DOE OSTI2024

Structure-property relationship between lignin structures and properties of 3D-printed lignin composites

Lignin is a low-cost and renewable bioresource with a huge annual production promising to prepare sustainable materials. However, the poor interfacial adhesion between many lignin-polymer pairs deteriorates the mechanical performance of the composites, which seriously limits the application of lignin in 3D printing via fused depositional modeling. This work examined lignin-polyamide 12 (PA 12) intermolecular interactions (e.g., hydrogen bonding) to address the interface challenge. To realize this goal, the phenolic hydroxyl content was increased for a kraft softwood lignin using a LiBr/HBr demethylation procedure, increasing phenoxy content by 61.7%. Increased hydrogen bonding interactions between modified lignin (Pine-Lig-OH) and PA 12 demonstrated a significantly improved molten dynamic modulus by rheological analysis. Regarding mechanical properties, by adding 20 wt% of Pine-Lig-OH, the tensile strength and Young's modulus reached 46.6 MPa and 1.62 GPa, 30.2% and 33.9% higher than PA 12, respectively. Further morphological analysis proved the interfacial interactions are enhanced by showing the difference in the phase gaps. The dynamic mechanical analysis (DMA) supported the conclusion that Pine-Lig-OH could interact with polymer chains, alternating segmental movements due to the strong interaction. Here, this study presents a method to enhance lignin composite properties by promoting interactions with the polymer matrix through modified functional groups, guiding future lignin composite research.

36 MATERIALS SCIENCE↗

DOE OSTI2024

3D printed lignin/polymer composite with enhanced mechanical and anti-thermal-aging performance

Lignin is the most abundant natural aromatic polymer globally but is still underutilized as a renewable material, even with its versatile properties. One approach to using lignin is to incorporate it in polymer composites, but this application is often limited by the poor mechanical performance of the resultant composite due to the poor interfacial adhesion. Following the structure–property relationship, stronger interactions were designed to be enhanced by alternating the functional groups of lignin. Here, this study applied a demethylation method to hardwood lignin (Ori-Lig) to introduce more phenolic hydroxyl groups. Research studies with rheology behavior and molecular simulations demonstrated that an increased phenolic hydroxyl content could improve the adhesion between the modified lignin (OH-Lig) and the polymer matrix at the interface. The tensile performance of the samples from the fused depositional modeling (FDM) 3D printing technique was also improved due to the improved interfacial adhesion. Specifically, by adding 10 wt% of the modified lignin, the tensile strength of the 3D printed samples could reach 46.1 MPa (40.2 MPa of Polyamide 12, PA12), and Young’s Modulus could be improved to 1.73 GPa (1.48 GPa of PA12). OH-Lig also improved anti-aging performance so that the tensile strength of the OH-Lig composite after thermo-aging (100 h at 140 °C) remained ~48MPa. The enhanced mechanical performance with anti-aging properties indicated that the OH-Lig composite may replace PA12 to reduce the use of petrol-based materials. This work showed the method of purposefully designing and modifying lignin structures to fulfill the interaction requirements between lignin and polymer matrix. The as-prepared lignin could be used to prepare functional composites to achieve improved mechanical performance and targeted functions at the same time.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗

DOE OSTI2023

Physics‐Informed Machine Learning for Inverse Design of Optical Metamaterials

Optical metamaterials manipulate light through various confinement and scattering processes, offering unique advantages like high performance, small form factor and easy integration with semiconductor devices. However, designing metasurfaces with suitable optical responses for complex metamaterial systems remains challenging due to the exponentially growing computation cost and the ill‐posed nature of inverse problems. To expedite the computation for the inverse design of metasurfaces, a physics‐informed deep learning (DL) framework is used. A tandem DL architecture with physics‐based learning is used to select designs that are scientifically consistent, have low error in design prediction, and accurate reconstruction of optical responses. The authors focus on the inverse design of a representative plasmonic device and consider the prediction of design for the optical response of a single wavelength incident or a spectrum of wavelength in the visible light range. The physics‐based constraint is derived from solving the electromagnetic wave equations for a simplified homogenized model. The model converges with an accuracy up to 97% for inverse design prediction with the optical response for the visible light spectrum as input, and up to 96% for optical response of single wavelength of light as input, with optical response reconstruction accuracy of 99%.

Sarkar, Sulagna↗