Layer-dependence study of two-dimensional ferromagnets: Fe3GeTe2 and Fe5Ge2Te2

We have investigated the electrical transport properties of nanodevices fabricated from exfoliated flakes of two-dimensional metallic ferromagnets Fe3GeTe2 (FGT) and Fe5Ge2Te2 (FG2T) down to below three layers in thickness. The per-layer anomalous Hall conductivity even in thick FGT and FG2T devices is found to be much smaller than ∼e2h, the approximate value calculated for thick undoped crystals. Moreover, we obtain a power-law scaling relation between the per-layer anomalous Hall and per-layer longitudinal conductivities with an exponent close to 1.6, which agrees with the universal value for poor ferromagnetic conductors. Both FGT and FG2T devices show clear layer-dependent Curie temperatures and layer-dependent perpendicular magnetic anisotropy, with FG2T dominating the former and FGT dominating the latter for all thicknesses. Despite their declining trend as the device thickness decreases, both Curie temperature and magnetic anisotropy retain a significant fraction of their bulk values (>60% and >80% of the bulk values, respectively, even in the thinnest FG2T device), indicating attractive potential for practical applications.

Physics↗

DOE OSTI2024

Tailored (La 0.2 Pr 0.2 Nd 0.2 Tb 0.2 Dy 0.2 ) 2 Ce 2 O 7 as a Highly Active and Stable Nanocatalyst for the Oxygen Evolution Reaction

Abstract Designing highly active and robust catalysts for the oxygen evolution reaction is key to improving the overall efficiency of the water splitting reaction. It has been previously demonstrated that evaporation induced self‐assembly (EISA) can be used to synthesize highly porous and high surface area cerate‐based fluorite nanocatalysts, and that substitution of Ce with 50% rare earth (RE) cations significantly improves electrocatalyst activity. Herein, the defect structure of the best performing nanocatalyst in the series are further explored, Nd 2 Ce 2 O 7 , with a combination of neutron diffraction and neutron pair distribution function analysis. It is found that Nd 3 + cation substitution for Ce in the CeO 2 fluorite lattice introduces higher levels of oxygen Frenkel defects and induces a partially reduced RE 1.5 Ce 1.5 O 5 +x phase with oxygen vacancy ordering. Significantly, it is demonstrated that the concentration of oxygen Frenkel defects and improved electrocatalytic activity can be further enhanced by increasing the compositional complexity (number of RE cations involved) in the substitution. The resulting novel compositionally‐complex fluorite– (La 0.2 Pr 0.2 Nd 0.2 Tb 0.2 Dy 0.2 ) 2 Ce 2 O 7 is shown to display a low OER overpotential of 210 mV at a current density of 10 mAcm −2 in 1M KOH, and excellent cycling stability. It is suggested that increasing the compositional complexity of fluorite nanocatalysts expands the ability to tailor catalyst design.

Chemistry↗