DOE OSTI2023

Improved Performance of Silicon-Containing Anodes with Organic Solvent-Solubilized Lithium Nitrate

Three different organic solvents (dimethylacetamide (DMAc), dimethylformamide (DMF), and dimethyl sulfoxide (DMSO)) were used to improve the solubility of LiNO 3 in a standard carbonate-based electrolyte with lithium difluoro(oxalato)borate (LiDFOB) as the salt. Together, the LiDFOB and organic-solvent solubilized LiNO 3 preferentially reduce on the surface of silicon-containing anodes to create an SEI rich in oxalates, nitrate decomposition species, and B-F species. The improved stability of the SEI throughout the first 100 cycles results in silicon and silicon/graphite composite anodes with better capacity retention than observed with standard electrolytes or fluoroethylene carbonate (FEC) containing electrolytes. This study demonstrates the feasibility of the use of non-traditional electrolyte solvents in the improvement and optimization of lithium ion-battery electrolytes.

25 ENERGY STORAGE↗

DOE OSTI2022

Use of Ethylene Carbonate Free Ester Solvent Systems with Alternative Lithium Salts for Improved Low-Temperature Performance in NCM622∣∣ Graphite Li-ion Batteries

An investigation of alternative lithium salts, lithium tetrafluoroborate (LiBF 4 ), lithium difluoro(oxalato)borate (LiDFOB) and lithium hexafluorophosphate (LiPF 6 ), in novel ester-based (methyl acetate/fluoroethylene carbonate- MA/FEC or methyl propionate/fluoroethylene carbonate- MP/FEC) electrolyte formulations has been conducted in LiNi 0.6 Co 0.2 Mn 0.2 O 2 (NCM622)/graphite cells to improve low temperature cycling performance of lithium ion batteries at −20 °C. Improved low temperature performance was observed with all the lithium salts in MA/FEC electrolyte while comparable room temperature (25 °C) capacities were observed with LiPF 6 salt only. Detailed ex-situ analysis of surface films generated with LiBF 4 , LiDFOB and LiPF 6 in ester-based electrolytes reveals that the solid electrolyte interphase (SEI) is predominately composed of lithium salt decompaction products and addition of 10% FEC (by volume%) may not be sufficient at forming a protective SEI.

25 ENERGY STORAGE↗

DOE OSTI2022

Investigation of the Electrode-Electrolyte Interphase in Ester-Based Electrolytes in NCM523/Graphite Cells

The use of methyl acetate (MA) and methyl propionate (MP) as co-solvents in carbonate/LiPF 6 electrolytes have been investigated in LiNi 0.5 Co 0.2 Mn 0.3 O 2 (NCM523)/graphite cells to improve electrochemical performance at low temperature (−20 °C). Consistent with previous investigations, improved low temperature performance was observed with all electrolyte formulations containing esters. Detailed ex situ surface analysis of the surface films generated with the ester-based electrolytes containing electrolyte additives reveal significant changes to the SEI on graphite upon cycling at moderately elevated temperature (45 °C). In the presence of vinylene carbonate (VC) lithium plating is observed upon cycling at low temperature (−20 °C) which leads to a thicker solid electrolyte interface (SEI) upon cycling at 45 °C. Incorporation of fluoroethylene carbonate (FEC) as an electrolyte additive results in the generation of a thin SEI and alters the structure of the surface film on the NCM523 cathode resulting in stable cycling over a wide temperature range.