Benchmark CO 2 separation achieved by highly fluorinated nanoporous molecular sieve membranes from nonporous precursor via in situ cross-linking
Molecular sieve membranes with rigid micropores and CO 2 -philic functionalities within the architectures are promising candidates in CO 2 separation. However, the development of ctieve approaches for their fabrication still remains a significant challenge. In this study, an in situ cross-linking strategy is developed for the preparation of nanoporous fluorinated moleffecular sieve membranes using commercially available dense and non-porous polystyrene (M PS ) as a precursor template. Based on the dehydrative Friedel-Crafts reactions with highly fluorinated benzylic alcohols, M PS membranes are cross-linked in situ upon exposure to Brønsted acid (CF 3 SO 3 H), affording fluorinated microporous polymeric membranes with surface areas up to 523 m 2 g –1 and the presence of micropores centered at 1.1–1.3 nm as well as ultra-micropores (~0.6 nm). The obtained modified membranes exhibit good ideal CO 2 permeability of 797 barrer and CO 2 /N 2 selectivity of 28.5. In addition, high fluorine content (up to 28.5 wt%) and good thermal stability made the cross-linked membranes promising candidates to produce fluorinated carbon molecular sieve membranes with improved textural properties, exhibiting surface areas up to 1020 m 2 g –1 and ultra-micropores of ~0.4 nm. These membranes achieve superior CO 2 /N 2 separation performances exceeding the Robeson upper bound limit (2008).