NASA NTRS1992

Fatigue damage in cross-ply titanium metal matrix composites containing center holes

The development of fatigue damage in (0/90) sub SCS-6/TI-15-3 laminates containing center holes was studied. Stress levels required for crack initiation in the matrix were predicted using an effective strain parameter and compared to experimental results. Damage progression was monitored at various stages of fatigue loading. In general, a saturated state of damage consisting of matrix cracks and fiber matrix debonding was obtained which reduced the composite modulus. Matrix cracks were bridged by the 0 deg fibers. The fatigue limit (stress causing catastrophic fracture of the laminates) was also determined. The static and post fatigue residual strengths were accurately predicted using a three dimensional elastic-plastic finite element analysis. The matrix damage that occurred during fatigue loading significantly reduced the notched strength.

Bakuckas, J. G., Jr.↗

NASA NTRS1992

Characterization of unnotched SCS-6/Ti-15-3 metal matrix composites at 650 C

Ti-15-3 reinforced with SCS-6 silicon carbide fibers, in five different layups, was tested at 650 C to determine monotonic and fatigue strengths, basic mechanical properties, and damage initiation and progression. The elevated temperature results were compared to those obtained at room temperature. Analytical predictions were made of the monotonic stress-strain response as well as cyclic stress-strain hysteresis. The fiber reinforcement was found to significantly increase the static and fatigue strengths of the laminates over that of the matrix material at elevated temperature while the increase was insignificant at room temperature. Initial damage, in either the fibers or the matrix, was partitioned as a function of the life and applied strain range in the constituents. High strains and short lives resulted in multiple fiber failure with no signs of matrix fatigue cracking. Low strains and long lives resulted in extensive matrix cracking and no fiber breaks away from the fracture surface. At 650 C the matrix was too weak to cause fiber-matrix interface failure prior to matrix yielding. Laminate fatigue lives were hypothesized to be a function of the 0 deg fiber stress. More scatter was found in the 0 deg fiber stress vs. high temperature fatigue life data than for the room temperature data. An initial unloading modulus that was greater than the initial loading modulus was observed in the elevated temperature fatigue tests.

Pollock, William D.↗

NASA NTRS1992

Prediction of matrix fatigue crack initiation in notched SCS-6/Ti-15-3 metal matrix composites

Several lay-ups of SCS-6/Ti-15-3 metal matrix composites were tested in either a center hole or a double edge notched geometry. At different cyclic stress levels, the number of cycles required to develop matrix fatigue cracks at the notches was recorded. A fatigue strat-life curve was developed for the Ti-15-3 matrix material. This modified parameter predicted the number of cycles required for matrix crack initiation at the notches. The predictions were in good agreement with the experimental data.

Hillberry, Benjamin M.↗

NASA NTRS1991

Prediction of matrix fatigue crack initiation in notched SCS-6/Ti-15-3 metal matrix composites

Several lay-ups of SCS-6/Ti-15-3 metal matrix composites were tested in either a center hole or a double edge notched geometry. At different cyclic strss levels, the number of cycles required to develop matrix fatigue cracks at the notches was recorded. A fatigue strat-life curve was developed for the Ti-15-3 matrix material. This modified parameter predicted the number of cycles required for matrix crack initiation at the notches. The predictions were in good agreement with the experimental data.

Hillberry, B. M.↗

NASA NTRS1991

Effect of fiber-matrix debonding on notched strength of titanium metal matrix composites

Two specimen configuration of a (0/90)2s SCS-6/Ti-15-3 laminate were tested and analyzed: a center hole (CH) specimen and a double edge notch (DEN) specimen. The two specimen configurations failed at similar stress levels. Two analytical techniques, a 3-D finite-element analysis and a macro-micromechanical analysis were used to predict the overall stress-deformation behavior and the notch-tip fiber-matrix interface stresses in both configurations.

Bigelow, C. A.↗

NASA NTRS1991

Analysis of thermomechanical fatigue of unidirectional titanium metal matrix composites

Thermomechanical fatigue (TMF) data was generated for a Ti-15V-3Cr-3Al-3Sn (Ti-15-3) material reinforced with SCS-6 silicon carbide fibers for both in-phase and out-of-phase thermomechanical cycling. Significant differences in failure mechanisms and fatigue life were noted for in-phase and out-of-phase testing. The purpose of the research is to apply a micromechanical model to the analysis of the data. The analysis predicts the stresses in the fiber and the matrix during the thermal and mechanical cycling by calculating both the thermal and mechanical stresses and their rate-dependent behavior. The rate-dependent behavior of the matrix was characterized and was used to calculate the constituent stresses in the composite. The predicted 0 degree fiber stress range was used to explain the composite failure. It was found that for a given condition, temperature, loading frequency, and time at temperature, the 0 degree fiber stress range may control the fatigue life of the unidirectional composite.

