DOE OSTI2023

Improving Durability of Fuel Cells with Platinum-rich Alloy Cathode Catalysts

Pt 3 Co-alloy based nanoparticle catalysts are very active for oxygen reduction reaction (ORR) thereby enabling high performance of proton exchange membrane fuel cells (PEMFC) for automotive propulsion. However, these catalyst materials degrade due to a combination of electrochemical surface area (ECSA) loss and dissolution of cobalt-alloying element from the nanoparticles. Dissolution of cobalt has a two-fold impact on the durability of fuel cells—i) a loss in the low-current density kinetic region due to a decrease in specific activity and ii) a loss in the high-current density transport region due to Co 2+ contamination of the ionomer phase. Cobalt dissolution-contamination needs to be mitigated as it limits fuel cell performance and lifetime for heavy-duty automotive applications. In this article, we study the use of PtCo-alloy catalysts with Pt-rich compositions using catalyst-specific accelerated stress test measurement in membrane electrode assemblies to decrease the amount of dissolved Co and mitigate its subsequent contamination effects. We demonstrate Pt 5 Co and Pt 7 Co compositions to enable significant improvements in durability (∼50 mV and ∼100 mV with respect to Pt 3 Co after 30,000 voltage cycles) with a minor but acceptable compromise in the initial specific activity of the catalyst.

08 HYDROGEN↗

DOE OSTI2023

Stabilizing High–Nickel Cathodes with High–Voltage Electrolytes

Electrolytes connect the two electrodes in a lithium battery by providing Li + transport channels between them. Advanced electrolytes are being explored with high-nickel cathodes and the lithium-metal anode to meet the high energy density and cycle life goals, but the origin of the performance differences with different electrolytes is not fully understood. Here, the mechanisms involved in protecting the high-capacity, cobalt-free cathode LiNiO 2 with a model high-voltage electrolyte (HVE) are delineated. The kinetic barrier posed by a thick surface degradation layer with poor Li + -ion transport is found to be the major contributor to the fast capacity fade of LiNiO 2 with the conventional carbonate electrolyte. In contrast, HVE reduces the side reactions between the electrolyte and the electrodes, leading to a thinner nano-interphase layer comprised of more beneficial species. Crucially, the HVE leads to a different surface reorganization pathway involving the formation of a thinner nanoscale LiNi 2 O 4 spinel phase on the LiNiO 2 surface. Finally, with a high 3D Li + -ion and electronic conductivity, the spinel LiNi 2 O 4 reorganization nanolayer preserves fast Li + transport across the cathode–electrolyte interface, reduces reaction heterogeneity in the electrode and alleviates intergranular cracking within secondary particles, resulting in superior long-term cycle life.

25 ENERGY STORAGE↗

DOE OSTI2022

Molten-Salt Synthesis of O 3 -Type Layered Oxide Single Crystal Cathodes with Controlled Morphology towards Long-Life Sodium-Ion Batteries

Sodium layered oxides show great promise as affordable alternatives to lithium layered oxides, but their poor cycle life and air stability limit their practical potential. Micron-scale single crystals with greater packing density and lower surface area can overcome these challenges and improve performance compared to the traditional polycrystalline morphology. Herein, the authors present the synthesis of layered O 3 -type Na(Ni 0.3 Fe 0.4 Mn 0.3 )O 2 single-crystals with greatly improved cycle life and air stability. A molten-salt synthesis technique is adopted with excess sodium hydroxide to obtain platelet-like single crystals. Because the main mechanisms of both capacity fade and air degradation occur as a result of surface reactions at the opening of the sodium diffusion channels, particle morphology is found to be a critical metric for materials performance. More important than particle size or total surface area, the smaller proportion of exposed edge planes in the platelet morphology greatly reduces the amount of harmful surface reactions. Furthermore, the molten-salt method is found to eliminate the need for coprecipitated precursors and even form better morphology, starting from metal oxides instead of coprecipitated hydroxides.

25 ENERGY STORAGE↗

DOE OSTI2021

Mitigation of PtCo/C Cathode Catalyst Degradation via Control of Relative Humidity

Maintaining the high performance of proton-exchange membrane fuel cells (PEMFC) over the course of its lifetime is a key enabling factor for its successful commercialization as a primary power source in zero-emission transportation applications. In this context, it is important to mitigate the degradation of PtCo-alloy based cathode catalysts used for oxygen reduction reaction (ORR). PtCo-alloy catalysts exhibit high activity at beginning-of-life (BOL) which tends to decrease during operation due to loss of electrochemical surface area (ECSA) and dissolution-contamination related effects of the Co-alloying component. Here, we demonstrate the use of relative humidity (RH) of the inlet gases as a controllable parameter to mitigate the degradation of PtCo-alloy catalyst degradation. We employ a catalyst-specific voltage cycling accelerated stress test (AST) durability protocol as a function of inlet RH to degrade PtCo catalysts. A series of in situ electrochemical diagnostics and ex situ characterizations have been carried out to investigate the catalyst layer characteristics at end-of-test (EOT). Our results show that at sub-saturated conditions of durability protocol operation, PtCo catalyst sustains higher EOT H 2 /air performance due to better retention of ECSA and smaller impact of Co 2+ dissolution/contamination.

25 ENERGY STORAGE↗

DOE OSTI2021

Intrinsic Li Distribution in Layered Transition-Metal Oxides Using Low-Dose Scanning Transmission Electron Microscopy and Spectroscopy

Understanding Li distribution in layered lithium transition-metal oxide (LiTMO) cathodes in Li-ion batteries has been a major challenge at the atomic scale and nanoscale. Li is extremely difficult to study by transmission electron microscopy (TEM) because the high-energy electrons impart significant energy and cause massive migration. Here, we directly map the intrinsic spatial distribution and bonding of Li in LiNiO 2 -layered cathode materials using low-dose and low-loss electron energy loss spectroscopy (EELS). EELS spectra of the Li–K edge are measured simultaneously with O–K and Ni–L, M 3,2 edges from layered, cation-mixed, and rock-salt phases and directly matched with atomic-resolution scanning TEM images to correlate the changes in peak intensities and positions to the stoichiometry changes with continual loss of Li and O. Changes in the Li content in the LiNiO 2 particles as a function of electron beam dose are studied by sequential Li spectroscopic mapping. We show that the “intrinsic” Li distribution can be observed using a total dose of less than ~1.5 × 10 8 e – nm –2 at an accelerating voltage of 80 kV. The method of nanoscale mapping of Li distribution introduced in this study is applicable to high-Ni LiTMO cathode materials (>89% of Ni) as well as LiNiO 2 . Further study on the extra peaks of the Li–K edge reveals that the peak at ~59 eV is from the Li ions intercalated in between NiO 2 layers barely interacting with each other with less Li K shell electrons pulled to the L shell electrons in NiO 2 . Furthermore, the results shown here provide improved low-loss TEM characterization approaches that can be used to understand the intrinsic fundamental behaviors in Li-ion batteries.

25 ENERGY STORAGE↗