Thermal barrier coatings with CMAS resistance
A coating on a substrate is disclosed having layers including yttrium aluminum garnet (YAG) and yttrium aluminum monoclinic (YAM).
Engineering topics
Publications and source records attributed to Jordan, Eric.
A coating on a substrate is disclosed having layers including yttrium aluminum garnet (YAG) and yttrium aluminum monoclinic (YAM).
Thermal barrier coatings and methods to make such coatings present improved resistance to CMAS infiltration. The method for forming a thermal barrier coating includes applying a layer of the thermal barrier coating to a component having a surface, forming a plurality of first channels in the thermal barrier coating, and forming a plurality of second channels in the thermal barrier coating. The first channels extend through a thickness of the thermal barrier coating from an interface with the surface of the component to a free surface opposite the interface. The second channels are disposed between the free surface and the interface and extending lengthwise generally parallel to the free surface of the thermal barrier coating, wherein the thermal barrier coating comprises a material comprising yttrium aluminum garnet (YAG) or yttria stabilized zirconia (YSZ).
A thermal barrier coating for an internal combustion engine includes an insulating thermal spray coating, where a chosen material of the insulating thermal spray coating has a thermal conductivity lower than 2 W/mK in fully dense form and the chosen material includes a coefficient of thermal expansion within 5 ppm/K of a coefficient of thermal expansion of a material of a component of the internal combustion engine upon which the coating is placed.
A thermal barrier coating for an internal combustion engine includes an insulating thermal spray coating, where a chosen material of the insulating thermal spray coating has a thermal conductivity lower than 2 W/mK in fully dense form and the chosen material includes a coefficient of thermal expansion within 5 ppm/K of a coefficient of thermal expansion of a material of a component of the internal combustion engine upon which the coating is placed.
A coating on a substrate is disclosed having layers including yttrium aluminum garnet (YAG) and yttrium aluminum perovskite (YAP).
The Solution Precursor Spray Process (SPPS) process has been shown to overcome the durability and property challenges of applying yttrium aluminum garnet (YAG) coating for high temperature thermal barrier coating (TBC) applications (1200°C+) but only limited testing has been performed in representative application environments. In this study, YAG coatings were developed to optimize microstructure and tailor properties for combustion components in an industrial gas turbine. Thermal conductivity, erosion resistance and furnace cycling durability were used to validate YAG properties against the standard yttria-stabilized zirconia coating (YSZ). Graded and multi-layered microstructures were applied to enhance performance while maintaining durability. Further YAG process development was required to replicate coating properties and optimize deposition on more complex fuel injector nozzle and combustion liner components. Rig testing of both components was performed and compared against the baseline YSZ coating validating the high temperature capability and lower thermal conductivity of the SPPS YAG coating. The components in both tests were cycled for a minimum of ten cycles with the fuel injector test targeting a higher operating temperature while the combustor liner operated at standard conditions. A development engine test is planned to further validate performance in a gas turbine engine of this promising material.
Thermal barrier coatings and methods to make such coatings present improved resistance to CMAS infiltration. The method for forming a thermal barrier coating includes applying a layer of the thermal barrier coating to a component having a surface, forming a plurality of first channels in the thermal barrier coating, and forming a plurality of second channels in the thermal barrier coating. The first channels extend through a thickness of the thermal barrier coating from an interface with the surface of the component to a free surface opposite the interface. The second channels are disposed between the free surface and the interface and extending lengthwise generally parallel to the free surface of the thermal barrier coating.
Prior experiments reported by the authors have proven the hypothesis that achieving a dynamic temperature swing on the combustion chamber surface will lead to improved thermal and combustion efficiencies of the homogeneous charge compression ignition engine. A thin layer of yttria-stabilized zirconia, roughly 150 μm, was plasma sprayed on the piston top. It led to markedly advanced ignition and heat release in the gasoline homogeneous charge compression ignition engine, accompanied with reduced unburnt hydrocarbon and carbon monoxide emissions, improved combustion efficiency, and a higher thermal efficiency. A related computational study highlighted the critical role of coating thermal conductivity in achieving a desired dynamic response; hence, the second phase of experimental investigations focused on introducing structured porosity in the yttria-stabilized zirconia coating, as a means of reducing effective conductivity. Indeed, additional incremental improvements were observed, as well as limitations related to adverse effects of the surface roughness and the fuel interactions with the surface roughness and open pores. Erosion can also be a problem in a direct injection engine. Therefore, the third round of investigations focused on a material with a natively low conductivity (low-k), sprayed on the top of an Al piston in a relatively dense form, and in a way that yields a smooth surface. The objective was to capitalize on the low conductivity, while avoiding the pitfalls accompanying high-porosity formulations. The heat-storage capacity was limited by keeping the thickness relatively low. The results verify the paramount importance of thermal conductivity in the context of high “temperature swing” behavior and indicate a potential to improve the homogeneous charge compression ignition engine’s combustion efficiency roughly 1.5%, with the overall indicated efficiency improvement on the order of 5%, on a relative basis. In addition, the low-k oxide thermal barrier applied to the piston extended significantly the low-load homogeneous charge compression ignition operability limit.
Explore the source record for details and available documents.
The goal is the development of constitutive equations to describe the elevated temperature stress-strain behavior of single crystal turbine blade alloys. The program includes both the development of a suitable model and verification of the model through elevated temperature-torsion testing. A constitutive model is derived from postulated constitutive behavior on individual crystallographic slip systems. The behavior of the entire single crystal is then arrived at by summing up the slip on all the operative crystallographic slip systems. This type of formulation has a number of important advantages, including the prediction orientation dependence and the ability to directly represent the constitutive behavior in terms which metallurgists use in describing the micromechanisms. Here, the model is briefly described, followed by the experimental set-up and some experimental findings to date.