Mirdamadi, M.↗

NASA NTRS1991

Comparison of some micromechanics models for discontinuously reinforced metal matrix composites

A systematic experimental evaluation of whisker and particulate reinforced aluminum matrix composites was conducted to assess the variation in tensile properties with reinforcement type, volume fraction, and specimen thickness. Each material was evaluated in three thicknesses, 1.8, 3.18, and 6.35 mm, to determine the size, distribution, and orientation of the reinforcements. This information was used to evaluate several micromechanical models that predict composite moduli. The longitudinal and transverse moduli were predicted for reinforced aluminum. The Paul model, the Cox model and the Halpin-Tsai model were evaluated. The Paul model gave a good upper bound prediction for the particulate reinforced composites but under predicted whisker reinforced composite moduli. The Cox model gave good moduli predictions for the whisker reinforcement, but was too low for the particulate. The Halpin-Tsai model gave good results for both whisker and particulate reinforced composites. An approach using a trigonometric projection of whisker length to predict the fiber contribution to the modulus in the longitudinal and transverse directions was compared to the more conventional lamination theory approach.

Johnson, W. S.↗

NASA NTRS1991

Observations of fatigue crack initiation and damage growth in notched titanium matrix composites

The purpose was to characterize damage initiation and growth in notched titanium matrix composites at room temperature. Double edge notched or center open hole SCS-6/Ti-15-3 specimens containing 0 deg plies or containing both 0 and 90 deg plies were fatigued. The specimens were tested in the as-fabricated (ASF) and in heat-treated conditions. A local strain criterion using unnotched specimen fatigue data was successful in predicting fatigue damage initiation. The initiation stress level was accurately predicted for both a double edge notched unidirectional specimen and a cross-plied center hole specimen. The fatigue produced long multiple cracks growing from the notches. These fatigue cracks were only in the matrix material and did not break the fibers in their path. The combination of matrix cracking and fiber/matrix debonding appears to greatly reduce the stress concentration around the notches. The laminates that were heat treated showed a different crack growth pattern. In the ASF specimens, matrix cracks had a more tortuous path and showed considerable more crack branching. For the same specimen geometry and cyclic stress, the (0/90/0) laminate with a hole had far superior fatigue resistance than the matrix only specimen with a hole.

Naik, Rajiv A.↗

NASA NTRS1991

Fatigue of continuous fiber reinforced titanium matrix composites

Several lay-ups of SCS-6/Ti-15-3 composites were investigated. Static and fatigue tests were conducted for both notched and unnotched specimens at room and elevated temperatures. Test results indicated that the stress in the 0 fibers is the controlling factor in fatigue life. The static and fatigue strength of these materials is shown to be dependent on the level of residual stresses and the fiber/ matrix interfacial strength. Fatigue tests of notched specimens showed that cracks can initiate and grow many fiber spacings in the matrix material without breaking fibers. These matrix cracks can significantly reduce the residual strength of notched composite.

Johnson, W. S.↗

NASA NTRS1990

Matrix fatigue crack development in a notched continuous fiber SCS-6/Ti-15-3 composite

In this study the extensive matrix fatigue cracking that has been observed in notched SCS-6/Ti-15-3 composites is investigated. Away from the notch a uniform spacing of the fatigue cracks develops. Closer to the notch, fiber-matrix debonding which occurs increases the crack spacing. Crack spacing and debond length determined from shear-lag cylinder models compare favorably with experimental observations. Scanning electron microscope (SEM) fractography showed that the principal fatigue crack initiation occurred around the zero degree fibers. Interface failure in the 90 degree plies does not lead to the development of the primary fatigue cracking.

Hillberry, B. M.↗

NASA NTRS1990

Micromechanical thermal analysis of interphase region in a titanium aluminide MMC

The high reactivity between the fiber and matrix in silicon carbide/titanium aluminide MMCs leads to the formation of brittle reaction products at the fiber/matrix (F/M) interface. Also, the high thermal expansion coefficient mismatch between the fiber and matrix leads to high tensile residual stresses at the F/M interface, and this can lead to premature cracking during cooldown. One solution to these problems is the use of a metallic fiber coating like Ta which acts as an F/M diffusion barrier and reacts with the matrix to form a beta stabilized compliant layer. A finite element micromechanics analysis was performed to study the effects of Ta and beta interphase layers on the thermal residual stresses during consolidation. A 5-micron-thick beta layer reduced cool-down stresses by 8 percent compared to a 2 percent reduction computed for a Ta layer of the same thickness. Plastic yielding in the Ta was not effective in reducing cool-down stresses. Compliant alpha-2 particles next to the stiffer gamma particles reduced stresses in the gamma particles by less than 2 percent. A simple closed form analysis was developed to calculate thermal residual stresses in a fiber/interphase/matrix system. A 2-micron-thick Ag interphase layer was found to reduce residual stresses by about 11 percent.

