DOE OSTI2022

Thermal Stability and Mechanical Properties of Cold-Sprayed Nickel-Yttria Coating

The microstructural evolution under the extreme environments imposed during cold spray deposition of cermet coatings and the microstructural recovery during post-processing annealing treatments is rather complex and not well understood. Here, Ni-Yttria cermet coatings on an SS304 substrate were produced using cold spray technique, resulting in a bimodal grain structure. The grain growth, phase stability, hardness, and wear properties are observed in as-deposited and annealed (at 400 °C) Ni-Yttria and pure Ni coatings. A multimodal microstructural characterization using electron microscopy, and atom probe tomography shows the structural and compositional stability of yttria particles and Ni grains. A fragmentation of Y-rich particles and dispersion in Ni was observed, however, no forced mixing/dissolution of Y in Ni is detected. Nano-yttria dispersed within the Ni grains slowed the grain growth during annealing. After annealing, Yttria reinforced coating was 1.5 times harder and showed better thermal and mechanical stability compared to the Ni coating.

Gwalani, Bharat↗
DOE OSTI2021

Optimization-based Design for Manufacturing

This report provides detailed documentation of the algorithms that where developed and implemented in the Plato software over the course of the Optimization-based Design for Manufacturing LDRD project.

42 ENGINEERING↗
DOE OSTI2021

Measuring the residual stress and stress-corrosion cracking susceptibility of additively manufactured 316L by ASTM G36-94

Residual stress is a contributor to stress-corrosion cracking (SCC) and a common byproduct of additive manufacturing (AM). In this work, the relationship between residual stress and SCC susceptibility in laser powder bed fusion AM 316L stainless steel was studied through immersion in saturated boiling magnesium chloride per ASTM G36-94. The residual stress was varied by changing the sample height for the as-built condition and additionally by heat treatments at 600, 800, and 1200 °C to control, and in some cases reduce, residual stress. In general, all samples in the as-built condition showed susceptibility to SCC with the thinner, lower residual stress samples showing shallower cracks and crack propagation occurring perpendicular to melt tracks due to local residual stress fields. The heat-treated samples showed a reduction in residual stress for the 800 and 1200 °C samples. Both were free of cracks after >300 hours of immersion in MgCl 2 , while the 600 °C sample showed similar cracking to their as-built counterpart. Geometrically necessary dislocation (GND) density analysis indicates that the dislocation density may play a major role in the SCC susceptibility.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Nonlinear ultrasonic technique for the characterization of microstructure in additive materials

This study employs nonlinear ultrasonic techniques to track microstructural changes in additively manufactured metals. The second harmonic generation technique based on the transmission of Rayleigh surface waves is used to measure the acoustic nonlinearity parameter, β. Stainless steel specimens are made through three procedures: traditional wrought manufacturing, laser-powder bed fusion, and laser engineered net shaping. The β parameter is measured through successive steps of an annealing heat treatment intended to decrease dislocation density. Dislocation density is known to be sensitive to manufacturing variables. In agreement with fundamental material models for the dislocation-acoustic nonlinearity relationship in the second harmonic generation, β drops in each specimen throughout the heat treatment before recrystallization. Geometrically necessary dislocations (GNDs) are measured from electron back-scatter diffraction as a quantitative indicator of dislocations; average GND density and β are found to have a statistical correlation coefficient of 0.852 showing the sensitivity of β to dislocations in additively manufactured metals. Moreover, β shows an excellent correlation with hardness, which is a measure of the macroscopic effect of dislocations.