Publications and source records attributed to Kang, Sujin.
Explore the source record for details and available documents.
To achieve good rate capability of lithium metal anodes for high-energy-density batteries, one fundamental challenge is the slow lithium diffusion at the interface. Here we report an interpenetrated, three-dimensional lithium metal/lithium tin alloy nanocomposite foil realized by a simple calendering and folding process of lithium and tin foils, and spontaneous alloying reactions. The strong affinity between the metallic lithium and lithium tin alloy as mixed electronic and ionic conducting networks, and their abundant interfaces enable ultrafast charger diffusion across the entire electrode. Furthermore, we demonstrate that a lithium/lithium tin alloy foil electrode sustains stable lithium stripping/plating under 30 mA cm -2 and 5 mAh cm -2 with a very low overpotential of 20 mV for 200 cycles in a commercial carbonate electrolyte. Cycled under 6 C (6.6 mA cm -2 ), a 1.0 mAh cm -2 LiNi 0.6 Co 0.2 Mn 0.2 O 2 electrode maintains a substantial 74% of its capacity by pairing with such anode.
Volumetric energy density is considered a primary factor in developing high-energy batteries. Despite its significance, less efforts have been devoted to its improvement. Silicon-based materials have emerged as next-generation anodes for lithium-ion batteries due to their high specific capacity. However, their volumetric capacities are limited by the volume expansion rate of silicon, which restricts mass loading in the electrodes. To address this challenge, we introduce porous silicon templated from earth-abundant minerals with native internal voids, capable of alleviating volumetric expansion during repeated cycles. In situ transmission electron microscopy analysis allows the precise determination of the expansion rate of silicon, thus presenting an analytical model for finding the optimal content in silicon/graphite composites. The inner pores in silicon reduce problems associated with its expansion and allow higher silicon loading of 42% beyond the conventional limitations of 13–14%. Consequently, the anode designed in this work can deliver a volumetric capacity of 978 mAh cc–1. Thus, suppressing volume expansion with natural abundant template-assisted materials opens new avenues for cost-effective fabrication of high volumetric capacity batteries.