NASA NTRS2013

Micro-Scale Mechanical Testing of Non-Woven Carbon Nanotube Sheets and Yarns

Non-woven carbon nanotube (CNT) sheets and yarns were tested using a novel micro-scale mechanical testing system. CNT sheets were observed to delaminate during uniaxial testing using an adbesive gripping method, resulting from a higher proportion of load bearing in the outer sheets versus internal sheets and an apparently low interlaminar shear strength. In response to this, a new spool-grip method was used to alleviate non-uniform through-thickness stresses, circumvent premature delamination, and allow the sheet material to sustain a 72% increase in measured tensile strength. Furthermore, tension tests of CNT yarns showed that the yarn-structure was approximaiely 7 times stronger than the sheet structure, owing to a higher degree of CNT alignment in the test direction.

Magargee, J.↗

NASA NTRS2012

Small-Scale Mechanical Characterization of Space-Exposed Fluorinated Ethylene Propylene Recovered from the Hubble Space Telescope

Multi-layer insulation panels from the Hubble Space Telescope have been recovered after 19.1 years of on-orbit service and micro-tensile experiments have been performed to characterize the effect of space exposure on the mechanical response of the outermost layer. This outer layer, 127 m thick fluorinated ethylene propylene with a 100 nm thick vapor deposited aluminum reflective coating, maintained significant tensile ductility but exhibited a degradation of strength that scales with severity of space exposure. This change in properties is attributed to damage from incident solar flux, atomic oxygen damage, and thermal cycling.

Jones, J. S.↗

NASA NTRS1984

Repair techniques for celion/LARC-160 graphite/polyimide composite structures

The large stiffness-to-weight and strength-to-weight ratios of graphite composite in combination with the 600 F structural capability of the polyimide matrix can reduce the total structure/TPS weight of reusable space vehicles by 20-30 percent. It is inevitable that with planned usage of GR/PI structural components, damage will occur either in the form of intrinsic flaw growth or mechanical damage. Research and development programs were initiated to develop repair processes and techniques specific to Celion/LARC-160 GR/PI structure with emphasis on highly loaded and lightly loaded compression critical structures for factory type repair. Repair processes include cocure and secondary bonding techniques applied under vacuum plus positive autoclave pressure. Viable repair designs and processes are discussed for flat laminates, honeycomb sandwich panels, and hat-stiffened skin-stringer panels. The repair methodology was verified through structural element compression tests at room temperature and 315 C (600 F).

Jones, J. S.↗

NASA NTRS1982

Celion/Larc-160 graphite/polyimide composite processing techniques and properties

Weight savings in the range from 25 to 35 percent could be achieved on Space Shuttle orbiter components and the thermal protection system (TPS) by employing a suitable graphite/polyimide (Gr/Pi) composite material system as a substitute for the baseline aluminum structural material. Predicted weight savings are based on the superior strength and stiffness-to-density ratios of Gr/Pi composite material over metallic counterparts. Specific strength and stiffness properties of Celion/Larc-160 composite laminates are compared with aluminum and titanium alloys. Aspects of materials and processes development are discussed, taking into account Celion/Larc-160 composite cure cycle and tooling evolution, complex shaped component process development, mechanical and physical properties testing and results, and structural element design fabrication, testing, and results. Attention is given to a demonstration of materials and processing technology, and a Celion/Larc-160 materials and processes summary is presented.

Jones, J. S.↗

NASA NTRS1981

Development and demonstration of manufacturing processes for fabricating graphite/LARC 160 polyimide structural elements

The development and demonstration of manufacturing technologies for the structural application of Celion graphite/LARC-160 polyimide composite material is discussed. Process development and fabrication of demonstration components are discussed. Process development included establishing quality assurance of the basic composite material and processing, nondestructive inspection of fabricated components, developing processes for specific structural forms, and qualification of processes through mechanical testing. Demonstration components were fabricated. The demonstration components consisted of flat laminates, skin/stringer panels, honeycomb panels, chopped fiber compression moldings, and a technology demonstrator segment (TDS) representative of the space shuttle aft body flap.

Frost, R. K.↗

NASA NTRS1978

Testing composite sheets at high temperatures

Candidate materials for skins of flexural sandwich beams can be compressive- or tensile-tested at high temperature by using corrosion resistant steel (CRES) for core material. Tests with CRES core have been made at temperatures as high as 260 C. Future tests at temperatures above 371 C may be permissible.

Jones, J. S.↗

NASA NTRS1969

Liquid oxygen-compatible insulation system

To provide insulation for tees, elbows, sumps, and valves that are used to pass or store fluids at cryogenic temperatures, individual parts are insulated in an environmentally controlled facility. It is desirable that such insulation be liquid oxygen compatible and be easily removable and reinstallable.

Jones, J. S.↗