NASA NTRS1993

Compressive behavior of undulations in filament-wound composites

The compressive performance of a filament-wound cylinder can be severely degraded by unavoidable fiber curvatures due to the presence of crossover bands. These crossover bands contain fiber undulations which influence the compressive strength, stiffness, and associated failure mechanisms of a filament-wound structure. The primary objectives of this study were to identify failure mechanisms and measure the compressive strength and stiffness of test specimens which model the microundulations. Compressive tests were conducted on flat-panel coupons which were developed to model the mechanics of large-scale fiber undulation regions in filament-wound composite cylinders. The primary effect of the undulation regions within a filament-wound structure is to initiate failure. Depending on the overall laminate configuration, the failure process includes various combinations of failure mechanisms, such as delaminations, matrix splitting and/or fiber fracture. These failure mechanisms are aggravated by the presence of large deformations caused by the reduction in local compressive stiffness and the introduction of complex material couplings due to the fiber undulation. Furthermore, the adjacent layers have been shown to strongly influence the compressive strength, stiffness, and associated failure mechanisms by weakening or reinforcing the laminate.

Jensen, David W.↗

NASA NTRS1992

Design and analysis of filament-wound cylinders in compression

The objective of the study was to develop a more accurate model for the prediction of the compressive behavior of filament-wound composite cylindrical shells. Results from a closed-form analytical model and a three-dimensional finite element model show that the extensional and bending stiffness of the laminate is significantly reduced in tow cross-over regions and that bending-extension coupling is increased in comparison with classical lamination theory. The material properties predicted by a micromechanics analysis are included in a global finite element model of a filament-wound circular cylindrical shell which also incorporates variations in the laminate stacking thickness. Results from the global shell analysis are compared with experimental data.

Hipp, Patrick A.↗

NASA NTRS1991

Scalable Performance Environments for Parallel Systems

As parallel systems expand in size and complexity, the absence of performance tools for these parallel systems exacerbates the already difficult problems of application program and system software performance tuning. Moreover, given the pace of technological change, we can no longer afford to develop ad hoc, one-of-a-kind performance instrumentation software; we need scalable, portable performance analysis tools. We describe an environment prototype based on the lessons learned from two previous generations of performance data analysis software. Our environment prototype contains a set of performance data transformation modules that can be interconnected in user-specified ways. It is the responsibility of the environment infrastructure to hide details of module interconnection and data sharing. The environment is written in C++ with the graphical displays based on X windows and the Motif toolkit. It allows users to interconnect and configure modules graphically to form an acyclic, directed data analysis graph. Performance trace data are represented in a self-documenting stream format that includes internal definitions of data types, sizes, and names. The environment prototype supports the use of head-mounted displays and sonic data presentation in addition to the traditional use of visual techniques.

Reed, Daniel A.↗

NASA NTRS1991

Compressive testing of filament-wound cylinders

An experimental investigation has been conducted on the compressive buckling and failure of filament-wound circular cylinders. This investigation identifies one of the relationships between structural performance and scale, as well as some of the causes of reduced structural performance in large-scale structures. It is hypothesized that this effect is related to two conditions: first, the number of fiber tow undulations; and second, the percentage of weak interfaces within the structure. The effect of winding pattern and the resulting location of the fiber undulations were studied by varying the winding parameters. Three types of cylinders were manufactured from Amoco T650-35/1908 graphite/epoxy preimpregnated tow with different winding sequences (0/+/-60)s, (+/-30/90)s, and (90/+/-30)s. The (90/+/-30)s cylinders were manufactured with two different winding patterns (distributed and classical) and radius-to-thickness ratios (15 and 55). All cylinders were loaded in compression to failure. Comparisons of the compressive strength and failure modes demonstrate the relationship between the winding parameters, scale, and structural performance of filament-wound composite cylinders.

Jensen, David W.↗

NASA NTRS1990

Ray tracing on distributed memory parallel systems

Among the many techniques in computer graphics, ray tracing is prized because it can render realistic images, albeit at great computational expense. In this note, the performance of several approaches to ray tracing on a distributed memory parallel system is evaluated. A set of performance instrumentation tools and their associated visualization software are used to identify the underlying causes of performance differences.

Jensen, David W.↗

NASA NTRS1990

Defect sensitivity of filament-wound structures in compression

Compression testing of 12-ply graphite/bismaleimide laminated plates with induced and natural defects is discussed, and emphasis is placed on resultant changes in strength and stiffness. Ply drops, ply cuts, and fiber crossovers are studied by comparison with a quasi-isotropic control group. It is observed that, as expected, failure initiates at the defects and progresses via delamination, sublaminate buckling, angle-ply cracking, and longitudinal ply failure. The ultimate stress is reduced by approximately 40 percent for all types of defects except the unsymmetrical cut-ply specimens which averages a 54-percent reduction. The average stiffness reduction of 10 percent is observed for specimens with induced defects. Fiber crossovers are found to reduce the laminate strength and stiffness significantly.

Jensen, David W.↗