Cryogenic Mixed Mode I – Mode II Fracture Toughness of Various Polymer Composite Materials

The present study investigates the mixed mode interlaminar fracture toughness of six polymer matrix composite materials at both room temperature and cryogenic liquid nitrogen temperature. The single leg bending test employed gives a mix of Mode I (opening) and Mode II (in-plane shearing) cracking. The tested thermoplastic-matrix composites were shown to have total mixed mode toughnesses 3.1–4.3 times higher than those of representative thermoset resin composites.

Carbon fiber↗
NASA NTRS2014

TPSAS-NF1676L-19616-DND

The present study has three goals: (1) perform an experiment where a simple laminate damage process can be characterized in high detail; (2) evaluate the performance of existing commercially available laminate damage simulation tools by modeling the experiment; (3) observe and understand the underlying physics of damage in a composite honeycomb sandwich structure subjected to low-velocity impact. A quasi-static indentation experiment has been devised to provide detailed information about a simple mixed-mode damage growth process. The test specimens consist of an aluminum honeycomb core with a cross-ply laminate facesheet supported on a stiff uniform surface. When the sample is subjected to an indentation load, the honeycomb core provides support to the facesheet resulting in a gradual and stable damage growth process in the skin. This enables real time observation as a matrix crack forms, propagates through a ply, and then causes a delamination. Finite element analyses were conducted in ABAQUS/Explicit(TradeMark) 6.13 that used continuum and cohesive modeling techniques to simulate facesheet damage and a geometric and material nonlinear model to simulate core crushing. The high fidelity of the experimental data allows a detailed investigation and discussion of the accuracy of each numerical modeling approach.

Mark McElroy↗
NASA NTRSDate not supplied

An Investigation on the Accuracy of Delamination Analysis Predictions for Unidirectional Laminate Configurations

The state-of-the-art methodologies for predicting delamination growth in composite laminates make use of the concept of mixed-mode fracture mechanics. In mixed-mode fracture approaches the individual Mode I, Mode II and Mode III components of the strain energy release rate (SERR) need to be determined under general loading conditions. Through the use of mixed-mode fracture, the individual components are used in combination with the critical strain energy release rates (interlaminar fracture toughnesses) for each fracture mode in a mixed mode criterion in order to predict delamination extension. These interlaminar fracture toughnesses are traditionally obtained by testing of unidirectional laminate coupons. This work presents an investigation on the accuracy of Double Cantilever Beam (DCB), End Notch Flexure (ENF) and Mixed-Mode Bending (MMB) delamination analysis predictions by comparing measured total strain-energy release rates obtained experimentally to results for structural analysis from closed-form expressions, shell finite element analysis, and continuum two-dimensional (2D) and three-dimensional (3D) (solid) finite element analysis.

Patrick Enjuto↗
NASA NTRSDate not supplied

Interlaminar R-Curve Effects in Thermoplastic Composites: Experiments and Model Correlations

The interlaminar fracture behavior of thermoplastic composites under Mode-I and Mode-II static loading is investigated in this research. The material system under consideration is a carbon fiber reinforced low melt semi-crystalline resin TC1225 LMPAEK T700G (T700/LMPAEK)†. Characterization experiments were conducted to measure the load-displacement response, peak load, and propagation of delamination from a pre-implanted Kapton® insert. The Mode-I response was characterized using a double cantilever beam (DCB) test according to the ASTM D5528-22 standard. It was observed that the propagation exhibited significant resistance to delamination growth, i.e., an R-Curve effect. The test data indicated that the steady-state fracture toughness, G SS I , was approximately twice the mean initiation fracture toughness, G Ic . The Mode-II response of an end notch flexure (ENF) specimen tested according to the ASTM D7905-19 standard exhibited an unexpected stable behavior upon attaining peak load. Prior to attaining peak load, the Mode-II response exhibited some non-linearity, which may be attributed to nonlinear bulk material response, e.g., hyper-elasticity, viscoelasticity, plasticity, etc., and potentially friction at the load/support rollers and R-Curve effects. Finite element models based on the Cohesive Zone Method (CZM) and the Virtual Crack Closure Technique (VCCT) were used to predict the DCB and ENF specimen responses. DCB analysis results obtained using G SS I predicted propagation consistent with experimental data. However, results obtained with the as characterized G Ic were inaccurate in predicting delamination growth onset and peak load. ENF analysis results obtained with the as-characterized Mode-II fracture toughness, G IIc , were inaccurate in predicting the peak load and propagation. Hence, R-Curve effects were included in both DCB and ENF simulations, which enabled improved predictions. The experimentally determined Mode-I R-Curve was used for the DCB simulations, whereas an R-Curve was derived for Mode-II assuming that the change in compliance of the specimen was associated with crack growth only.

Prabhakar Rao↗
NASA NTRSDate not supplied

Mapping Process Model Results to Fracture Model Initial Conditions for Adhesive Bonding

A systematic approach is proposed for mapping adhesive bonding process outcomes to initial conditions for progressive damage analysis (PDA). Herein, two mapping procedures are developed: 1) direct mapping for residual stresses, strains, and deformations obtained from a process model; and 2) functional mapping for quantities such as bondline thickness, degree of cure, and porosity that are assumed to have a functional relationship with fracture toughness but are not discretely modeled in the PDA. The spatial distribution of functionally mapped quantities may be determined by process modeling or inspection. The functional maps between the quantity of interest and fracture toughness may be obtained from independent lower-scale numerical simulations or empirical test campaigns. The proposed mapping procedure links the adhesive bonding process to the structural performance. Therefore, by accounting for the effects of bondline nonuniformities in structural analysis, analytical predictive accuracy can be improved, and off-nominal conditions can be evaluated. The mapping procedures are demonstrated and verified with example problems.