Effects of CMAS Application on the Isothermal and Gradient Thermal Cycling Behavior of a Yb 2 Si 2 O 7 EBC

Environmental barrier coatings (EBCs) are critical to the continued advancement of gas turbine hot section materials technology. EBCs are required to protect Si-based ceramics such as silicon carbide fiber-reinforced silicon carbide (SiC/SiC) ceramic matrix composites (CMCs) from oxidation and corrosion in the combustion environment. One of the current challenges concerning EBC lifetime is the thermochemical reactions between calcium-magnesium-aluminosilicate (CMAS) deposits and the EBC that leads to changes in both composition and stress state. These changes can severely reduce the integrity of the EBC leading to crack formation, delamination, and spallation. Current techniques for evaluating CMAS in the laboratory rely on the pre-application of CMAS. Two commonly used application methods to deposit CMAS on EBC materials are tape-casting and air spray. In both methods, the CMAS is applied to the EBC surface at ambient temperature, and then subject to a heat treatment process for binder burnout. The purpose of this study is to compare the tape-cast and air spray methods on the CMAS corrosion of an ytterbium disilicate (Yb 2 Si 2 O 7 ) EBC subject to isothermal, and gradient thermal cycling. The results highlight if any differences exist in the CMAS infiltration kinetics between the two application methods.

Environmental barrier coatings (EBCs)↗
NASA NTRS2023

Influence of Cation Species on Thermal Expansion of Y2Si2O7–Gd2Si2O7 Solid Solutions

Mixtures of Y 2 Si 2 O 7 and Gd 2 Si 2 O 7 were synthesized by solid-state reaction at 1600°C and characterized via in situ x-ray diffraction (XRD) to determine their coefficients of thermal expansion (CTE). All solid solutions within the system exhibited the orthorhombic δ-RE 2 Si 2 O 7 (Pna2 1 ) structure. Thermal expansion measurements of Y 2 Si 2 O 7 and Gd 2 Si 2 O 7 correlated well with reported values in literature, and all synthesized solid solutions exhibited CTEs between Y 2 Si 2 O 7 and Gd 2 Si 2 O 7 . Generally, there was a slight decrease in CTE exhibited by the materials with increasing Gd 2 Si 2 O 7 content, with Gd 2 Si 2 O 7 having the lowest CTEs and Y 2 Si 2 O 7 the highest CTEs. The decrease in CTE was attributed to stronger bonds of Gd-O over Y-O, as determined by calculated crystal orbital Hamilton populations using density functional theory. However, such differences were very small and crystal structure was the dominating factor in CTE trends.

rare earth silicates↗
NASA NTRS2023

The Effect of Oxidation in Environmental Barrier Coatings Subject to Foreign Object Damage

Oxidation and foreign object damage (FOD) are two key failure modes for environmental barrier coatings (EBCs). For EBCs with a silicon (Si) bond coat, a thermally grown oxide (TGO) layer forms at the EBC –bond coat interface. The TGO layer is considered the weak interface, and directly influences the life of the EBC. Moreover, FOD has been shown to cause significant subsurface damage resulting in delamination or spallation of the EBC which can occur at the EBC -bond coat interface or the bond coat -substrate interface. The purpose of this work is to investigate the synergistic effects of oxidation and FOD in a ytterbium disilicate (𝑌𝑏2𝑆𝑖2𝑂7) EBC. FOD testing is conducted on as-deposited and steam oxidized samples at room temperature using a 1.59-mm hardened steel ball projectile. The resulting damage is characterized by optical profilometry and scanning electron microscopy (SEM). Additionally, a quasi-static, mechanical assessment of the EBC bond strength in the presence of a growing TGO is presented.

environmental barrier coatings (EBCs)↗
NASA NTRS2023

High Temperature Solid Particle Erosion of Environmental and Thermal Barrier Coatings

