NASA NTRS1990

The microstructure and properties of rapidly solidified, dispersion-strengthened NiAl

An advanced rapid solidification technology for processing reactive and refractory alloys, utilized to produce large quantities of melt-spun filaments of NiAl, is presented. The melt-spun filaments are pulverized to fine particle sizes, and subsequently consolidated by hot extrusion or hot isostatic pressing. Rapid solidification process gives rise to very fine-grained microstructures. However, exposure to elevated temperature during hot consolidation leads to grain growth. Alloying agents such as borides, carbides, and tungsten can pin the grain boundaries and retard the grain growth. Various alloy compositions are investigated. The eventual goal is to utilize the hot-extruded and forged stock to grow single-crystal NiAl blades for advanced gas-turbine engine applications. Single-crystal NiAl, containing a uniform dispersion of carbide strengthening precipitates, is expected to lead to highly creep-resistant turbine blades, and is of considerable interest to the aerospace propulsion industry.

Jha, S. C.↗

NASA NTRS1989

Dispersoids in rapidly solidified B2 nickel aluminides

Rapid solidification processing has been successfully used to create a uniform distribution of 30-nm TiB2 and HfC precipitates in a B2-ordered NiAl matrix, in order to enhance the matrix material's high-temperature strength and creep behavior. Attention is drawn to the question of the stability of carbide and boride dispersoids in an NiAl matrix during high-temperature exposures. The present alloys were consolidated at temperatures above 1422 K; the small size of precipitates in materials processed at such high temperatures gives an indication of their thermal stability, and further coarsening of the precipitates at elevated service temperatures is rendered unlikely by their low solubility in the matrix.

Jha, S. C.↗

NASA NTRS1988

Dispersion strengthened NiAl alloys produced by rapid solidification processing

Initial experimental results are presented concerning the relationship between microstructure and properties in rapidly solidified NiAl alloys whose melting point is of the order of 1900 K. When the dispersoid content of NiAl alloys is increased, the dispersoids begin to populate the grain boundaries, rendering them weak, so that failure must propagate intergranularly. It is concluded that NiAl alloys' strength can be significantly increased through dispersoid additions without sacrifice of high temperature ductility.

Jha, S. C.↗