Thermochemical/Thermomechanical Synergies in High Temperature Solid Particle Erosion of CMAS Exposed EBCs

Environmental barrier coatings (EBCs) are an enabling technology for the use of SiC-based ceramic matrix composites in next generation gas turbine engines. In the extreme engine environment, EBCs must be able to withstand a variety of individual damage mechanisms and their interactions with each other. Ingested particulates/debris can cause both thermochemical and thermomechanical degradation of EBCs. Siliceous debris primarily based on calcium magnesium aluminosilicates (CMAS) can melt and infiltrate and/or react with EBCs above >1200°C. Similarly, ingested debris can lead to mechanical damage and recession of coatings due to particulate erosion. Both modes of degradation can occur simultaneously during engine operation, and it is crucial to comprehensively understand the mechanisms of coating failure due to high-temperature particulate interactions. This study assesses the erosion durability of Yb 2 Si 2 O 7 -based EBCs exposed to CMAS of various loads in NASA Glenn’s Erosion Burner Rig Facility. CMAS exposures and erosion testing were carried out at 1316°C. The effects of CMAS loading and exposure time on EBC erosion durability were evaluated using Al2O3 as an erodent material.

EBC↗

NASA NTRSDate not supplied

Development of Luminescence Lifetime-Based Surface Temperature Mapping for Environmental Barrier Coatings

Luminescence lifetime-based temperature mapping for thermal barrier coatings (TBCs) has been previously demonstrated up to temperatures approaching 1200 °C. Advantages of this method include insensitivities to reflected radiation and emissivity uncertainties. Because of a push towards greater efficiency turbine engine operation using higher turbine inlet temperatures, there is an ongoing movement from TBC-coated superalloy turbine engine components to SiC/SiC ceramic matrix composite components protected by environmental barrier coatings (EBCs). The useful application of luminescence lifetime-based temperature mapping to EBCs requires a significant increase in high temperature capability from below 1200 °C up into the 1300 to 1500 °C temperature range where the much higher background thermal radiation is a challenging issue. In addition, the luminescing sensing layer must exhibit thermochemical compatibility with the EBC. To meet these requirements, Er-doped Y 2 SiO 5 was selected as the luminescing sensor layer material both for its enhanced temperature sensitivity above 1300 °C and its compatibility with rare-earth disilicate EBC topcoats. Both localized spot temperature measurements as well as luminescence lifetime imaging-based temperature mapping were demonstrated up to 1560 °C for Er-doped Y 2 SiO 5 disks. In addition, temperature mapping capability was demonstrated from a 15 µm thick Er-doped Y 2 SiO 5 layer at the surface of a Sc 2 Si 2 O 7 based EBC topcoat. Both localized spot and temperature mapping by luminescence lifetime imaging were demonstrated up to 1380 °C (upper temperature limit of this slurry-based layered EBC) with excellent suppression of background thermal radiation and no degradation of the Er-doped Y 2 SiO 5 temperature sensing surface layer. The source of the novel enhanced temperature sensitivity above 1300 °C will be discussed as well as a path towards compatibility between sensing layer and EBC topcoat to higher temperatures.

temperature measurement↗

NASA NTRSDate not supplied

Thermochemical and microstructural contributions of high temperature particle erosion durability in CMAS exposed EBCs

Particulate/debris damage caused by ingestion of calcium magnesium aluminosilicates (CMAS) hinders the use of environmental barrier coatings (EBCs) to protect SiC-based ceramic matrix composite components in next generation gas turbine engines. Similarly, ingestion of any debris in the engine can lead to mechanical damage and recession of coatings due to particulate erosion. Investigating particulate interactions at relevant engine conditions is crucial in determining limiting mechanisms in the operating lifetime of EBCs. This study assesses the effects of extrinsic phase formation and microstructural changes due to CMAS interactions on the erosion durability of Yb 2 Si 2 O 7 -based EBCs in NASA Glenn’s Erosion Burner Rig Facility. CMAS exposures and erosion testing were carried out at 1316°C. Using 60 µm Al 2 O 3 particles as the erodent material, the effects of CMAS loading on erosion durability at various impingement angles were evaluated.

Jamesa L. Stokes↗