DOE OSTI2024

Unveiling the Thermal Stability of Sodium Ion Pouch Cells Using Accelerating Rate Calorimetry

The thermal stability of ~420 mAh Na 0.97 Ca 0.03 [Mn 0.39 Fe 0.31 Ni 0.22 Zn 0.08 ]O 2 (NCMFNZO)/hard carbon (HC) pouch cells was investigated using accelerating rate calorimetry (ARC) at elevated temperatures. 1 m NaPF 6 in propylene carbonate (PC):ethyl methyl carbonate (EMC) (1:1 by volume) was used as a control electrolyte. Adding 2 wt% fluoroethylene carbonate to the electrolyte improves the cell's thermal stability by decreasing the self-heating rate (SHR) across the whole testing temperature range. The selected states-of-charge (SoC), including 70%, 84%, and 100%, exhibit minimal impact on the exothermic behavior, except for a slight decrease in SHR after ~275 °C at 70% SoC. When compared to traditional lithium-ion batteries operating at 100% SoC, NCMFNZO/HC pouch cells demonstrate inferior thermal stability compared to LiFePO 4 (LFP)/graphite pouch cells, displaying a higher SHR from 220 to 300 °C. LiNi 0.8 Mn 0.1 Co 0.1 O 2 /graphite + SiO x pouch cells exhibit the worst safety performance, with an early onset temperature of ~100 °C and the highest SHR across the entire temperature range. These results offer a direct comparison of the impact of SoC and electrolyte compositions on the thermal stability of SIBs at elevated temperatures, highlighting that there is still room for improvement in SIBs safety performance compared to LFP/graphite chemistry.

42 ENGINEERING↗

DOE OSTI2024

Weakly solvating ester electrolyte for high voltage sodium-ion batteries

Ethyl acetate (EA) was identified as a promising electrolyte solvent for sodium-ion batteries (SIBs), exhibiting low viscosity, cost-effectiveness, and low toxicity. Despite a significant portion of aggregation being linked to the weak solvation of Na + /EA as revealed by molecular dynamics (MD) simulations, pulsed-field gradient nuclear magnetic resonance (pfg-NMR) analysis identified a noteworthy Na+ diffusion coefficient of 3.95×10 -10 m 2 s -1 at 25°C in the presence of 1 m NaPF 6 salt. Employing fluoroethylene carbonate (FEC) as a film-forming additive to create electrode-electrolyte interphase, this electrolyte surprisingly made ~210 mAh Na 0.97 Ca 0.03 [Mn 0.39 Fe 0.31 Ni 0.22 Zn 0.08 ]O 2 (NCMFNZO)/hard carbon (HC) pouch cells achieve a lengthy cycling lifetime of 250 cycles with ~80 % capacity retention, cycled up to 4.0 V at 40°C. X-ray photoelectron spectroscopy (XPS) revealed increasing interphasial organic species over cycling, augmenting charge transfer resistance on both cathode and anode, particularly during fast charging or low temperatures (<10°C), promoting Na plating. Finally, gas chromatography-mass spectrometry combined with density functional theory identified CO 2 as the major gas generated from charged cathode/electrolyte interactions, exhibiting temperature/voltage dependence.

25 ENERGY STORAGE↗

DOE OSTI2024

Communication — The Impact of Co-solvent Selection for Dimethyl-2,5-dioxahexane carboxylate in Sodium Ion Batteries

Traditional linear carbonates including dimethyl carbonate (DMC), diethyl carbonate (DEC), and ethyl methyl carbonate (EMC) were investigated as co-solvents for the dimethyl-2,5-dioxahexane carboxylate (DMOHC)-based electrolyte in Na 0.97 Ca 0.03 [Mn 0.39 Fe 0.31 Ni 0.22 Zn 0.08 ]O 2 (NCMFNZO)/hard carbon (HC) pouch cells. The EMC-containing cell displays excellent electrochemical performance, exhibiting only a 1.6 mAh irreversible capacity loss during 500 h of storage at 4 V and 40 °C, and maintaining over 80% capacity retention after 200 cycles up to 4 V at 40 °C. Severe gas evolution and Na plating issues are present in all the tested systems.

25 ENERGY STORAGE↗

DOE OSTI2023

The Impact of Fluoroethylene Carbonate Additive on Charged Sodium Ion Electrodes/Electrolyte Reactivity Studied Using Accelerating Rate Calorimetry

The effects of fluoroethylene carbonate (FEC) electrolyte additive on charged sodium ion electrode/electrolyte reactivity at elevated temperatures were investigated using accelerating rate calorimetry (ARC). The beneficial effect of FEC on cell lifetime was demonstrated using Na 0.97 Ca 0.03 [Mn 0.39 Fe 0.31 Ni 0.22 Zn 0.08 ]O 2 (NCMFNZO)/hard carbon (HC) pouch cells first prior to ARC measurements. Electrodes from these pouch cells were utilized as sample materials and 1.0 M NaPF 6 in propylene carbonate (PC):ethyl methyl carbonate (EMC) (1:1 by vol.) was chosen as control electrolyte. Adding 2 wt% and 5 wt% FEC to the electrolyte does not significantly affect the reactivity of de-sodiated NCMFNZO compared to the control electrolyte. However, the addition of FEC obviously changed the reactivity between sodiated HC and electrolytes, especially by showing a suppression on the exothermal behavior between 160 °C and 230 °C. These results give a head to head comparison of the reactivity of FEC additive containing electrolytes with charged sodium ion electrode materials at elevated temperatures and show that the use of FEC at additive levels should not compromise the cell safety when extending cell lifetime.

25 ENERGY STORAGE↗

DOE OSTI2023

Understanding High-Voltage Behavior of Sodium-Ion Battery Cathode Materials Using Synchrotron X-ray and Neutron Techniques: A Review

Despite substantial research efforts in developing high-voltage sodium-ion batteries (SIBs) as high-energy-density alternatives to complement lithium-ion-based energy storage technologies, the lifetime of high-voltage SIBs is still associated with many fundamental scientific questions. In particular, the structure phase transition, oxygen loss, and cathode–electrolyte interphase (CEI) decay are intensely discussed in the field. Synchrotron X-ray and neutron scattering characterization techniques offer unique capabilities for investigating the complex structure and dynamics of high-voltage cathode behavior. In this review, to accelerate the development of stable high-voltage SIBs, we provide a comprehensive and thorough overview of the use of synchrotron X-ray and neutron scattering in studying SIB cathode materials with an emphasis on high-voltage layered transition metal oxide cathodes. We then discuss these characterizations in relation to polyanion-type cathodes, Prussian blue analogues, and organic cathode materials. Finally, future directions of these techniques in high-voltage SIB research are proposed, including CEI studies for polyanion-type cathodes and the extension of neutron scattering techniques, as well as the integration of morphology and phase characterizations.

25 ENERGY STORAGE↗