Polymorphic structure of $\langle a \rangle$-type screw dislocation cores in $\alpha$-Ti
The dislocation core structure has a significant role in determining the dominant slip plane and the magnitude of the Peierls stress for a dislocation. An important challenge when studying dislocation cores is to determine the stable and metastable core morphologies, and then relate these structures to the dynamics of the dislocations. ere this study introduces a method for identifying core structures that are metastable at zero temperature. Application of this method to $\langle$a$\rangle$-type screw dislocations in α-Ti (as described using an empirical potential) reveals a multitude of (meta)stable nonplanar cores. Molecular dynamics studies show how the competing metastable core structures determine the properties of the dislocations at temperature and under a range of non-Schmid stresses.