NASA NTRS1989

Anomalous effects in silicon solar cell irradiated by 1-MeV protons

Several silicon solar cells having thicknesses of approximately 63 microns, with and without back-surface fields (BSF), were irradiated with 1-MeV protons having fluences between 10 to the 10th and 10 to the 12th sq cm. The irradiations were performed using both normal and isotropic incidence on the rear surfaces of the cells. It was observed that after irradiation with fluences greater than 10 to the 11th protons/sq cm, all BSF cells degraded at a faster rate than cells without BSF. The irradiation results are analyzed using a model in which irradiation-induced defects in the BSF region are taken into account. Tentatively, it is concluded that an increase in defect density due to the formation of aluminum and proton complexes in BSF cells is responsible for the higher-power loss in the BSF cells compared to the non-BSF cells.

Kachare, R.↗

NASA NTRS1988

Annealing results on low-energy proton-irradiated GaAs solar cells

AlGaAs/GaAs solar cells with an approximately 0.5-micron-thick Al(0.85)Ga(0.15)As window layer were irradiated using normal and isotropic incident protons having energies between 50 and 500 keV with fluence up to 1 x 10 to the 12th protons/sq cm. The irradiated cells were annealed at temperatures between 150 and 300 C in nitrogen ambient. The annealing results reveal that significant recovery in spectral response at longer wavelengths occurred. However, the short-wavelength spectral response showed negligible annealing, irrespective of the irradiation energy and annealing conditions. This indicates that the damage produced near the AlGaAs/GaAs interface and the space-charge region anneals differently than damage produced in the bulk. This is explained by using a model in which the as-grown dislocations interact with irradiation-induced point defects to produce thermally stable defects.

Kachare, R.↗

NASA NTRS1988

Tunneling effects in the current-voltage characteristics of high-efficiency GaAs solar cells

Evidence is that tunneling via states in the forbidden gap is the dominant source of excess current in the dark current-voltage (I-V) characteristics of high-efficiency DMCVD grown Al(x)Ga(1-x)As/GaAs(x is equal to or greater than 0.85) solar cells. The dark forward and reverse I-V measurements were made on several solar cells, for the first time, at temperatures between 193 and 301 K. Low-voltage reverse-bias I-V data of a number of cells give a thermal activation energy for excess current of 0.026 + or - 0.005 eV, which corresponds to the carbon impurity in GaAs. However, other energy levels between 0.02 eV and 0.04 eV were observed in some cells which may correspond to impurity levels introduced by Cu, Si, Ge, or Cd. The forward-bias excess current is mainly due to carrier tunneling between localized levels created in the space-charge layer by impurities such as carbon, which are incorporated during the solar cell growth process. A model is suggested to explain the results.

Kachare, R.↗

NASA NTRS1987

Results of 1 MeV proton irradiation of front and back surfaces of silicon solar cells

Several silicon solar cells with and without back surface fields (BSF), having thicknesses of 200 microns and 63 microns were irradiated with 1 MeV protons having fluences between 1 times 10 to the 10th power and 1 times 10 to the 12th power p/square cm. The irradiation was performed using both normal and isotropic incidence on the front as well as back surfaces of the solar cells. The results of the back surface irradiations are analyzed using a model in which irradiation induced defects across the high-low (BSF) junction are considered. It is concluded that degradation of the high-low junction is responsible for the severe performance loss in thinner cells when irradiated from the rear.

Anspaugh, B. E.↗

NASA NTRS1987

Radiation damage of gallium arsenide production cells

High efficiency liquid phase epitaxy (LPE) gallium arsenide cells were irradiated with 1 Mev electrons up to fluences of 1 times 10 to the 16th power cm-2. Measurements of spectral response and dark and illuminated I-V data were made at each fluence and then, using computer codes, the experimental data was fitted to gallium arsenide cell models. In this way it was possible to determine the extent of the damage, and hence damage coefficients in both the emitter and base of the cell.

