Quenched-in defects in flashlamp-annealed silicon
Deep levels introduced in boron-doped silicon by heat-pulse annealing with a tungsten-halogen flashlamp are investigated using deep-level transient spectroscopy. Two majority-carrier trapping levels in the band gap, at Ev + 0.32 eV and at Ev + 0.45 eV, are observed. These results are compared to those obtained by furnace-quenching and laser-annealing studies. Both the position in the gap and the annealing kinetics of the hole trap at Ev + 0.45 eV suggest that this center is due to an interstitial iron impurity in the lattice. The deep levels are not consistently observed in all flashlamp-annealed Si crystals utilized.
Borenstein, J. T.↗