DOE OSTI2023

A novel additive manufacturing compression overmolding process for hybrid metal polymer composite structures

Metal polymer composites combining low density, high strength composites with highly ductile and tough metals have gained traction over the last few decades as lightweight and high-performance materials for industrial applications. However, the mechanical properties are limited by the interfacial bonding strength between metals and polymers achieved through adhesives, welding, and surface treatment processes. In this paper, a novel manufacturing process combining additive manufacturing and compression molding to obtain hybrid metal polymer composites with enhanced mechanical properties is presented. Additive manufacturing enabled deposition of polymeric material with fibers in a predetermined pattern to form tailored charge or preform for compression molding. Here, a grade 300 maraging steel triangular lattice is first fabricated using AddUp FormUp350 laser powder bed system and compression overmolded with additively manufactured long carbon fiber-reinforced polyamide-6,6 (40% wt. CF/PA66) preform. The fabricated hybrid metal polymer composites showed high stiffness and tensile strength. The stiffness and failure characteristics determined from the uniaxial tensile tests were correlated to a finite element model within 20% deviation. Fractographic analyses was performed using microscopy to investigate failure mechanisms of the hybrid structures.

36 MATERIALS SCIENCE↗

DOE OSTI2022

Systems and methods for powder bed additive manufacturing anomaly detection

Detection and classification of anomalies for powder bed metal additive manufacturing. Anomalies, such as recoater blade impacts, binder deposition issues, spatter generation, and some porosities, are surface-visible at each layer of the building process. A multi-scaled parallel dynamic segmentation convolutional neural network architecture provides additive manufacturing machine and imaging system agnostic pixel-wise semantic segmentation of layer-wise powder bed image data. Learned knowledge is easily transferrable between different additive manufacturing machines. The anomaly detection can be conducted in real-time and provides accurate and generalizable results.

Scime, Luke R.↗

DOE OSTI2021

Mechanical Properties of Additively Manufactured 316L Stainless Steel Before and After Neutron Irradiation (FY21)

This report presents the materials property data of additively manufactured (AM) 316L stainless steel (SS) accumulated for the assessment of core materials in the Transformational Challenge Reactor (TCR) program. The TCR manufacturing approach includes using the laser powder bed fusion (LPBF) method for metallic (316L and Inconel 718) components. To assess the mechanical performance of printed components in reactor-relevant conditions and build a property database for the AM materials, mechanical tests and evaluations were performed before and after neutron irradiation. Miniature tensile specimens were irradiated in the High Flux Isotope Reactor to 0.2, 2, 8, and 10 dpa at target temperatures of 300 and 600°C. Postirradiation evaluation for the 0.2 and 2 dpa specimens was performed during FY20 and FY21, and the results are presented and discussed in this document.

22 GENERAL STUDIES OF NUCLEAR REACTORS↗

DOE OSTI2021

Mechanical behavior of additively manufactured and wrought 316L stainless steels before and after neutron irradiation

Fabrication of nuclear reactor components using additive manufacturing (AM) methods is now a practical option since the AM technologies have advanced to allow for building of complex parts with high quality materials. To assess the mechanical performance of printed components in reactor-relevant conditions and to build a property database for the AM 316L stainless steel (SS), mechanical testing and characterization were performed before and after neutron irradiation. In this work, miniature tensile specimens were irradiated at the High Flux Isotope Reactor (HFIR) to 0.2 and 2 displacements per atom (dpa) at 300 and 600°C. The AM 316L SS was tested in the as-built, stress-relieved, and solution-annealed conditions, and the wrought (WT) 316L SS in solution-annealed condition as a reference alloy. The baseline test result showed that the AM 316L SS, regardless of the post-build heat treatment, had higher strength than the WT 316L SS, but similar ductility. Post-irradiation tensile testing was conducted at RT, 300°C, and 500°C for selected irradiation conditions. Neutron irradiation induced significant changes in the mechanical behavior of the AM stainless steels, including both hardening and softening. Although the as-built 316L steel after 300°C irradiation showed necking just after yielding, the overall property changes of the as-printed alloy became less significant after 600°C irradiation. Irradiation-induced ductilization was also observed after the higher temperature irradiation. In general, the strength change was smaller in the relatively stronger as-built and stress-relieved AM SSs than in the solution-annealed AM and WT SSs. These relatively lower strength 316L SSs overall retained higher ductility in the irradiation conditions tested, but the stronger 316L SSs demonstrated a similar level of ductility after the higher temperature (600°C) irradiation. It is a positive assessment for the AM 316L materials that no embrittlement was observed within the test and irradiation conditions of the experiment.

36 MATERIALS SCIENCE↗

DOE OSTI2020

Mechanical Properties and Deformation Behavior of Additively Manufactured 316L Stainless Steel (FY2020)

The Transformational Challenge Reactor (TCR) program plans to build most of the TCR core components through additive manufacturing (AM) processes. These processes include laser powder bed fusion (LPBF) for the metallic (316L) components and the newly developed combined process of binderjet printing and chemical vapor infiltration (CVI) for the SiC fuel matrix. Mechanical testing and characterization tasks have been carried out since the beginning of the TCR program to (1) build a property database for the AM materials that will be used in TCR core and (2) to assess the materials’ performance in TCR-relevant conditions. This document reports the outcome of the testing and characterization efforts for the fiscal year with a focus on the mechanical performance data of AM 316L stainless steel (SS). Baseline tensile testing over a wide temperature range of room temperature–600 °C was completed for the AM 316L alloy in as-built, stress-relieved, and solution-annealed conditions. The as-built 316L showed the highest strength, and the alloy after the post-build treatments showed reduced strengths in the low-strain range. However, the strength differences among the AM materials became insignificant in the later part of deformation. Furthermore, regardless of post-build processing, the AM 316L SS showed higher strength and comparable ductility when compared with wrought 316L SS. Thermal creep testing and microstructural evolution during creep deformation were also performed under selected conditions. It was found that the AM 316L steel showed the best creep resistance in the stress-relieved condition. In-situ tensile tests were performed using scanning electron microscopy and 1-ID beamline at the Advanced Photon Source to elucidate the deformation and fracture behavior of AM 316L and the evolution of crystalline stress, dislocations, and pore distribution. Using these in-situ testing data, an in-depth analysis of the roles of microstructural features in deformation and fracture processes is presented herein. The final section of the document introduces ongoing and future activities for materials testing and characterization, including irradiation effect studies and ball punch testing on AM 316L and AM IN718 alloys.

21 SPECIFIC NUCLEAR REACTORS AND ASSOCIATED PLANTS↗