DOE OSTI2023

Direct Mechanochemical Synthesis, Phase Stability, and Electrochemical Performance of α-NaFeO 2

To better understand polymorph control in transition metal oxides, the mechanochemical synthesis of NaFeO 2 was explored. In this paper, we report the direct synthesis of α-NaFeO 2 through a mechanochemical process. By milling Na 2 O 2 and γ-Fe 2 O 3 for 5 h, α-NaFeO 2 was prepared without high-temperature annealing needed in other synthesis methods. While investigating the mechanochemical synthesis, it was observed that changing the starting precursors and mass of precursors affects the resulting NaFeO 2 structure. Density functional theory calculations on the phase stability of NaFeO 2 phases show that the α phase is stabilized over the β phase in oxidizing environments, which is provided by the oxygen-rich reaction between Na 2 O 2 and Fe 2 O 3 . This provides a possible route to understanding polymorph control in NaFeO 2 . Annealing the as-milled α-NaFeO 2 at 700 °C has resulted in increased crystallinity and structural changes that improved electrochemical performance in terms of capacity over the as-milled sample.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2023

Probing how Ti- and Nb-substitution affect the stability and improve the electrochemical performance of β- and ε-LiVOPO 4

LiVOPO 4 is a promising next-generation multi-electron cathode material, boasting a theoretical capacity of 305 mA h g -1 , significantly higher than any commercially used Li-ion battery cathode material. However, the material still faces several limitations, including the difficulty in attaining the full theoretical capacity at higher rates and capacity fade over several cycles. Here, in this paper, we show that Ti- and Nb-substitution can be used to improve the thermal stability and electrochemical performance of LiVOPO 4 . We show through in situ heating with XRD and a novel gradient heating technique that both Ti- and Nb-substitution cause β-LiVOPO 4 to be stabilized relative to ε-LiVOPO 4 . This is due to transition-metal substitution, which increases the O-vacancy formation energies, pushing the β → ε transition to higher temperatures. We show that it is still possible to synthesize pure-phase ε-LiVOPO 4 through the use of high temperatures to generate these O-vacancies. We show that even 1% of Ti- or Nb-substitution can improve the initial capacity and long term cycling capability of LiVOPO 4 by improving the high-voltage capacity and reducing the capacity fade in both the high- and low-voltage regions. This is due to the overall improved Li + ion diffusion which is caused by an improved charge-transfer resistance during cycling.

25 ENERGY STORAGE↗