Judge, Colin D.

Publications and source records attributed to Judge, Colin D..

4 records

DOE OSTI2024

Characterization of Fuel Cladding Chemical Interaction on a High Burnup U-10Zr Metallic Fuel via Electron Energy Loss Spectroscopy Enhanced by Machine Learning

Fuel cladding chemical interaction (FCCI) is one of the main performance limiting factors for metallic nuclear fuels. The interaction destabilizes the martensitic microstructure and deteriorates mechanical properties of HT-9 cladding. The detection of low atomic number elements (Z<10) and overlapping of elemental peaks can be problematic in interpreting energy dispersive X-ray spectroscopy (EDS) data. Electron energy loss spectroscopy (EELS) provides precise elemental edge energy values and can detect elements with a low atomic number. This work utilizes EELS to study the distribution of lanthanides and light elements at the interaction region. The sample was prepared from the FCCI region of a U-10Zr (wt.%) solid fuel with HT-9 cladding, irradiated to a burnup of 13.2 at.%. Processing the EELS data included three major steps: 1) enhance the signal to noise ratio by denoising the spectrum with principal component analysis (PCA) method, removing background and performing deconvolution; 2) identify chemical elements with core energy loss edges; 3) confirm different phases using a popular machine learning method, K-means. This work presents qualitative assessment of lanthanides and light elements like carbon (C) and oxygen (O) enhanced by the application of machine learning algorithms. By comparing with EDS elemental maps, EELS provides higher resolution chemical maps, reveals the distribution of carbon at the interaction region supporting the formation of zirconium carbide, a rind-like microstructure feature that was proposed to mitigate the chemical interaction. Furthermore, the plasmon peak map was also found to indicate an energy shift associated with the formation of phases/compounds. K-means clustering method was used on the processed electron energy loss (EEL) spectrum to automatically reveal different phases. The resulting clustered maps from K-means clustering align well with elemental maps confirming certain phases, especially Fe-Ce and Zr-C, in the FCCI region.

EELS↗

DOE OSTI2024

Segmentation and Classification of Fission as Pores in Reactor Irradiated Annular U–10Zr Metallic Fuel Using Machine Learning Models

Metallic fuels, particularly U—10Zr, are promising candidates for next-generation sodium-cooled fast reactors. Irradiation of nuclear fuels in reactors can lead to the formation of solid and gas fission product which subsequently forms microstructural pores, deteriorating fuel performance. Due to the massive amount of pores and complex phases formed, a quantitative description of fission gas pores is not yet available, preventing the development of microstructure-informed fuel performance modeling for fuel qualification. This paper applied a pre-trained deep learning model to ~10,260 high magnification scanning electron microscopy images. This method increased the accuracy of fission gas pore segmentation and allows statistical features to be extracted which cannot be achieved manually. A pre-trained decision tree model worked on the segemenation results and further classified the pores into different categories to produce a correlation between the pores, movement of lanthanides, and temperature gradient during irradiation. Finally, this paper emphasizes the potentials of machine learning models to accelerate fuel research, development, and qualification for advanced reactors.

36 MATERIALS SCIENCE↗

DOE OSTI2022

Measurement of grain boundary strength of Inconel X-750 superalloy using in-situ micro-tensile testing techniques in FIB/SEM system

Grain boundaries (GBs), known as two-dimensional defects, are omnipresent in polycrystalline metallic alloys and thus influence a wide range of mechanical properties under different environmental conditions like irradiation and corrosion. Therefore, quantifying the strength of individual GBs is critical for understanding the degradation of mechanical properties of materials under different conditions. In this study we developed an efficient approach for the fabrication of micro-tensile specimens with a GB almost perpendicular to the tensile direction, which is expected to advance the development of individual GB tensile testing at micro or nanoscale in a wide scope of materials. Further, an in-situ cantilever micro-tensile testing method was developed and used to quantify the strength of a Σ3 GB in Inconel X-750 with the combination of finite element modeling. The average ultimate tensile strength (UTS) of a non-irradiated Σ3 GB is estimated at around 1.4 GPa, comparable to that of a neutron-irradiated Σ3 GB with a dose of ~1.5 dpa (1.3 GPa). Moreover, the in-situ push-to-pull micro-tensile testing technique developed in this work provides valuable insights into the high-angle GB deformation and fracture behavior. This method generates qualitatively similar ductility behavior before and after neutron irradiation as the bulk material testing. However, the ductility and UTS values obtained from this method are different from bulk measurements due to vastly different specimen dimensions.

36 MATERIALS SCIENCE↗

DOE OSTI2022

Small-scale mechanical testing and characterization of fuel cladding chemical interaction between HT9 cladding and advanced U-based metallic fuel alloy

Fuel cladding chemical interactions (FCCI) occurred on the interface between the nuclear metal fuel and cladding is the primary cause of cladding wastage, weakening cladding mechanical integrity, and placing fuel and cladding at risk. Although the microstructural and phase information of FCCI has been fairly understood, mechanical properties remain less studied due to limited reaction volume. Here, through a combining of advanced electron microscopy characterizations and small-scale mechanical testing techniques, including indentation and micro-tensile testing, this study investigated the microscale mechanical properties of FCCI between the ferritic/martensitic (F/M) HT9 cladding and an advanced Uranium (U)-based metallic fuel irradiated at the Advanced Test Reactor to 2.2% FIMA with peak inner cladding temperature reached to 650 °C. Mechanical testing results show significant hardening and embrittlement in the FCCI region. The brittle fracture of FCCI specimen is mainly attributed to the formation of nano-crystallized intermetallic σ-FeCr phase. Whereas mechanical softening was revealed in the unreacted HT9 matrix due to irradiation-induced microstructural and microchemical evolution, specifically, the disappearance of martensitic lath structure and the formation of Fe 2 Mo Laves phase precipitation which consumed the solid solution strengthening Mo from the F/M HT9 matrix. Due to the achieved high cladding temperature, this fuel pin is of particular significance for revealing the high-temperature irradiation effect on the mechanical properties of HT9 cladding. Therefore, the outcomes of this study are expected to contribute to the development of multi-scale mechanical behavior modeling of HT9 cladding for Generation IV reactors which requires cladding to run at higher temperature (above 600 ?).