Solid particle erosion (SPE) is a common phenomenon observed in gas turbine engines. Particles entrained in the gas flow impact engine hardware resulting in micro-scale damage that leads to deleterious effects such as material removal. For protective coatings, damage due to SPE is a key concern since it can negatively affect the durability of the coating and subsequently the life of the underlying component. In this work, the high temperature SPE behavior of two state-of-the-art environmental barrier coatings (EBCs) deposited via air plasma spray (APS) is investigated using alumina erodent to understand the effect of particle kinetic energy, impingement angle and temperature. The SPE behavior of the EBCs is also compared to APS and electron beam – physical vapor deposition (EB-PVD) thermal barrier coatings (TBCs) to elucidate similarities and differences in the erosion response. The EBCs were more susceptible to SPE than the EB-PVD TBC but had greater SPE resistance compared to the APS TBC. Coating microstructure and porosity were shown to have a strong influence on the observed behavior.

Solid particle erosion↗
NASA NTRS2022

Thermochemical Degradation of HfSiO4 by Molten CMAS

The thermochemical degradation of hafnium silicate (HfSiO4) was investigated with a molten calcium-magnesium-aluminosilicate (CMAS) glass relevant to gas turbine engine applications. Sintered HfSiO4 coupons were fabricated, within which wells were drilled and filled with CMAS glass powder at a loading of ~35 mg/cm2. Samples were heat treated at1200°C, 1300°C, 1400°C, and 1500°C for 1 hour, 10 hours, and 50 hours. At 1200°C and1300°C, slow formation of a Ca2HfSi4O12 cyclosilicate phase was observed at the HfSiO4-CMASinterface. At 1300°C and higher, rapid infiltration of CMAS into the material along the grain boundaries was observed. Initial conjecture into CMAS degradation mechanisms of HfSiO4 are presented herein.

CMAS↗
NASA NTRS2021

Optimizing Surfactant Templating of Yttria-Stabilized Zirconia Aerogels for High-Temperature Applications: Effect of Cationic Surfactant

Aerogels can be used in spaceflight applications as thermal insulators due to their low density, low thermal conductivity, and tortuous path for solid conduction. However, the aerogel formulation must be optimized to increase the thermal stability of the aerogels, as a drastic densification and decrease in surface area often is exhibited after high-temperature exposure. This work considers yttria-stabilized zirconia (YSZ) aerogels, whichhave low thermal conductivity and are expected to be used for temperatures between 600°C and 1000°C. It is anticipated that new sol-gel chemistries will yield YSZ aerogels that exhibit retained mesoporous structure, increased surface area, and minimized shrinkage upon exposure to higher temperatures in the expected use range. This work investigates the addition of surfactant to 20 mol% YSZ aerogels. The cationic surfactant, cetrimonium bromide (CTAB), was used as the templating agent, preventing the collapse of the mesoporous structure upon gelation and drying. It was determined that adding one-half times the critical micelle concentration of CTAB increased the surface area of the aerogels by 72% and 41% and increased the pore volume following exposure to 600°C and1000°C, respectively. This level of CTAB had the greatest increase in surface area and pore volume as compared to aerogels without CTAB or with twice the critical micelle concentration of CTAB. By optimizing the concentration of CTAB, the thermal stability ofYSZ aerogels can be enhanced to make these materials more efficient when used as thermal management systems.

Yttria-stabilized zirconia aerogel↗
NASA NTRS2021

Thermal Expansion Coefficients of Ca2Y8(SiO4)6O2 and Ca2Yb8(SiO4)6O2 Apatite-type Silicates

