 330 h −1 per Rh atom at 120 °C. Under dry conditions, the main product above 100 °C is N 2 with N 2 O being the minor product. The presence of water promotes low‐temperature activity of 0.1 wt % Rh 1 /CeO 2 . In the wet stream, ammonia and nitrogen are the main products above 120 °C. The uniformity of Rh ions on the support, allows us to detect the intermediates of (CO+NO) reaction via IR measurements on Rh cations on zeolite and ceria. We also show that NH 3 formation correlates with the water gas shift (WGS) activity of the material and detect the formation of Rh hydride species spectroscopically.
Nuclear magnetic resonance (NMR) spectroscopy represents an important technique to understand the structure and bonding environment of molecules. There exists a drive to conduct characterization experiment under conditions relevant to the chemical process of interest. To address this, in situ high-temperature, high-pressure MAS NMR methods have been developed to enable the observation of chemical interactions over a range of pressures (vacuum to several hundred bar) and temperatures (well below 0°C to 250°C). Further, the chemical identity of the samples can be comprised of solids, liquids, and gases or mixtures of the three. The method incorporates all-zirconia NMR rotors (sample holder for MAS NMR) which can be sealed using a threaded cap to compress an O-ring. This rotor exhibits great chemical resistance, temperature compatibility, low NMR background, and can withstand high pressures. These factors combined enable its use in a wide range of system combinations which permit its use in diverse fields as carbon sequestration, catalysis, material science, geochemistry, and biology. The flexibility of this technique makes it an attractive option for scientists from numerous disciplines.
Abstract High‐temperature treatment of γ‐Al 2 O 3 can lead to a series of polymorphic transformations, including the formation of δ‐Al 2 O 3 and θ‐Al 2 O 3 . Quantification of the microstructure in the range where δ‐ and θ‐Al 2 O 3 are formed represents a formidable challenge, as both phases accommodate a high degree of structural disorder. In this work, we explore the use of an XRD recursive‐stacking formalism for the quantification of high‐temperature transition aluminas. We formulate the recursive‐stacking methodology for modelling of disorder in δ‐Al 2 O 3 and twinning in θ‐Al 2 O 3 and show that explicitly accounting for the disorder is necessary to reliably model the XRD patterns of high‐temperature transition alumina. We also use the recursive stacking approach to study phase transformation during high‐temperature (1050 °C) treatment. We show that the two different intergrowth modes of δ‐Al 2 O 3 have different transformation characteristics and that a significant portion of δ‐Al 2 O 3 is stabilized with θ‐Al 2 O 3 even after prolonged high‐temperature exposures.
Ethanol is a promising platform molecule for production of a variety of fuels and chemicals. Of particular interest is producing middle distillate fuels (i.e., jet and diesel blendstock) from renewable ethanol feedstock. State-of-the-art alcohol-to-jet technology requires multiple process steps based on catalytic dehydration of ethanol to form ethylene, followed by sometimes a multi-step oligomerization, and then hydrotreatment and distillation. Here we report on a new catalytic route in which ethanol is directly converted to n-butene (1- and 2-butene mixtures) over Ag-ZrO2/SBA-16, thus offering the potential for a reduction in the number of required processing steps versus conventional alcohol-to-jet technology. This catalyst system provides the balanced metal and Lewis acid sites required to selectively facilitate a cascading sequence of reactions that includes dehydrogenation, aldol condensation, Meerwein–Ponndorf–Verley reduction, dehydration, and hydrogenation. High conversion and selectivity toward either n-butene or 1,3-butadiene is achieved by tuning the hydrogen feed partial pressure and other process/catalyst parameters. With sufficient hydrogen partial pressure 1,3-butadiene is completely and selectively hydrogenated to form n-butene. The reaction mechanism was elucidated through operando-nuclear magnetic resonance investigations coupled with reactivity measurements. Combined experimental-computational investigation reveals how changes in silver and zirconium composition and the silver oxidation state affects reactivity under controlled hydrogen partial pressures and after prolonged run times. Finally, catalyst effectiveness also was demonstrated when using wet ethanol feed, thus highlighting process flexibility in terms of feedstock purity requirements. This work was financially supported by the U.S. Department of Energy (DOE), Office of Energy Efficiency and Renewable Energy, Bioenergy Technologies Office, and was performed at the Pacific Northwest National Laboratory (PNNL) under Contract No. DE-AC05-76RL01830 and the National Renewable Energy Laboratory under Contract No. DE-AC36- 08GO28308. Part of the work conducted by S. A. Akhade was performed under the auspices of the U.S. DOE at Lawrence Livermore National Laboratory under Contract No. DE-AC52-07NA27344. This work was partly supported through the PNNL-WSU Distinguished Graduate Research Program for ADW. NMR and XPS experiments were performed using EMSL (grid.436923.9), a DOE Office of Science User Facility sponsored by the Office of Biological and Environmental Research
