Kang, Sung Bong | Search NASA

DOE OSTI2022

Ferric chloride aided peracetic acid pretreatment for effective utilization of sugarcane bagasse

The synergetic impacts of ferric chloride aided peracetic acid (FPA) pretreatment were investigated to enhance the total biomass utilization through effective cellulose conversion and high-quality lignin production. The sugarcane bagasse pretreatment with 2% peracetic acid (PAA) and 0.1 mol/L ferric chloride (FeCl 3 ) effectively removed 57.3% of lignin and 72.2% of xylan while preserving ~ 97% of cellulose from sugarcane bagasse under mild temperature (90 °C). The FPA pretreated sugarcane bagasse was effectively hydrolyzed with a glucose yield of 313.0 mg/g-biomass, which was 4.5 times higher than the yield of untreated biomass (69.75 mg/g-biomass) and 1.6 and 3.6 times higher than that of individual PAA and FeCl 3 pretreated sugarcane bagasse, respectively. The regenerated lignin (FPA lignin) showed great potential for further valorization by preserving the major interunit linkage (up to 86% of β-O-4) without significant carbohydrate contamination and lignin condensation due to its mild reaction conditions. In this paper, the combination of PAA and FeCl 3 synergistically enhanced the pretreatment efficiency on sugarcane bagasse and resulted in high fermentable sugar and high-quality lignin production.

09 BIOMASS FUELS↗

DOE OSTI2020

Coupled methane and NO x conversion on Pt + Pd/Al 2 O 3 monolith: Conversion enhancement through feed modulation and Mn 0.5 Fe 2.5 O 4 spinel addition

The performance of a dual-layer Pt-Pd/Al 2 O 3 washcoated monolith promoted by an Al 2 O 3 -supported Mn 0.5 Fe 2.5 O 4 spinel base layer was evaluated with the objective to develop a catalyst with a lower loading of Platinum group metal (PGM) for stoichiometric natural gas vehicle (NGV) emission control. Flow reactor results show that a combination of a lean/rich modulated feed and spinel addition gives enhanced methane and NO conversions compared to a steady-state feed having the same overall composition. Washcoated catalysts – PGM-only, spinel-only, PGM + spinel – were compared over a wide range of operating conditions. The results show a decrease in the methane conversion light-off temperature of up to 85 °C for an application-relevant feed (CH 4 + NO + H 2 + CO + O 2 + H 2 O + CO 2 ) while a moderate 40 °C decrease was observed for a simple feed (CH 4 + O 2 + H 2 O + CO 2 ). In the absence of spinel the modulation enhancement is negatively impacted at high methane conversion (> 80 %). The data show that the O 2 storage and release property of the spinel is needed to fully exploit the modulation enhancement. The mechanism responsible for the enhancement is linked to suppression of O 2 inhibition on the methane oxidation rate near the stoichiometric neutral point (λ = 1). Sufficiently fast cycling achieves a balance between a metallic and oxidic precious metal crystallites favorable for methane activation. The addition of spinel moves this balance closer to the λ = 1 feed, enabling a high oxidation efficiency with lower byproduct NH 3 selectivity. Enhancement in the NO conversion follows the methane conversion due to an easier NO reduction under the slightly rich of stoichiometric feed. Comparison of the PGM + spinel catalysts to PGM-only catalysts shows that the addition of spinel in combination with modulation can achieve the same activity with a lower PGM loading.

03 NATURAL GAS↗