Naik, R. A.↗

NASA NTRS1990

Observations of fatigue crack initiation and damage growth in notched titanium matrix composites

Naik, R. A.↗

NASA NTRS1990

Fatigue damage growth mechanisms in continuous fiber reinforced titanium matrix composites

The role of fiber/matrix interface strength, residual thermal stresses, and fiber and matrix properties on fatigue damage accumulation in continuous fiber metal matrix composites (MMC) is discussed. Results from titanium matrix silicon carbide fiber composites is the primary topic of discussion. Results were obtained from both notched and unnotched specimens at room and elevated temperatures. The stress in the 0 deg fibers was identified as the controlling factor in fatigue life. Fatigue of the notched specimens indicated that cracks can grow in the matrix materials without breaking fibers.

Johnson, W. S.↗

NASA NTRS1990

Thermal and mechanical behavior of metal matrix and ceramic matrix composites

The present conference discusses local stresses in metal-matrix composites (MMCs) subjected to thermal and mechanical loads, the computational simulation of high-temperature MMCs' cyclic behavior, an analysis of a ceramic-matrix composite (CMC) flexure specimen, and a plasticity analysis of fibrous composite laminates under thermomechanical loads. Also discussed are a comparison of methods for determining the fiber-matrix interface frictional stresses of CMCs, the monotonic and cyclic behavior of an SiC/calcium aluminosilicate CMC, the mechanical and thermal properties of an SiC particle-reinforced Al alloy MMC, the temperature-dependent tensile and shear response of a graphite-reinforced 6061 Al-alloy MMC, the fiber/matrix interface bonding strength of MMCs, and fatigue crack growth in an Al2O3 short fiber-reinforced Al-2Mg matrix MMC.

Kennedy, John M.↗

NASA NTRS1990

Mechanical characterization of unnotched SCS6/Ti-15-3 metal matrix composites at room temperature

The Ti-15-3 metal matrix composites containing silicon-carbide (SCS6) fibers, in five different lay-ups, have been tested at room temperature to determine static strengths and mechanical properties. Experimental data and predicted values of the laminate properties and strengths showed good correlation. The off-axis laminate plies (that is, 90 and 45 deg) suffered fiber/matrix interface failures at stress levels as low as 20 ksi, thus significantly affecting the mechanical properties of the laminate. Edge replicas were used to verify the fiber/matrix separations. Microscopic examinations determined that the fiber/matrix failures were occurring in the titanium/silicon reaction layer. Fatigue tests were performed on unnotched specimens to determine the number of cycles to failure versus cyclic stress level. It was found that the stress in the 0 deg fiber could be used to correlate the fatigue life of different laminates containing 0 deg plies.

Johnson, W. S.↗

NASA NTRS1990

Characterization of the tensile and microstructural properties of an aluminum metal matrix composite

This study examines a powder metallurgy aluminum alloy in the unreinforced state and with a discontinuous reinforcement of 15 v/o or 30 v/o SiC whisker or 15 v/o SiC particulate. The materials were extruded and then hot-rolled to three plate thicknesses of 6.35, 3.18 and 1.8 mm and were investigated in the as-fabricated and peak aged conditions. The influence of mechanical working on the reinforcement morphology and distribution were examined. A comparison of the mechanical properties was made and the elastic moduli of the reinforced materials were predicted using a micromechanics model. Fractography of tensile specimens revealed that the fracture process was dominated by the presence of microstructural inhomogeneities which were related to both the matrix alloy and to the reinforcement type. An analysis of these microstructural features and a description of the micromechanics model are presented in the paper.

Birt, M. J.↗

NASA NTRS1990

Fatigue damage growth mechanisms in continuous fiber reinforced titanium matrix composites

The role of fiber/matrix interface strength, residual thermal stresses, and fiber and matrix properties on fatigue damage accumulation in continuous fiber metal matrix composites (MMC) will be discussed. Results from titanium matrix/silicon-carbide fiber composites will be the primary topic of discussion. Results have been obtained from both notched and unnotched specimens at room and elevated temperatures. The stress in the 0 deg fibers has been indentified as the controlling factor in fatigue life. Fatigue of the notched specimens indicated that cracks can grow many fiber spacings in the matrix materials without breaking fibers.

Johnson, W. S.↗

NASA NTRS1990

Matrix fatigue crack development in a notched continuous fiber SCS-6/Ti-15-3 composite

In this study the extensive matrix fatigue cracking that has been observed in notched SCS-6/Ti-15-3 composites is investigated. Away from the notch uniform spacing of the fatigue cracks develops. Closer to the notch, fiber-matrix debonding which occurs increases the crack spacing. Crack spacing and debond length determined from shear-lag cylinder models compare favorably with experimental observations. Scanning electron microscope (SEM) fractography showed that the principal fatigue crack initiation occurred around the zero degree fibers. Interface failure in the 90 degree plies does not lead to the development of the primary fatigue cracking.

Hillberry, B. M.↗