Jech, R. W.

Publications and source records attributed to Jech, R. W..

At least 19 records
All sourcesNASA NTRSDOE OSTI
NASA NTRS1985

Ductility in rapidly solidified NiAl

An attempt is made to refine the grain structure of equiatomic NiAl by means of rapid solidification processing, and to examine the effect of small grain size on room temperature ductility. Free melt spinning was used to produce the rapidly solidified material. Room temperature bend testing of both as-spun and heat-treated NiAl ribbon was conducted by free bending the ribbon around a mandrel of successively smaller diameter until failure occurred. Room-temperature plastic deformation was exhibited both before and after a 1-h heat treatment at 1000 C. Heat treatment increased the observed ductility.

Gaydosh, D. J.↗
NASA NTRS1984

Rapid solidification via melt spinning - Equipment and techniques

One of the simpler methods available to accomplish rapid solidification processing is free jet melt spinning. With only a modest expenditure of time, effort, and capital, an apparatus suitable for preliminary experimentation can be assembled. Wheel and crucible materials, process atmospheres, crucible design, heating methods, and process parameters and their relationship to melt composition are described. Practical solutions to processing problems, based on 'hands-on' experience, are offered. Alloys with melting points up to 3000 F have been rapidly solidified using the techniques described.

Jech, R. W.↗
NASA NTRS1979

Evaluation of silicon carbide fiber/titanium composites

Izod impact, tensile, and modulus of elasticity were determined for silicon carbide fiber/titanium composites to evaluate their potential usefulness as substitutes for titanium alloys or stainless steel in stiffness critical applications for aircraft turbine engines. Variations in processing conditions and matrix ductility were examined to produce composites having good impact strength in both the as-fabricated condition and after air exposure at elevated temperature. The impact strengths of composites containing 36 volume percent silicon carbide (SiC) fiber in an unalloyed (A-40) titanium matrix were found to be equal to unreinforced titanium-6 aluminum-4 vanadium alloy; the tensile strengths of the composites were marginally better than the unreinforced unalloyed (A-70) matrix at elevated temperature, though not at room temperature. At room temperature the modulus of elasticity of the composites was 48 percent higher than titanium or its alloys and 40 percent higher than that of stainless steel.

Jech, R. W.↗
NASA NTRS1975

Critical aspect ratio for tungsten fibers in copper-nickel matrix composites

Stress-rupture and tensile tests were conducted at 816 C (1500 F) to determine the effect of matrix composition on the minimum fiber length to diameter ratio (critical aspect ratio) below which fibers in a tungsten fiber/copper-nickel alloy matrix composite could not be stressed to their ultimate load carrying capability. This study was intended to simulate some of the conditions that might be encountered with materials combinations used in high-temperature composites. The critical aspect ratio for stress-rupture was found to be greater than for short-time tension, and it increased as the time to rupture increased. The increase was relatively slight, and calculated fiber lengths for long service appear to be well within practical size limits for effective reinforcement and ease of fabrication of potential gas turbine components.

Jech, R. W.↗
NASA NTRS1972

Required critical aspect ratio of fibers intended for stress rupture applications.

The observed critical aspect ratio for pullout specimens of tungsten wire in a copper matrix tested in stress rupture at 649 and 816 C was slightly greater than for tension tests at the same temperature. Time for failure of the stress rupture specimens was controlled by the properties of the fiber (tungsten) at aspect ratios greater than the critical aspect ratio and by the properties of the matrix (copper) at aspect ratios less than the critical ratio.