DOE OSTI2020

Characterizing photovoltaic backsheet adhesion degradation using the wedge and single cantilever beam tests, Part I: Field Modules

Photovoltaic backsheets are exposed to harsh outdoor weathering conditions throughout their service lives that can compromise their protective function, through adhesive debonding between their constituent layers and between the backsheet and the module. We report a large-scale study on adhesive degradation was conducted on 37 field-exposed modules, that spanned 19 different module manufacturers, that were deployed among six Köppen–Geiger climatic zones, and that were fielded between 0 and 28 years. Six outer layer polymer classes were identified among the backsheets: polyamide (PA), polyethylene terephthalate (PET), polyvinyl fluoride (PVF), polyvinylidene fluoride (PVDF), fluoroethylene vinyl ether copolymer (FEVE), and tetrafluoroethylene hexafluoropropylene vinylidene fluoride copolymer (THV). Two adhesion tests were used to measure the adhesive strength: the wedge test and the width-tapered single-cantilever beam (SCB) test. Adhesion energies were compared across exposure time and Köppen–Geiger climatic zone. Many of the PET-, PVF-, and PVDF-based backsheets experienced degradation of the adhesive layer between the backsheet outer and core layers. A consistent trend of decreasing adhesion energy with exposure time was observed in five out of the six backsheet types. Trends among adhesion energy and climatic zone, while expected, were not observed, possibly due to broad ranges in temperature, humidity, and precipitation defining Köppen–Geiger climatic zones. The cantilever beam measurements produced an upper cutoff of approximately 100 J/m 2 , above which no modules exhibited field delamination. The results are part of a two-part study quantifying adhesion in both field-weathered and indoor-exposed PV backsheets.

14 SOLAR ENERGY↗

DOE OSTI2020

Characterizing photovoltaic backsheet adhesion degradation using the wedge and single cantilever beam tests, Part II: Accelerated tests

Photovoltaic (PV) backsheets provide critical moisture, mechanical, and electrical insulation to the backside of PV modules, but their continued functionality depends upon their ability to remain well adhered over years of harsh environmental exposure. A study of adhesive strength was conducted on several PV backsheet types exposed to indoor accelerated weathering. Two adhesion tests – the wedge test and single cantilever beam test – were used to measure adhesion energy in four backsheets: two with fluoropolymer-based outer (airside) layers – polyvinyl fluoride (PVF), polyvinylidene fluoride (PVDF) – and two with non-fluoropolymer-based outer layers–polyamide (PA) and polyethylene terephthalate (PET). The effects of changes in temperature, ultraviolet (UV) irradiance, relative humidity, and a periodic water spray were studied. The PET-, PVF- and PVDF-based backsheets all showed instances of debonding in an adhesive layer, which is commonly reported. Furthermore, for the PA-, PET-, and PVDF-based backsheets, adhesion energy dropped fairly rapidly with exposure, reaching very low levels by 4000 h. The PVF-based backsheet was relatively robust to weathering. Pull-off of an outer chalking layer in the PA- and PET-based backsheets suggested a sensitivity to UV. Adhesion in these two backsheets was also highly sensitive to changes in moisture level. Changes in UV irradiance and temperature did not show a statistically significant effect on adhesion loss for the exposure levels used. The present work is part of a two-part adhesion study on both field-weathered and indoor-exposed backsheets, and forms a basis for understanding adhesion degradation across a variety of backsheet types and degradation factors.

14 SOLAR ENERGY↗

DOE OSTI2020

Impact of environmental variables on the degradation of photovoltaic components and perspectives for the reliability assessment methodology

Backsheet cracking has been a major issue observed in the field; however, standardized qualification tests, such as IEC61215, are inadequate to reliably identify such failures of PV modules due to the lack of the critical weathering factors applied sequentially or in combination, such as those found in the service environments. To address this problem, in this work we investigated the effects of various environmental variables on the degradation and failure behaviors of the polyamide-based backsheet in PV modules retrieved from five different locations, encompassing a variety of climates, including humid subtropical, hot-summer Mediterranean, tropical savanna climate and hot arid. The correlations between the degradation indicators and the weathering variables were further demonstrated by principle components analysis (PCA). We found strong relationships between: carbonyl formation and reflected solar radiation; hydroxyl formation and module temperature; yellowness and NO2 concentration, while no simple correlation could be found between a specific weathering factor and cracking. By introducing additional stress factors to the aged polyamide-based backsheet films with the novel 'fragmentation test', we successfully reproduced the field cracking behaviour. This study has demonstrated that different degradation modes of PV components respond differently to the environmental stresses encountered in service. Thereby, any accelerated laboratory test based on a single set condition or lacking key environmental variables would be inadequate to assess the long-term performance of PV modules and components. A new reliability-based methodology is proposed to quantitatively link laboratory testing with field results for the service life prediction of PV materials.

14 SOLAR ENERGY↗