Mardesich, N.↗

NASA NTRS1987

Front surface passivation of silicon solar cells with antireflection coating

It is demonstrated that the deposition and postdeposition sintering of an antireflection (AR) coating in hydrogen acts to passivate silicon solar cells. Cells with and without an SiO2 passivating layer, coated with a TiO(x)/Al2O3 AR coating, showed comparable enhancements in short-wavelength spectral response and in open-circuit voltage Voc after sintering at 400 C for 5 min in a hydrogen ambient. The improvement in Voc of cells without SiO2 is attributed to front-surface passivation by the AR coating during processing.

Crotty, G.↗

NASA NTRS1987

Radiation characteristics of low resistivity float zone silicon solar cells

The effects of 1-MeV electron irradiation on silicon solar cells with AM0 efficiencies ranging from 17 to 17.7 percent are described. These cells were processed on low-resistivity FZ substrates using techniques recently developed for high-efficiency terrestrial silicon solar cells. Results indicate that these cells are more susceptible to radiation damage. However, they do maintain a greater overall power output than conventional cells to which they were compared. These cells do not demonstrate post-electron-irradiation photon decay as has been described for cells processed on 1-10 ohm-cm FZ silicon.

Crotty, G. T.↗

NASA NTRS1986

Spatial resolution and nature of defects produced by low-energy proton irradiation of GaAs solar cells

AlGaAs/GaAs solar cells with about 0.5-micron-thick Al(0.85)Ga(0.15)As window layers were irradiated using isotropic and normal incidence protons having energies between 50 and 500 keV with fluences up to 1 x 10 to the 12th protons/sq cm. Although the projected range for these protons varies from 0 to more than 4.5 microns, the recombination losses due to the irradiation-induced defects were observed to be maximum in the vicinity of the AlGaAs/GaAs interface and the space-charge region irrespective of the proton energy. This was found by analyzing spectral response measurements. The results are explained by using a model in which the interaction of as-grown dislocations with irradiation-induced point defects is considered.

Kachare, R.↗

NASA NTRS1985

A summary report on the Flat-Plate Solar Array Project Workshop on Transparent Conducting Polymers

The proceedings and technical discussions of a workshop on Transparent Conducting Polymers (TCP) for solar cell applications are reported. This is in support of the Device Research Task of the Flat-Flate Solar Array Project. The workshop took place on January 11 and 12, 1985, in Santa Barbara, California. Participants included university and industry researchers. The discussions focused on the electronic and optical properties of TCP, and on experimental issues and problems that should be addressed for high-efficiency solar cell application.

Kachare, R.↗

NASA NTRS1985

Summary of high-efficiency solar-cell research

High-efficiency solar-cell activities supporting efforts to achieve the DOE Five-Year Plan goals are summarized. Specific objectives are to identify and resolve key generic problems that limit cell efficiency to below theoretically predicted values and to design and fabricate cells having efficiences equal to or greater than 20% (AM1.5). Theoretical curves for various p-n junction cells were shown. The effects of practical barriers on cell efficiency was depicted along with the modeling parameters. Cell design parameters used in the analyses were described. The usefulness and present limitations of the existing modeling capabilities were presented. The historical evolution of the efficiencies of cells made from web and edge-defined film-fed growth (EFG) silicon ribbons were also described. The status of contemporary higher-efficiency technical capabilities and future activities to raise efficiencies were stated.

Kachare, R.↗

NASA NTRS1985

Proceedings of the Flat-plate Solar Array Project Research Forum on High-efficiency Crystalline Silicon Solar Cells

The high-efficiency crystalline silicon solar cells research forum addressed high-efficiency concepts, surface-interface effects, bulk effects, modeling and device processing. The topics were arranged into six interactive sessions, which focused on the state-of-the-art of device structures, identification of barriers to achieve high-efficiency cells and potential ways to overcome these barriers.