We successfully synthesized uniform SSZ-39 with an average crystal size of about a micron. Pd (0.7 - 3 wt%) was supported on SSZ-39 with Si/Al ratio ~12. The as-synthesized materials were characterized by FTIR, XRD, Helium Ion Microscopy, HAADF-STEM imaging, 27 Al, 29 Si and H solid state NMR spectroscopic techniques. FTIR studies with CO and NO probe molecules reveal that the 0.7 wt% Pd/SSZ-39 material with Si/Al ~12 has the majority of Pd dispersed atomically as isolated Pd(II) and Pd(II)-OH centers, and thus can be used as a low-temperature passive NOx adsorber. Pd(II)-NO, Pd(II)(OH)(NO) and Pd(II)(CO)(NO) complexes form during PNA in this material. We compare this PNA material directly with the Pd/SSZ-13 system (with Si/Al ratio ~12) and show its superior hydrothermal stability. Remarkably, Pd/SSZ-39 with Si/Al ratio ~12 survives hydrothermal aging up to 815 ºC in 10% H 2 O/Air vapor for 16 hours without significant loss in activity. The SSZ-39 crystal structure remains intact during hydrothermal aging up to 1,000 ºC as we elucidate it with XRD and HAADF-STEM imaging/EDS mapping. However, changes to the framework during such harsh hydrothermal treatment significantly change the NOx release profiles during PNA as evidenced by high-field 27 Al NMR on fresh and aged Pd/SSZ-39 samples as well as PNA performance measurements. Besides PNA application, these hydrothermally very stable materials (3 wt% Pd on SSZ-39 with Si/Al ratio ~12) can be used as a robust methane combustion catalyst under industrially relevant conditions (GHSV~600,000hr -1 ). This catalyst shows minimal deactivation after both harsh hydrothermal aging at 750 and 800 ºC, and prolonged time on stream (105 hrs) at 425 °C. In contrast, both 3wt% Pd/alumina and 3wt% SSZ-13 supported samples lose a significant portion of their activity. Our study opens new avenues to prepare the most hydrothermally stable known Pd/zeolite materials with applications for adsorption and catalytic hydrocarbon combustion under industrially relevant conditions.
One of the main impediments faced for predicting important emergent properties of a multivalent electrolyte (such as conductivity and electrochemical stability) is the lack of quantitative analysis of ion-ion and ion-solvent interactions, which manifest in solvation structures and dynamics. In particular, the role of ion-solvent interactions is still unclear in cases where the strong electric field from multivalent cations can influence structural evolution of lower permittivity organic solvent molecules on solvation structure. These influences are commonly refered to as electrostriction pheonmena. Using quantitative 1H, 19F, 17O, and 25Mg NMR together with 19F nuclear spin relaxation and diffusion measurments, we find an unusual correlation between ion concentration and solvation structure of Mg(TFSI)2 salt in dimethoxyethane (DME) solution. The domiant solvation structure evolves from contact ion pairs (i.e. [Mg(TFSI)(DME)1-2]+) to fully solvated clusters (i.e. [Mg(DME)3]2+) as salt concentration increases or as temperature decreases. This transition is coupled to a phase separation, which we study here between 0.06 M and 0.36 M. Subsequent analysis is based on an explanation of the electrostriction phenomena and the competion between solvent molecules and TFSI anions for cation coordination.
Zeolites with different framework structures (SSZ-13, ZSM-5, BEA) but similar Si/Al ratios and Pd loading (~1 wr%) were synthesized and evaluated as low temperature passive NOx adsorbers (PNA). These materials exhibit high NOx adsorption efficiency with atomically dispersed Pd the active adsorption site. Hydrothermal aging at 750 ºC for 16 hours in the presence of 10% water vapor in air resulted in the formation of PdO nanoparticles in all three samples as evidenced by high energy XRD. Hydrothermal aging of the small-pore Pd/SSZ-13 (Si/Al = 6), which contain ~100-90% atomically dispersed palladium ions, decreases its PNA performance only by ~10-20%. High-field solid state 27Al NMR studies on the fresh and aged samples substantiate dealumination and significant changes in the distribution of Al (and thus, Bronsted acid) sites after hydrothermal aging. FTIR measurements with NO probe molecule and titration of Bronsted acid sites with nitrosyl (NO+) ions further corroborate the 27Al NMR data. Because framework aluminum atoms are the anchoring sites for atomically dispersed Pd ions, their elution from the framework causes the loss of active atomically dispersed Pd species. Furthermore, with the aid of HAADF-STEM imaging and synchrotron XRD studies, we further confirm and visualize the fate of these Pd species – they agglomerate into PdO nanoparticles on the external surface of zeolite. Consequently, these changes lead to the decrease in PNA performance of these materials after hydrothermal aging. The thus formed agglomerates cannot be re-dispersed back to their ionic state due to the loss of framework Al T-sites and/or inherent stability of such large PdO particles. Our study clearly demonstrates that, unlike in previous studies that found increased PNA performance upon HTA , high temperatures hydrothermal aging of PNA materials that contain atomically dispersed Pd initially, results in a decrease in NOx storage efficiency due mostly to the formation of PdO agglomerates. However, we also highlight the high hydrothermal stability of predominantly atomically dispersed 1-3 wt% Pd/SSZ-13 (Si/Al = 6), whose performance decreases only marginally after prolonged hydrothermal aging at 750 ºC. Overall, this study shows that hydrothermally stable passive NOx materials can be prepared using small-pore SSZ-13 zeolite.