High temperature X-ray diffraction (XRD) scans of Y2Si2O7 and Yb2Si2O7 reactions with calcium-magnesium-aluminosilicates (CMAS) were utilized to determine thermal expansion coefficients (CTEs) of Ca2Y8(SiO4)6O2 and Ca2Yb8(SiO4)6O2 apatite materials. In order to validate these measurements, the CTEs of Y2Si2O7, Yb2Si2O7 and SiO2 were also determined from the same scans. The directional CTEs for γ-Y2Si2O7 were determined to be αa=5.84×10-6/K, αb=6.81×10-6/K and αc=0.81×10-6/K, and β-Yb2Si2O7 was determined to have values of αa=6.89×10-6/K, αb=4.81×10-6/K and αc=2.78×10-6/K. The average CTEs of γ-Y2Si2O7 and β-Yb2Si2O7 were determined to be 4.5×10-6/K and 4.7×10-6/K, respectively, which agreed with previous analyses. Ca2Y8(SiO4)6O2 exhibited directional CTEs of αa=9.36×10-6/K and αc=7.95×10-6/K (averaged between two sets of data), whereas Ca2Yb8(SiO4)6O2 had values that were very similar (αa=9.63×10-6/K, αc=7.45×10-6/K). Both results for the Ca2RE8(SiO4)6O2 apatites correlated well with the limited data on apatite-type silicates available in literature.

rare earth↗
NASA NTRSDate not supplied

Optimization of Aerogels for High Temperature Applications

Aerogels can be used in spaceflight applications as thermal insulators due to their low density, low thermal conductivity, and tortuous path for solid conduction. However, the aerogel formulation must be optimized to increase the thermal stability of the aerogels as drastic densification and decrease in surface area is often exhibited after high-temperature exposure. Current research investigates yttria-stabilized zirconia (YSZ) aerogels, which have low thermal conductivity and are expected to be used between 600°C and 1000°C. We anticipate that new sol-gel chemistries and processing will yield YSZ aerogels that display retained mesoporous structure, increased surface area, and minimized shrinkage upon exposure to higher temperatures in the projected use range. This work investigates the cationic surfactant, cetrimonium bromide (CTAB), as a templating agent to prevent the collapse of the aerogel pore structure upon gelation and drying. It was determined that adding one-half times the critical micelle concentration (CMC) of CTAB increased the surface area and pore volume of the aerogels, as compared to aerogels without CTAB or with twice the CMC of CTAB, following high-temperature exposure. By optimizing CTAB, the thermal stability of YSZ aerogels can be enhanced to make these materials more efficient when used as thermal management systems.

Rebecca C Walker↗
NASA NTRSDate not supplied

A Machine Learning-Derived Atomistic Potential for Y2Si2O7

Incorporation of SiC/SiC ceramic matrix composite (CMC) hot section components into aircraft engines promises to increase efficiency and safety. However, SiC/SiC CMCs are subject to water vapor-induced oxidation and recession at the high temperatures of engine operation, and thus environmental barrier coatings (EBCs) are required to reduce this degradation and enable their widespread adoption. An understanding of EBCs failure mechanisms, including thermochemical and thermomechanical mechanisms, is essential as coating degradation leads to reduced CMC component service life. Computational modeling approaches can provide insight into EBC material properties important for coating design. However, density functional theory (DFT) is computationally expensive and atomistic potentials are lacking for materials of interest. In this work, we utilize a machine learning approach and DFT training data to parameterize atomistic potentials for two candidate EBC materials, Y2Si2O7 and Yb2Si2O7. These potentials enable near DFT-accurate calculations of thermodynamic and thermomechanical properties essential to EBC design.

Cameron J Bodenschatz↗
NASA NTRSDate not supplied

Thermochemical/Thermomechanical Synergies in High Temperature Solid Particle Erosion of CMAS-Exposed EBCs

Environmental barrier coatings (EBCs) are an enabling technology for the use of SiC-based ceramic matrix composites in next generation gas turbine engines. In the extreme engine environment, EBCs must be able to withstand a variety of individual damage mechanisms and their interactions with each other. Ingested particulates/debris can cause both thermochemical and thermomechanical degradation of EBCs. Siliceous debris primarily based on calcium magnesium aluminosilicates (CMAS) can melt and infiltrate and/or react with EBCs above >1200°C. Similarly, ingested debris can lead to mechanical damage and recession of coatings due to particulate erosion. Both modes of degradation can occur simultaneously during engine operation, and it is crucial to comprehensively understand the mechanisms of coating failure due to high-temperature particulate interactions. This study assesses the erosion durability of Yb2Si2O7-based EBCs exposed to CMAS of various loads in NASA Glenn’s Erosion Burner Rig Facility. CMAS exposures and erosion testing were carried out at 1316°C. The effects of CMAS loading and exposure time on EBC erosion durability were evaluated using Al2O3 as an erodent material.

