DOE OSTI2020

Structure and stability of alkali gallates structurally reminiscent of hollandite

Abstract Single crystals of CsGa 7 O 11 , RbGa 7 O 11 , and RbGa 4 In 5 O 14 were grown from alkali halide melts and their structures were characterized by single crystal and powder X‐ray diffraction. CsGa 7 O 11 and RbGa 7 O 11 adopt the same structure type, reminiscent of the hollandite structure type, as it contains nearly rectangular channels made up of two dimers of edge‐sharing GaO 6 octahedra, and two corner‐sharing octahedron/tetrahedron pairs. The structure of RbGa 4 In 5 O 14 is more complex and is comprised of indium octahedra, gallium trigonal bipyramids, and gallium tetrahedra, and contains similar sized tunnels as CsGa 7 O 11 and RbGa 7 O 11 . CsGa 7 O 11 and RbGa 4 In 5 O 14 were further characterized by TGA, ion exchange experiments, and DFT studies revealing that both structures are thermodynamically stable up to 850°C; however, CsGa 7 O 11 decomposes to GaO(OH) xH 2 O when heated in warm aqueous solutions. CsGa 7 O 11 undergoes ion exchange in both an aqueous solution of RbCl and a RbNO 3 melt, as predicted by DFT studies, where the ion exchange is more extensive in the RbNO 3 melt.

Juillerat, Christian A.↗

DOE OSTI2020

Targeted crystal growth of uranium gallophosphates via the systematic exploration of the UF 4 –GaPO 4 –ACl (A = Cs, Rb) phase space

The flux synthesis of a uranium gallophosphate and a uranium gallate, Cs 4 [UO 2 Ga 2 (PO 4 ) 4 ] and Cs 2 UO 2 Ga 2 O 5 , and 4 uranium phosphates, [Rb 2 Rb 3.93 Cl 0.93 ][(UO 2 ) 5 (PO 4 ) 5 ], Rb 11 [(UO 2 ) 8 (PO 4 ) 9 ], Rb 7.6 [(UO 2 ) 8 O 8.6 F 0.4 (PO 4 ) 2 ], and Rb 6 [(UO 2 ) 5 O 2 (PO 4 ) 4 ], is reported.

Juillerat, Christian A.↗

DOE OSTI2020

Fluorination and reduction of CaCrO 3 by topochemical methods

Topochemical reactions between CaCrO 3 and polyvinylidene difluoride yield the new fluorinated phase CaCrO 2.5 F 0.5 , which was characterized by powder synchrotron X-ray diffraction, X-ray photoemission spectroscopy, and magnetic susceptibility measurements. The reaction proceeds via reduced oxide intermediates, CaCrO 2.67 and CaCrO 2.5 , in which CrO 6 octahedral and CrO 4 tetrahedral layers are stacked in a different manner along the c axis of CaCrO 3 . These two intermediate phases can be selectively synthesized by the carbothermal reduction with g-C 3 N 4. Both CaCrO 3 and CaCrO 2.5 F 0.5 adopt the same orthorhombic space group, Pbnm ; however, the fluorinated phase has decreased Cr–O–Cr bond angles as compared to the parent compound in both the ab plane and along the c -direction, which indicates an increased orthorhombic distortion due to the fluorination. Overall, while the oxygen vacancies are ordered in both intermediate phases, CaCrO 2.67 and CaCrO 2.5 , a site preference for fluorine in the oxyfluoride phase cannot be confirmed. CaCrO 3 and CaCrO 2.5 F 0.5 undergo antiferromagnetic phase transitions involving spin canting, where the fluorination causes the transition temperature to increase from 90 K to 110 K, as a result of the competition between the increased octahedral tilting and the enhancement of superexchange interactions involving Cr 3+ ions in the CaCrO 2.5 F 0.5 structure.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