Engineering topics
Jesus, Lílian M.
Publications and source records attributed to Jesus, Lílian M..
In-situ synchrotron X-ray diffraction of hydroxyapatite-zirconia composite during conventional and flash sintering
Here, we conducted in-situ X-ray diffraction to study the crystalline phase evolution in hydroxyapatite-zirconia composites during both conventional and flash sintering processes. Additionally, we examined the thermal history and microstructure of the composite under these sintering conditions. Despite both sintering methods reaching similar average temperatures, they yielded distinct results in terms of crystalline phase composition and microstructure. In the flash sintered samples, we observed a complete transformation of hydroxyapatite into α- tricalcium phosphate and a complete tetragonal to cubic phase transition in zirconia. Conversely, the conventionally sintered samples remained practically stable. Notably, the flash sintered samples exhibited needle-like microstructures, which were absent in their conventionally sintered counterparts. This divergence suggests that the application of an electric field plays a role in generating athermal effects during the sintering of hydroxyapatite-zirconia composites.
Phase evolution during conventional and reactive flash sintering of (Mg,Ni,Co,Cu,Zn)O via in situ X-ray diffraction
Reactive flash sintering (RFS) enables the simultaneous synthesis and sintering of ceramics and has been shown to affect the reaction pathway of different materials. Herein, in situ synchrotron X-ray diffraction (XRD) is used to investigate the (Mg,Ni,Co,Cu,Zn)O entropy-stabilized oxide formation during: (i) conventional heating and (ii) RFS under current rate-controlled mode. The same reaction pathway is verified in both instances: the starting rock-salt (RS), spinel (Co 3 O 4 ), tenorite (CuO), and wurtzite (ZnO) phases transform into a single RS phase with a (1 1 1) to (2 0 0) intensity ratio of 0.67, consistent with a random distribution of the cations into the structure. Pt lattice peak shift from the XRD patterns is used as standard to monitor the sample surface temperature, revealing a strong endothermic reaction during the RS single-phase formation (Pt peaks shift toward higher angles while increasing sample temperature/current density). Furthermore, in RFS, the single-phase RS structure is formed in just 60 s at a furnace temperature of 600°C and a current rate of 220 mA mm -2 /min. Therefore, RFS greatly accelerates the synthesis of (Mg,Ni,Co,Cu,Zn)O, however, it does not play a role in the reaction pathway for this material formation.
Phase evolution during reactive flash sintering of Li 6.25 Al 0.25 La 3 Zr 2 O 12 starting from a chemically prepared powder
Here, reactive flash sintering (RFS) of a chemically prepared multiphase precursor powder was performed to fabricate Li 6.25 Al 0.25 La 3 Zr 2 O 12 (Al-LLZO) ceramics. This approach allowed for obtaining single-phase dense samples in a remarkably short processing time of 30 s, at a furnace temperature of 600 °C, with an electric field of 50 V cm -1 and a current limit of 150 mA mm -2 . The ceramics display high bulk conductivity of 0.18 mS cm -1 at room temperature. Furthermore, phase evolution is studied by in-situ X-ray diffraction during: i) conventional heating and ii) RFS under current rate mode. As expected, the intermediate phases progressively dissolved into the Al-LLZO matrix by conventional heating. On the other hand, RFS promoted the growth of the intermediate La 2 Zr 2 O 7 , an effect that was overcome by the thermally driven formation of Al-LLZO at higher temperatures. The observed different reaction pathway suggests that RFS can be used for stabilizing phases that are not thermodynamically favored upon conventional heating.