EBC↗
NASA NTRSDate not supplied

A Dynamic Testing Approach for Particulate Erosion–Corrosion for Gas Turbine Coatings

Particle interactions in gas turbine engines can be multicomponent, complex phenomena leading to the degradation of thermal (TBCs) and environmental barrier coatings (EBCs) meant to protect engine components. Ingestion of particles into the engine can lead to recession of coatings due to particle erosion. Similarly, these same particles can become molten, adhere to coatings and result in thermochemical corrosion of coating materials. Particle erosion testing is often carried out where the particles are injected into a gas stream, accelerated within a nozzle, and impinge on sample. Conversely, most molten particle corrosion testing is often done in static laboratory furnaces, which does not capture the dynamic nature of deposition in application. Nevertheless, these damage mechanisms are often tested separately and no single standard exists to test both erosive and corrosive particle interactions with coating materials under relevant operating conditions for gas turbine engines. Understanding the synergies of particle interactions in engines is crucial in determining operating lifetimes of potential coating materials. Such considerations emphasize the need for realistic approaches in standardizing particle interaction testing in combustion environments. The current study outlines initial efforts at NASA Glenn’s Erosion Burner Rig Facility in improving dynamic erosion/corrosion testing methods by assessing the durability of state-of-the-art (SOA) TBC material 7 wt.% yttria stabilized zirconia (7YSZ) as a function of particle deposition rate, burner temperature, and particle size. Calibration data to determine particle deposition rate will be presented, and mass and optical profilometry measurements were utilized to estimate mass/volume loss versus deposition per increment of particulate used over time. Electron microscopy analyses were then carried out to assess coating damage after testing.

TBC↗
NASA NTRSDate not supplied

Foreign Object Damage in Yb 2 Si 2 O 7 Environmental Barrier Coatings

Environmental Barrier Coatings (EBCs) have been developed as an enabling technology for silicon carbide based ceramic matrix composites in gas turbine engines. Two of the key failure mechanisms identified in EBC systems are foreign object damage (FOD) and the oxidative growth of a SiO 2 thermally grown oxide (TGO) layer that can lead to premature coating spallation. Previously the effects of FOD on NASA’s second generation Ytterbium Disilicate EBC were studied and recently it was shown that the addition of oxide modifiers resulted in improved oxidation resistance in the EBC. This work will compare FOD of the baseline Ytterbium Disilicate EBC to the that of the modified EBC. FOD was performed at room temperature using a 1.59 mm hardened steel ball with projectile velocities of 50-300 m/s. Additionally, the effects of oxidation via cyclic steam exposure prior to impact were investigated.

environmental barrier coatings (EBCs)↗
NASA NTRSDate not supplied

Advanced Environmental Barrier Coating Testing and Development for Gas Turbine Engines

Environmental barrier coatings (EBCs) are an enabling technology for the use of SiC-based ceramic matrix composites (CMCs) in next generation gas turbine engines. SiC-based CMCs are lightweight and have higher temperature stability than traditional nickel based superalloys. However, SiC is susceptible to rapid oxidation and recession due to high temperature reactions with water vapor and other combustion species. Thus, EBCs were developed to protect these components and extend operating lifetime. In the extreme engine environment, EBCs must be able to withstand a variety of damage mechanisms and the synergies of degradation between them. This presentation will provide an overview of NASA Glenn Research Center, current aeronautics research, and an introduction to EBC failure modes and environmental durability test methods.

Jamesa L Stokes↗